Process for obtaining ultra-high modulus line products with enhanced mechanical properties
Assignee: Polteco Inc
•
Filing: 1994-01-06
•
Granted: 1995-04-18
•
Expires: 2014-01-06
Abstract
Abstract A method of producing high modulus and high strength products of polyethylene and other thermoplastic polymers by swelling with a suitable solvent a melt crystallized, or compacted powder morphology to form a pseudo-gel, drying the pseudo-gel, compressing it, and drawing it. The optimum process involves swelling the initial morphology in the form of a tape/ribbon/rod/monofilament/sheet/tube in a non-volatile solvent at temperatures near the polymer crystalline melting point, cooling the morphology under controlled conditions, lightly compressing it to remove the non-volatile solvent, extracting the non-volatile solvent by volatile solvent, removing the volatile solvent by evaporation or vacuum, compressing the morphology between rolls, and then stretching it at temperatures below the crystalline melting point of the polymer to obtain tapes, ribbons, monofilaments, sheets or tubes with improved mechanical properties. Products from the method include improved dental floss, fishing line and numerous other applications.
Inventors
- 👤 Anagnostis E. Zachariades
- 👤 Premal Shukla
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 23:13
CPC Classifications
A; A61; A61C; A61C15/00; A61C15/04; A61C15/041; B; B29; B29C; B29C55/00; B29C55/005; B29D; B29D7/00; B29D7/01; B29K; B29K2023/00; B29K2023/04; B29K2023/06; B29K2023/0658; B29K2023/0683
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
162 words
A method for making a thermoplastic tape, ribbon or line material comprising the steps of: a--providing a melt crystallized precursor polyethylene tape having a MW over 300,000; b--immersing the precursor tape in a liquid bath around 130° C. for a time sufficient to cause said tape to swell into a pseudo-gel state; c--compressing the swollen tape lightly to remove the bath liquid; d--treating the tape in a solvent to remove all residual bath liquid; e--heating the tape to remove all residual solvent and thereby provide a dried porous product with higher porosity than the original melt crystallized tape; f--compressing the porous product under 100-30,000 psi depending on the thickness for a preselected time period; g--stretching the tape while at a temperature of 80°-130° C. to obtain a drawn product with increased mechanical properties including a modulus in the range of at least 0.5 GPa to 100 GPa and a tensile strength in the range of at least 0.1 GPa to 2 GPa.
Claim 2
Independent Claim
162 words
A method for making a thermoplastic tape, ribbon or line material comprising the steps of: a--providing a melt crystallized precursor polyethylene tape having a MW over 300,000; b--immersing the precursor tape in a liquid bath around 130° C. for a time sufficient to cause said tape to swell into a pseudo-gel state; c--compressing the swollen tape lightly to remove the bath liquid; d--treating the tape in a solvent to remove all residual bath liquid; e--heating the tape to remove all residual solvent and thereby provide a dried porous product with higher porosity than the original melt crystallized tape; f--compressing the porous product under 100-30,000 psi depending on the thickness for a preselected time period; g--stretching the tape while at a temperature of 80°-130° C. to obtain a drawn product with increased mechanical properties including a modulus in the range of at least 0.5 GPa to 100 GPa and a tensile strength in the range of at least 0.1 GPa to 2 GPa.
Claim 3
Dependent Claim
19 words
The method of claim 1 wherein the precursor tape is formed by skiving a solid block of polyethylene material.
Claim 4
Dependent Claim
16 words
The method of claim 1 wherein the precursor tape is obtained by a melt extrusion process.
Claim 5
Dependent Claim
31 words
The method of claim 1 wherein the precursor tape is prepared by powder compaction at a temperature range of 80° C. to 240° C. and under a pressure of 1000-60,000 psi.
Claim 6
Dependent Claim
31 words
The method of claim 1 wherein the precursor tape is prepared by powder sintering at a temperature range of 145° C. to 240° C. and under a pressure of 1000-60,000 psi.
Claim 7
Dependent Claim
20 words
The method of claim 1 wherein said precursor material has a thickness in the range of 0.001 to 0.1 inch.
Claim 8
Dependent Claim
26 words
The method of claim 1 wherein the liquid bath is paraffin oil maintained at a temperature 130°-160° C. for a period of 1 to 5 minutes.
Claim 9
Dependent Claim
30 words
The method of claim 4 including the step of predrawing the precursor tape to a draw ratio of around 6 before the final stretching step at a temperature 80°-130° C.
Claim 10
Dependent Claim
27 words
The method of claim 1 wherein the weight of the liquid taken by the precursor tape is about 3 to 5 times the weight of the tape.
Claim 11
Dependent Claim
34 words
The method of claim 1 wherein said precursor material is frozen with liquid nitrogen and then is exposed to a solvent at room temperature to cause said material to swell into a pseudo-gel state.
Claim 12
Dependent Claim
10 words
The method of claim 10 wherein said solvent is xylene.
Claim 13
Dependent Claim
14 words
The method of claim 1 wherein the swollen tape is compressed lightly between rolls.
Claim 14
Dependent Claim
27 words
The method of claim 1 wherein the compressed swollen tape is treated in hexane at room temperature for up to 10 minutes to remove residual bath liquid.
Claim 15
Dependent Claim
27 words
The method of claim 1 wherein the dried porous product is compressed at a temperature range of room temperature to 130° C. before the product is stretched.
Claim 16
Dependent Claim
23 words
The method of claim 1 including the step of combining said porous products with an additive material before the step of compressing it.
Claim 17
Dependent Claim
14 words
The method of claim 15 wherein said additive material is a flavor enhancing material.
Claim 18
Dependent Claim
13 words
The method of claim 15 wherein said additive material is a medicinal material.
References Cited (Backward Citations)
US4655769A
Cited
US4820466A
Cited
US4873034A
Cited
US5091133A
Cited
US5030402A
Cited
US5037928A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-04-17 | 1998-10-17 | 1999-04-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-04-17 | 2002-10-17 | 2003-04-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-04-17 | 2006-10-17 | 2007-04-18 | $7700.00 | Window Closed / Lapsed |