Method of fabricating a semiconductor device having a triple well structure
Assignee: Sharp Corp
•
Filing: 1992-10-02
•
Granted: 1995-03-14
•
Expires: 2012-10-02
Abstract
Abstract A method of fabricating a semiconductor device having a p-type semiconductor substrate and a p-well for memory cells which is formed in the substrate is disclosed. N-type impurities are implanted into a region of the substrate in which the p-well for memory cells is to be formed. Then, the region is selectively and thermally oxidized to form an oxide film on the first region, and the n-type impurities are simultaneously diffused in the substrate. After the oxide film is removed, the p-well is formed within the region of the substrate in which the n-type impurities are diffused.
Inventors
- 👤 Katsuji Iguchi
- 👤 Makoto Tanigawa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 05:50
CPC Classifications
H; H10; H10B; H10B12/00; H10B12/30
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
277 words
A method of fabricating a semiconductor device having a semiconductor substrate of a first conductivity type and a first well of the first conductivity type which is formed in the semiconductor substrate, the method comprising the steps of: forming an anti-oxidation film on the semiconductor substrate; selectively removing the anti-oxidation film in a first region of the semiconductor substrate in which the first well is to be formed; selectively implanting impurities of a second conductivity type into the first region of the semiconductor substrate; selectively and thermally oxidizing the first region to form an oxide film on the first region and diffusing the impurities of the second conductivity type in the semiconductor substrate, thereby forming a deep diffusion including the impurities of the second conductivity type; selectively removing the anti-oxidation film in a second region of the semiconductor substrate in which a second well of the second conductivity type is to be formed; implanting the impurities of the second conductivity type into the second region of the semiconductor substrate; selectively and thermally oxidizing the second region to form another oxide film on the second region and diffusing the impurities of the second conductivity type in the semiconductor substrate, thereby forming the second well including the impurities of the second conductivity type, the second well being formed adjacent to the deep diffusion but having a depth which is smaller than that of the deep diffusion; removing the oxide films on the first and second regions so as to make the top surface of the first region lower than the top surface of second region; and forming the first well of the first conductivity type within the deep diffusion.
Claim 2
Independent Claim
277 words
A method of fabricating a semiconductor device having a semiconductor substrate of a first conductivity type and a first well of the first conductivity type which is formed in the semiconductor substrate, the method comprising the steps of: forming an anti-oxidation film on the semiconductor substrate; selectively removing the anti-oxidation film in a first region of the semiconductor substrate in which the first well is to be formed; selectively implanting impurities of a second conductivity type into the first region of the semiconductor substrate; selectively and thermally oxidizing the first region to form an oxide film on the first region and diffusing the impurities of the second conductivity type in the semiconductor substrate, thereby forming a deep diffusion including the impurities of the second conductivity type; selectively removing the anti-oxidation film in a second region of the semiconductor substrate in which a second well of the second conductivity type is to be formed; implanting the impurities of the second conductivity type into the second region of the semiconductor substrate; selectively and thermally oxidizing the second region to form another oxide film on the second region and diffusing the impurities of the second conductivity type in the semiconductor substrate, thereby forming the second well including the impurities of the second conductivity type, the second well being formed adjacent to the deep diffusion but having a depth which is smaller than that of the deep diffusion; removing the oxide films on the first and second regions so as to make the top surface of the first region lower than the top surface of second region; and forming the first well of the first conductivity type within the deep diffusion.
Claim 3
Dependent Claim
37 words
A method according to claim 1, wherein the method further comprises a step of forming a third well of the first conductivity type in a third region excluding the first and second regions of the semiconductor substrate.
Claim 4
Independent Claim
248 words
A method of fabricating a semiconductor device having a semiconductor substrate of a first conductivity type and a first well of the first conductivity type which is formed in the semiconductor substrate, the method comprising the steps of: forming an anti-oxidation film on the semiconductor substrate; selectively removing the anti-oxidation film in a first region of the semiconductor substrate in which the first well is to be formed; selectively implanting impurities of a second conductivity type into the first region of the semiconductor substrate; selectively and thermally oxidizing the first region to form an oxide film on the first region and diffusing the impurities of the second conductivity type in the semiconductor substrate, thereby forming a deep diffusion including the impurities of the second conductivity type; selectively removing the anti-oxidation film in a second region of the semiconductor substrate in which a second well of the second conductivity type is to be formed; implanting the impurities of the second conductivity type into the second region of the semiconductor substrate; selectively and thermally oxidizing the second region to form another oxide film on the second region and diffusing the impurities of the second conductivity type in the semiconductor substrate, thereby forming the second well including the impurities of the second conductivity type, wherein part of the second well is in contact with the deep diffusion; removing the oxide films on the first and second regions, and; forming the first well of the first conductivity type within the deep diffusion.
