Zinc oxide coated substrates
Assignee: Ensci Inc
•
Filing: 1994-01-18
•
Granted: 1995-04-18
•
Expires: 2014-01-18
Abstract
Abstract Processes for coating substrates, in particular substrates including shielded surfaces, with zinc oxide-containing coatings are disclosed. Such processes comprise contacting a substrate with a zinc oxide precursor, preferably maintaining the precursor coated substrate at conditions to equilibrate the coating, and then oxidizing the precursor to form a substrate containing zinc oxide. Also disclosed are substrates coated with zinc oxide-containing coatings for use in various applications.
Inventors
- 👤 Thomas J. Clough
- 👤 Victor L. Grosvenor
- 👤 Naum Pinsky
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 17:51
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/45; C04B41/50; C04B41/5025; C04B41/5036; C04B41/009; C04B41/80; C04B41/81; C04B41/85; C04B41/87; Y; Y10; Y10T; Y10T428/00; Y10T428/11; Y10T428/1157; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/294; Y10T428/2958; Y10T428/2982; Y10T428/2991
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
248 words
An article comprising a three dimensional inorganic substrate other than electrically conductive zinc oxide having a coating containing electrically conductive zinc oxide on at least a portion of all three dimensions thereof produced by a process comprising; contacting an inorganic three dimensional substrate which includes external surfaces and shielded surfaces which are at least partially shielded by other portions of said substrate with a composition comprising a zinc oxide-forming compound other than zinc oxide at conditions effective to form a zinc oxide-forming compound containing coating on at least a portion of said substrate; forming a liquidus zinc oxide forming compound containing coating on at least a portion of the three dimensions of said substrate including the shielded surfaces of said substrate; contacting said substrate with at least one dopant forming component at conditions effective to form a dopant component-containing coating on at least a portion of said substrate including at least a portion of the three dimensions of said substrate including the shielded surfaces of said substrate; said contacting being initiated at least prior to the substantially complete oxidation of said zinc oxide forming compound to zinc oxide; contacting said substrate having said zinc oxide forming compound containing coating and said dopant component-containing coating thereon with an oxidizing agent at conditions effective to convert said zinc oxide forming compound to zinc oxide and form a doped zinc oxide coating on at least a portion of said three dimensions of said substrate including the shielded surfaces of said substrate.
Claim 2
Dependent Claim
248 words
An article comprising a three dimensional inorganic substrate other than electrically conductive zinc oxide having a coating containing electrically conductive zinc oxide on at least a portion of all three dimensions thereof produced by a process comprising; contacting an inorganic three dimensional substrate which includes external surfaces and shielded surfaces which are at least partially shielded by other portions of said substrate with a composition comprising a zinc oxide-forming compound other than zinc oxide at conditions effective to form a zinc oxide-forming compound containing coating on at least a portion of said substrate; forming a liquidus zinc oxide forming compound containing coating on at least a portion of the three dimensions of said substrate including the shielded surfaces of said substrate; contacting said substrate with at least one dopant forming component at conditions effective to form a dopant component-containing coating on at least a portion of said substrate including at least a portion of the three dimensions of said substrate including the shielded surfaces of said substrate; said contacting being initiated at least prior to the substantially complete oxidation of said zinc oxide forming compound to zinc oxide; contacting said substrate having said zinc oxide forming compound containing coating and said dopant component-containing coating thereon with an oxidizing agent at conditions effective to convert said zinc oxide forming compound to zinc oxide and form a doped zinc oxide coating on at least a portion of said three dimensions of said substrate including the shielded surfaces of said substrate.
Claim 3
Dependent Claim
35 words
The article of claim 1 wherein said zinc oxide forming compound is selected from the group consisting of zinc chloride, low molecular weight zinc organic salts, low molecular weight zinc organic complexes and mixtures thereof.
Claim 4
Dependent Claim
14 words
The article of claim 1 wherein said zinc oxide forming compound is zinc chloride.
Claim 5
Dependent Claim
29 words
The article of claim 1 wherein said dopant-forming component is a dopant oxide precursor selected from the group consisting of aluminum, cobalt, gallium, tin, germanium, chromium, titanium and indium.
Claim 6
Dependent Claim
33 words
The article of claim 1 wherein said dopant-forming component is a dopant oxide precursor selected from the group consisting of aluminum, gallium and indium and said zinc oxide forming compound is zinc chloride.
