Composite tubular article and process for producing the same
Assignee: Nitto Denko Corp
•
Filing: 1990-07-20
•
Granted: 1995-05-02
•
Expires: 2010-07-20
Abstract
Abstract The present invention relates to a composite tubular article for use as the fixing belt in an image-forming device such as a copying machine etc., particularly as a fixing belt suited for thermal fixing, and also relates to a process for producing the same. Conventionally known as an image-fixing belt is a belt consisting of a polyimide resin as the inner layer and a fluoroplastic as the outer layer. However, this fixing belt has problems that clear images cannot be obtained because the thickness of each layer is uneven, and that unglossed, so-called matt images cannot be obtained because the belt surface is smooth. This invention provides a composite tubular article comprising a tubular inner layer made of a polyimide resin and a tubular outer layer made of a fluoroplastic, the outer circumferential surface of the fluoroplastic tubular outer layer having a surface roughness of 1 to 10 μm. The invention further provides, as a production process for the same, a process in which the outer layer is formed by use of a cylinder having an inner circumferential surface with a surface roughness of 1 to 10 μm, and a polyimide-resin tubular inner layer is formed on the inner circumferential surface of the outer layer by converting a poly(amic acid) into a polyimide, or a process in which an inner layer formed by converting a poly(amic acid) into a polyimide is immersed in or sprayed with a fluoroplastic solution in which a particulate material of 5 μm or smaller has been dispersed, thereby to form an outer layer.
Inventors
- 👤 Toshio Nakajima
- 👤 Masayuki Kaneto
- 👤 Toshihiko Tomita
- 👤 Tokio Fujita
- 👤 Hitoshi Ishizaka
- 👤 Chiaki Harada
- 👤 Gosei Uemura
- 👤 Taizo Sasaki
- 👤 Masao Nakamura
- 👤 Mamoru Hondo
- 👤 Tadanori Michimoto
- 👤 Toshiaki Iwamoto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 06:34
CPC Classifications
G; G03; G03G; G03G15/00; G03G15/20; G03G15/2003; G03G15/2014; G03G15/2053; G03G15/2057; B; B29; B29C; B29C41/00; B29C41/02; B29C41/22; B29D; B29D23/00; B29D99/00; B29D99/0032; B29D99/0035; G03G15/2064; G03G5/00; G03G5/10; B29K; B29K2027/00; B29K2027/12; B29K2079/00; B29K2995/00; B29K2995/0003; B29K2995/0005; B29L; B29L2023/00; B29L2031/00; B29L2031/32; B29L2031/324; B29L2031/709; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49544; Y10T29/4956; Y10T428/00; Y10T428/13; Y10T428/1352; Y10T428/1372; Y10T428/139; Y10T428/1393; Y10T428/24; Y10T428/24628; Y10T428/31504; Y10T428/3154; Y10T428/31721
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
52 words
A composite tubular article for a fixing belt comprising a tubular inner layer made of a polyimide resin and a tubular outer layer made of a fluoroplastic, characterized by that the outer circumferential surface of said fluoroplastic tubular outer layer has a surface roughness (R z ) of 1 to 10 μm.
Claim 2
Dependent Claim
52 words
A composite tubular article for a fixing belt comprising a tubular inner layer made of a polyimide resin and a tubular outer layer made of a fluoroplastic, characterized by that the outer circumferential surface of said fluoroplastic tubular outer layer has a surface roughness (R z ) of 1 to 10 μm.
Claim 3
Dependent Claim
35 words
A composite tubular article for a fixing belt as claimed in claim 1, wherein the outer circumferential surface of the fluoroplastic tubular outer layer has a pure water contact angle of 90 degrees or more.
Claim 4
Dependent Claim
33 words
A composite tubular article for a fixing belt as claimed in claim 1, wherein the fluoroplastic tubular outer layer contains a particulate material having an average particle diameter of 5 μm or less.
Claim 5
Dependent Claim
23 words
A composite tubular article for a fixing belt as claimed in claim 3, wherein the particulate material is an electrically conductive particulate material.
Claim 6
Dependent Claim
37 words
A composite tubular article for a fixing belt as claimed in any one of claims 1 to 3, wherein the inner circumferential surface of the fluoroplastic tubular outer layer has been treated with a sodium complex salt.
Claim 7
Dependent Claim
48 words
A composite tubular article for a fixing belt as claimed in any one of claims 1 to 3, wherein the outer circumferential surface of the polyimide-resin tubular inner layer has undergone at least one treatment selected from alkali treatment, primer treatment, corona treatment, plasma treatment, and UV treatment.
Claim 8
Dependent Claim
126 words
A process for producing a composite tubular article for a fixing belt characterized by coating a fluoroplastic solution on the inner circumferential surface of a cylinder to form a tubular outer layer made of the fluoroplastic, said inner circumferential surface having a surface roughness (R z ) of 1 to 10 μm, further coating a poly(amic acid) solution on the inner circumferential surface of the thus-formed fluoroplastic tubular outer layer, causing a bullet-shaped or spherical runner to run along the inner circumferential surface on which the poly(amic acid) solution has been coated, subsequently imidizing the poly(amic acid) to form a tubular inner layer made of a polyimide resin, thereby to obtain a composite tubular article, and then taking the composite tubular article out of the cylinder.
