Methods for preparing conductive polyanilines
Assignee: University of Pennsylvania
•
Filing: 1993-08-12
•
Granted: 1995-04-04
•
Expires: 2013-08-12
Abstract
Abstract Methods for preparing conductive polyaniline forms are provided in which the conductivity of the polyaniline form can be substantially increased by contacting the polyaniline form with a phenolic compound that acts as a secondary dopant for the polyaniline. Generally, a doped polyaniline solution is prepared in which the polyaniline is initially doped by a protonic acid and a doped polyaniline form is then prepared from this solution. The polyaniline form can then be contacted with the phenolic compound in either its vapor or liquid state, however it is preferred that the polyaniline form be maintained in either the gelatinous or solid state during the contacting step. The conductivity of the polyaniline form can be raised by a factor of up to about 500-1000.
Inventors
- 👤 Alan G. MacDiarmid
- 👤 You N. Xia
- 👤 Joanna M. Wiesinger
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 01:38
CPC Classifications
H; H01; H01B; H01B1/00; H01B1/06; H01B1/12; H01B1/124; H01B1/128; C; C08; C08G; C08G73/00; C08G73/02; C08G73/026; C08G73/0266; C08L; C08L79/00; C08L79/02
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
69 words
A method for processing polyaniline, comprising contacting a substantially solid polyaniline having a determinable conductivity with a phenolic compound comprising phenol, or mono- or disubstituted phenolic compound wherein said substituent comprises hydroxyl, halogen and an alkyl or alkoxy having 1-20 carbon atoms under conditions which are effective to increase said conductivity by at least a factor of 10 while maintaining said polyaniline in either a gelatinous or solid state.
Claim 2
Independent Claim
69 words
A method for processing polyaniline, comprising contacting a substantially solid polyaniline having a determinable conductivity with a phenolic compound comprising phenol, or mono- or disubstituted phenolic compound wherein said substituent comprises hydroxyl, halogen and an alkyl or alkoxy having 1-20 carbon atoms under conditions which are effective to increase said conductivity by at least a factor of 10 while maintaining said polyaniline in either a gelatinous or solid state.
Claim 3
Dependent Claim
29 words
The method of claim 1 wherein said contacting comprises wetting said polyaniline with said phenolic compound up to about the saturation point of said polyaniline in said phenolic compound.
Claim 4
Dependent Claim
30 words
The method of claim 2 wherein the phenolic compound comprises a mono- or di-substituted phenolic compound, wherein said substituent comprises hydroxyl, a halogen, and an alkyl having 1-20 carbon atoms.
Claim 5
Dependent Claim
14 words
The method of claim 3 wherein the phenolic compound comprises a mono-substituted phenolic compound.
Claim 6
Dependent Claim
36 words
The method of claim 2 wherein the phenolic compound consists of a mono- or di-substituted phenolic compound, wherein said substituent group is selected from the group consisting of hydroxy, halogen, and alkyl having 1-20 carbon atoms.
Claim 7
Dependent Claim
31 words
The method of claim 2 wherein said phenolic compound is a mono-substituted phenolic compound and wherein said substituent is selected from the group consisting of hydroxy, chlorine, fluorine, methyl, and ethyl.
Claim 8
Dependent Claim
18 words
The method of claim 2 wherein said phenolic compound comprises cresol, 3-ethylphenol, 2-cholophenol, 2-fluorophenol, phenol, or mixtures thereof.
Claim 9
Dependent Claim
27 words
The method of claim 1 wherein said contacting consists essentially of exposing said polyaniline to said phenolic compound wherein said phenolic compound is in the gaseous state.
Claim 10
Dependent Claim
31 words
The method of claim 8 wherein the phenolic compound comprises a mono- or di-substituted phenolic compound, and wherein said substituent comprises hydroxyl, a halogen, and an alkyl having 1-20 carbon atoms.
Claim 11
Dependent Claim
14 words
The method of claim 9 wherein the phenolic compound comprises a mono-substituted phenolic compound.
Claim 12
Dependent Claim
38 words
The method of claim 8 wherein the phenolic compound consists of a mono- or di-substituted phenolic compound, and wherein said substituent group is selected from the group consisting of hydroxyl, a halogen, and alkyl having 1-20 carbon atoms.
Claim 13
Dependent Claim
31 words
The method of claim 8 wherein said phenolic compound is a mono-substituted phenolic compound and wherein said substituent is selected from the group consisting of hydroxyl, chlorine, fluorine, methyl, and ethyl.
Claim 14
Dependent Claim
18 words
The method of claim 8 wherein said phenolic compound comprises cresol, 3-ethylphenol, 2-cholophenol, 2-fluorophenol, phenol, or mixtures thereof.