Claim 7
Dependent Claim
90 words
The article of claim 1 wherein said substrate is maintained for a period of time at conditions effective to do at least one of the following: (1) coat a larger portion of said substrate with said zinc oxide forming compound: (2) distribute said zinc oxide forming compound over said substrate; (3) make said zinc oxide forming compound-containing coating more uniform in thickness; (4) incorporate said dopant component in said zinc oxide forming compound coating; and (5) distribute said dopant component more uniformly in said zinc oxide forming compound containing coating.
Claim 8
Dependent Claim
36 words
The article of claim 1 wherein said substrate is in a form selected from the group consisting of spheres, extrudates, flakes, fibers, fiber rovings, chopped fibers, fiber mats, porous substrates, irregularly shaped particles and multi-channel monoliths.
Claim 9
Dependent Claim
39 words
The article of claim 5 wherein said substrate is an inorganic oxide and in a form selected from the group consisting of spheres, extrudates, flakes, fibers, porous substrates, and irregularly shaped particles, and said substrate is substantially non-electrically conductive.
Claim 10
Dependent Claim
206 words
An article comprising a three dimensional inorganic substrate other than electrically conductive zinc oxide having a coating containing electrically conductive zinc oxide on at least a portion of all three dimensions thereof produced by a process comprising; contacting an inorganic three dimensional substrate which includes external surfaces and shielded portions of said substrate with a composition comprising a zinc chloride-forming compound at conditions effective to form a zinc chloride-forming compound containing coating on at least a portion of said substrate; forming a liquidus zinc chloride-forming compound containing coating on at least a portion of the three dimensions of said substrate including the shielded surfaces of said substrate and at conditions effective to do at least one of the following: (1) coat a larger portion of said substrate with said zinc chloride-forming compound (2) distribute said zinc chloride-forming compound over said substrate; and (3) make said zinc chloride-forming compound containing coating more uniform in thickness; and contacting said substrate with said zinc chloride-forming compound containing coating with an oxidizing agent at conditions effective to convert the zinc chloride-forming compound to zinc oxide and form a zinc oxide coating on at least a portion of said three dimensions of said substrate including the shielded surfaces of said substrate.
Claim 11
Dependent Claim
206 words
An article comprising a three dimensional inorganic substrate other than electrically conductive zinc oxide having a coating containing electrically conductive zinc oxide on at least a portion of all three dimensions thereof produced by a process comprising; contacting an inorganic three dimensional substrate which includes external surfaces and shielded portions of said substrate with a composition comprising a zinc chloride-forming compound at conditions effective to form a zinc chloride-forming compound containing coating on at least a portion of said substrate; forming a liquidus zinc chloride-forming compound containing coating on at least a portion of the three dimensions of said substrate including the shielded surfaces of said substrate and at conditions effective to do at least one of the following: (1) coat a larger portion of said substrate with said zinc chloride-forming compound (2) distribute said zinc chloride-forming compound over said substrate; and (3) make said zinc chloride-forming compound containing coating more uniform in thickness; and contacting said substrate with said zinc chloride-forming compound containing coating with an oxidizing agent at conditions effective to convert the zinc chloride-forming compound to zinc oxide and form a zinc oxide coating on at least a portion of said three dimensions of said substrate including the shielded surfaces of said substrate.
Claim 12
Dependent Claim
49 words
The article of claim 9 which further comprises contacting said substrate with a dopant-forming component at conditions effective to form a dopant-forming component containing coating on said substrate, said dopant forming component contacting occurring prior to the substantially complete oxidation of said zinc chloride forming compound to the oxide.
Claim 13
Dependent Claim
36 words
The article of claim 9 wherein said substrate is in a form selected from the group consisting of spheres, extrudates, flakes, fibers, fiber rovings, chopped fibers, fiber mats, porous substrates, irregularly shaped particles and multi-channel monoliths.
Claim 14
Dependent Claim
200 words
An article comprising a three dimensional inorganic substrate other than electrically conductive zinc oxide having a coating containing electrically conductive zinc oxide on at least a portion of all three dimensions thereof produced by a process comprising; contacting an inorganic three dimensional substrate with a composition comprising a zinc oxide precursor powder other than zinc oxide at conditions effective to form a coating containing zinc oxide precursor on at least a portion of the substrate; forming a liquidus zinc oxide precursor on at least a portion of the three dimensions of said substrate including the shielded surfaces of said substrate and at conditions effective to do at least one of the following: (1) coat a larger portion of said substrate with said coating containing zinc oxide precursor; (2) distribute said coating containing zinc oxide precursor over said substrate; and (3) make said coating containing zinc oxide precursor more uniform in thickness; and contacting said coated substrate with an oxidizing agent at conditions effective to convert said zinc oxide precursor to zinc oxide on at least a portion of said three dimensions of said substrate including the shielded surfaces of said substrate and form a substrate having a zinc oxide-containing coating.