Claim 9
Dependent Claim
126 words
A process for producing a composite tubular article for a fixing belt characterized by coating a fluoroplastic solution on the inner circumferential surface of a cylinder to form a tubular outer layer made of the fluoroplastic, said inner circumferential surface having a surface roughness (R z ) of 1 to 10 μm, further coating a poly(amic acid) solution on the inner circumferential surface of the thus-formed fluoroplastic tubular outer layer, causing a bullet-shaped or spherical runner to run along the inner circumferential surface on which the poly(amic acid) solution has been coated, subsequently imidizing the poly(amic acid) to form a tubular inner layer made of a polyimide resin, thereby to obtain a composite tubular article, and then taking the composite tubular article out of the cylinder.
Claim 10
Dependent Claim
38 words
A process for producing a composite tubular article for a fixing belt as claimed in claim 7, wherein the fluoroplastic solution contains a particulate material having an average particle diameter of 5 μm or less uniformly dispersed therein.
Claim 11
Dependent Claim
53 words
A process for producing a composite tubular article for a fixing belt as claimed in claim 7, wherein the inner circumferential surface of the formed fluoroplastic tubular outer layer is treated by bringing a sodium complex salt into contact with the inner circumferential surface, and thereafter the polyimide-resin tubular inner layer is formed.
Claim 12
Dependent Claim
128 words
A process for producing a composite tubular article for a fixing belt characterized by coating a poly(amic acid) solution on the inner circumferential surface of a cylinder, causing a bullet-shaped or spherical runner to run along the inner circumferential surface on which the poly(amic acid) solution has been coated, subsequently imidizing the poly(amic acid) to form a tubular inner layer made of a polyimide resin, thereafter taking the polyimide-resin tubular inner layer out of the cylinder, and then immersing the tubular inner layer in a fluoroplastic solution in which a particulate material having an average particle diameter of 5 μm or less has been uniformly dispersed, thereby to form a tubular outer layer made of the fluoroplastic on the outer circumferential surface of the polyimide-resin tubular inner layer.
Claim 13
Dependent Claim
128 words
A process for producing a composite tubular article for a fixing belt characterized by coating a poly(amic acid) solution on the inner circumferential surface of a cylinder, causing a bullet-shaped or spherical runner to run along the inner circumferential surface on which the poly(amic acid) solution has been coated, subsequently imidizing the poly(amic acid) to form a tubular inner layer made of a polyimide resin, thereafter taking the polyimide-resin tubular inner layer out of the cylinder, and then immersing the tubular inner layer in a fluoroplastic solution in which a particulate material having an average particle diameter of 5 μm or less has been uniformly dispersed, thereby to form a tubular outer layer made of the fluoroplastic on the outer circumferential surface of the polyimide-resin tubular inner layer.
Claim 14
Dependent Claim
122 words
A process for producing a composite tubular article for a fixing belt characterized by coating a poly(amic acid) solution on the inner circumferential surface of a cylinder, causing a bullet-shaped or spherical runner to run along the inner circumferential surface on which the poly(amic acid) solution has been coated, subsequently imidizing the poly(amic acid) to form a tubular inner layer made of a polyimide resin, thereafter taking the polyimide-resin tubular inner layer out of the cylinder, and then spray-coating the outer circumferential surface of the tubular inner layer with a fluoroplastic solution in which a particulate material having an average particle diameter of 5 μm or less has been uniformly dispersed, thereby to form a tubular outer layer made of the fluoroplastic.
Claim 15
Dependent Claim
122 words
A process for producing a composite tubular article for a fixing belt characterized by coating a poly(amic acid) solution on the inner circumferential surface of a cylinder, causing a bullet-shaped or spherical runner to run along the inner circumferential surface on which the poly(amic acid) solution has been coated, subsequently imidizing the poly(amic acid) to form a tubular inner layer made of a polyimide resin, thereafter taking the polyimide-resin tubular inner layer out of the cylinder, and then spray-coating the outer circumferential surface of the tubular inner layer with a fluoroplastic solution in which a particulate material having an average particle diameter of 5 μm or less has been uniformly dispersed, thereby to form a tubular outer layer made of the fluoroplastic.
Claim 16
Dependent Claim
33 words
A process for producing a composite tubular article for a fixing belt as claimed in any one of claims 7, 10, and 11, wherein the particulate material is an electrically conductive particulate material.
Claim 17
Dependent Claim
60 words
A process for producing a composite tubular article for a fixing belt as claimed in claim 10 or 11, wherein the outer circumferential surface of the formed polyimide-resin tubular inner layer is subjected to at least one treatment selected from alkali treatment, primer treatment, corona treatment, plasma treatment, and UV treatment, and thereafter the fluoroplastic tubular outer layer is formed.
References Cited (Backward Citations)
DE2049978A1
Cited
US3933825A
Cited
JPS5599031A
Cited
US4482603A
Cited
US4505573A
Cited
JPS61203460A
Cited
EP0283604A2
Cited
JPS638776A
Cited
EP0293482A1
Cited
JPS63192069A
Cited
EP0286543A2
Cited
EP0338479A1
Cited
US5011727A
Cited
JPH0274944A
Cited
JPH0333784A
Cited
JP3008776U
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-05-01 | 1998-10-31 | 1999-05-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-05-01 | 2002-10-31 | 2003-05-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-05-01 | 2006-10-31 | 2007-05-02 | $7700.00 | Window Closed / Lapsed |