Claim 15
Independent Claim
115 words
A method for selectively increasing the conductivity of polyaniline, comprising: (a) providing a solution of polyaniline in the emeraldine oxidation state, a dopant comprising a protonic acid, and a solvent for the polyaniline; (b) preparing a substantially solid polyaniline form from the solution of step a) having a conductivity of below about 5 S/cm; and (c) contacting said polyaniline form with a phenolic compound comprising phenol, or mono- or di-substituted phenolic compound, wherein said substituent comprises hydroxyl, a halogen and an alkyl or alkoxy having 1-20 carbon atoms under conditions which are effective to increase said conductivity to at least about 25 S/cm while maintaining said polyaniline form in either the gelatinous or solid state.
Claim 16
Independent Claim
115 words
A method for selectively increasing the conductivity of polyaniline, comprising: (a) providing a solution of polyaniline in the emeraldine oxidation state, a dopant comprising a protonic acid, and a solvent for the polyaniline; (b) preparing a substantially solid polyaniline form from the solution of step a) having a conductivity of below about 5 S/cm; and (c) contacting said polyaniline form with a phenolic compound comprising phenol, or mono- or di-substituted phenolic compound, wherein said substituent comprises hydroxyl, a halogen and an alkyl or alkoxy having 1-20 carbon atoms under conditions which are effective to increase said conductivity to at least about 25 S/cm while maintaining said polyaniline form in either the gelatinous or solid state.
Claim 17
Dependent Claim
23 words
The method of claim 14 wherein said conductivity is increased to at least about 50 S/cm by the contacting with the phenolic compound.
Claim 18
Dependent Claim
23 words
The method of claim 14 wherein said conductivity is increased to at least about 100 S/cm by the contacting with the phenolic compound.
Claim 19
Dependent Claim
20 words
The method of claim 16 wherein said conductivity of said polyaniline form of step (b) is below about 1 S/cm.
Claim 20
Dependent Claim
34 words
The method of claim 14 wherein said dopant protonic acid is selected from the group consisting of hydrochloric acid, hydrobromic acid, sulfuric acid, methane sulfonic acid, benzene sulfonic, toluene sulfonic acid, and combinations thereof.
Claim 21
Dependent Claim
18 words
The method of claim 14 wherein said solvent for the polyaniline comprises chloroform, NMP, acetic acid and DMF.
Claim 22
Dependent Claim
29 words
The method of claim 19 wherein said phenolic compound comprises a mono- or di-substituted phenol, wherein said substituent comprises hydroxyl, a halogen, or an alkyl having 1-20 carbon atoms.
Claim 23
Dependent Claim
30 words
The method of claim 19 wherein said phenolic compound is a mono-substituted phenol and wherein said substituent is selected from the group consisting of hydroxyl, chlorine, fluorine, methyl, and ethyl.
Claim 24
Dependent Claim
18 words
The method of claim 19 wherein said phenolic compound comprises cresol, 3-ethylphenol, 2-cholophenol, 2-fluorophenol, phenol, or mixtures thereof.
Claim 25
Independent Claim
140 words
A method of increasing the conductivity of an emeraldine base polyaniline form, comprising: (a) providing a polyaniline form prepared from a solution comprising emeraldine base polyaniline; (b) preparing a substantially solid polyaniline form from said solution, said polyaniline form comprising polyaniline in the emeraldine base state; (c) doping said polyaniline form with a protonic acid, said doped polyaniline form having a determinable conductivity and being in a substantially solid form; (d) increasing the conductivity of said doped polyaniline form by contacting said doped polyaniline form with a phenolic compound comprising phenol, or mono- or di-substituted phenolic compound, wherein said substituent comprises hydroxyl, a halogen, and an ankyl or alkoxy having 1-20 carbon atoms under conditions which are effective to increase said conductivity by at least a factor of 10 while maintaining said polyaniline in either a gelatinous or solid state.
Claim 26
Independent Claim
140 words
A method of increasing the conductivity of an emeraldine base polyaniline form, comprising: (a) providing a polyaniline form prepared from a solution comprising emeraldine base polyaniline; (b) preparing a substantially solid polyaniline form from said solution, said polyaniline form comprising polyaniline in the emeraldine base state; (c) doping said polyaniline form with a protonic acid, said doped polyaniline form having a determinable conductivity and being in a substantially solid form; (d) increasing the conductivity of said doped polyaniline form by contacting said doped polyaniline form with a phenolic compound comprising phenol, or mono- or di-substituted phenolic compound, wherein said substituent comprises hydroxyl, a halogen, and an ankyl or alkoxy having 1-20 carbon atoms under conditions which are effective to increase said conductivity by at least a factor of 10 while maintaining said polyaniline in either a gelatinous or solid state.
References Cited (Backward Citations)
US5177187A
Cited
US5147913A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-04-03 | 1998-10-03 | 1999-04-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-04-03 | 2002-10-03 | 2003-04-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-04-03 | 2006-10-03 | 2007-04-04 | $7700.00 | Window Closed / Lapsed |