Claim 15
Dependent Claim
200 words
An article comprising a three dimensional inorganic substrate other than electrically conductive zinc oxide having a coating containing electrically conductive zinc oxide on at least a portion of all three dimensions thereof produced by a process comprising; contacting an inorganic three dimensional substrate with a composition comprising a zinc oxide precursor powder other than zinc oxide at conditions effective to form a coating containing zinc oxide precursor on at least a portion of the substrate; forming a liquidus zinc oxide precursor on at least a portion of the three dimensions of said substrate including the shielded surfaces of said substrate and at conditions effective to do at least one of the following: (1) coat a larger portion of said substrate with said coating containing zinc oxide precursor; (2) distribute said coating containing zinc oxide precursor over said substrate; and (3) make said coating containing zinc oxide precursor more uniform in thickness; and contacting said coated substrate with an oxidizing agent at conditions effective to convert said zinc oxide precursor to zinc oxide on at least a portion of said three dimensions of said substrate including the shielded surfaces of said substrate and form a substrate having a zinc oxide-containing coating.
Claim 16
Dependent Claim
45 words
The article of claim 12 which further comprises contacting said substrate with dopant-forming component at conditions effective to from a dopant-forming component-containing coating on said substrate, said dopant-forming component contacting occurring prior to the substantially complete oxidation of said zinc oxide precursor to zinc oxide.
Claim 17
Dependent Claim
34 words
The article of claim 12 wherein said zinc oxide precursor is selected from the group consisting of zinc chloride, low molecular weight zinc organic salts, low molecular weight zinc organic complexes and mixtures thereof.
Claim 18
Dependent Claim
13 words
The article of claim 14 wherein said zinc oxide precursor is zinc chloride.
Claim 19
Dependent Claim
29 words
The article of claim 13 wherein said dopant-forming component is a dopant oxide precursor selected from the group consisting of aluminum, cobalt, gallium, tin, germanium, chromium, titanium and indium.
Claim 20
Dependent Claim
32 words
The article of claim 16 wherein said dopant-forming component is a dopant oxide precursor selected from the group consisting of aluminum, gallium and indium, and the zinc oxide precursor is zinc chloride.
Claim 21
Dependent Claim
32 words
The article of claim 12 wherein said substrate is selected from the group consisting of spheres, extrudates, flakes, fibers, porous substrates, and irregularly shaped particles and said substrate is substantially non-electrically conductive.
Claim 22
Dependent Claim
41 words
The article of claim 17 wherein said substrate is an inorganic oxide and in a form in a from selected from the group consisting of spheres, extrudates, flakes, porous, substrates, and irregularly shaped particles, and said substrate is substantially non-electrically conductive.
Claim 23
Dependent Claim
70 words
An article comprising a three dimensional inorganic substrate other than an electrically conductive zinc oxide having a particle type shape which includes external surfaces and shielded surfaces which are at least partially shielded by other portions of said substrate, said substrate having a coating containing electrically conductive doped zinc oxide coating on at least a portion of said three dimensions of said substrate including the shielded surfaces of said substrate.
Claim 24
Dependent Claim
70 words
An article comprising a three dimensional inorganic substrate other than an electrically conductive zinc oxide having a particle type shape which includes external surfaces and shielded surfaces which are at least partially shielded by other portions of said substrate, said substrate having a coating containing electrically conductive doped zinc oxide coating on at least a portion of said three dimensions of said substrate including the shielded surfaces of said substrate.
Claim 25
Dependent Claim
28 words
The article of claim 20 wherein said substrate is a shape selected from the group consisting of spheres, extrudates, flakes, fibers, porous substrates, particles and irregularly shaped particles.
Claim 26
Dependent Claim
32 words
The article of claim 21 wherein said substrate is an inorganic oxide and in a shaped selected form the group consisting of spheres, extrudates, flakes, porous substrates, particles and irregularly shaped particles.
References Cited (Backward Citations)
No citation records indexed.
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-04-17 | 1998-10-17 | 1999-04-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-04-17 | 2002-10-17 | 2003-04-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-04-17 | 2006-10-17 | 2007-04-18 | $7700.00 | Window Closed / Lapsed |