Claim 5
Independent Claim
248 words
A method of fabricating a semiconductor device having a semiconductor substrate of a first conductivity type and a first well of the first conductivity type which is formed in the semiconductor substrate, the method comprising the steps of: forming an anti-oxidation film on the semiconductor substrate; selectively removing the anti-oxidation film in a first region of the semiconductor substrate in which the first well is to be formed; selectively implanting impurities of a second conductivity type into the first region of the semiconductor substrate; selectively and thermally oxidizing the first region to form an oxide film on the first region and diffusing the impurities of the second conductivity type in the semiconductor substrate, thereby forming a deep diffusion including the impurities of the second conductivity type; selectively removing the anti-oxidation film in a second region of the semiconductor substrate in which a second well of the second conductivity type is to be formed; implanting the impurities of the second conductivity type into the second region of the semiconductor substrate; selectively and thermally oxidizing the second region to form another oxide film on the second region and diffusing the impurities of the second conductivity type in the semiconductor substrate, thereby forming the second well including the impurities of the second conductivity type, wherein part of the second well is in contact with the deep diffusion; removing the oxide films on the first and second regions, and; forming the first well of the first conductivity type within the deep diffusion.
Claim 6
Independent Claim
242 words
A method of fabricating a semiconductor device having a semiconductor substrate of a first conductivity type and a first well of the first conductivity type which is formed in the semiconductor substrate, the method comprising the steps of: forming an anti-oxidation film on the semiconductor substrate; selectively removing the anti-oxidation film in a first region of the semiconductor substrate in which the first well is to be formed; selectively implanting impurities of a second conductivity type into the first region of the semiconductor substrate; selectively and thermally oxidizing the first region to form an oxide film on the first region and diffusing the impurities of the second conductivity type in the semiconductor substrate, thereby forming a deep diffusion including the impurities of the second conductivity type; selectively removing the anti-oxidation film in a second region of the semiconductor substrate in which a second well of the second conductivity type is to be formed; implanting the impurities of the second conductivity type into the second region of the semiconductor substrate; selectively and thermally oxidizing the second region to form another oxide film on the second region and diffusing the impurities of the second conductivity type in the semiconductor substrate, thereby forming the second well including the impurities of the second conductivity type, the second well surrounding the deep diffusion;, removing the oxide films on the first and second regions; and forming the first well of the first conductivity type within the deep diffusion.
Claim 7
Independent Claim
242 words
A method of fabricating a semiconductor device having a semiconductor substrate of a first conductivity type and a first well of the first conductivity type which is formed in the semiconductor substrate, the method comprising the steps of: forming an anti-oxidation film on the semiconductor substrate; selectively removing the anti-oxidation film in a first region of the semiconductor substrate in which the first well is to be formed; selectively implanting impurities of a second conductivity type into the first region of the semiconductor substrate; selectively and thermally oxidizing the first region to form an oxide film on the first region and diffusing the impurities of the second conductivity type in the semiconductor substrate, thereby forming a deep diffusion including the impurities of the second conductivity type; selectively removing the anti-oxidation film in a second region of the semiconductor substrate in which a second well of the second conductivity type is to be formed; implanting the impurities of the second conductivity type into the second region of the semiconductor substrate; selectively and thermally oxidizing the second region to form another oxide film on the second region and diffusing the impurities of the second conductivity type in the semiconductor substrate, thereby forming the second well including the impurities of the second conductivity type, the second well surrounding the deep diffusion;, removing the oxide films on the first and second regions; and forming the first well of the first conductivity type within the deep diffusion.
Claim 8
Dependent Claim
34 words
A method according to claim 1, wherein an alignment mark is formed on the semiconductor substrate when the oxide film on the first region is formed, the alignment mark being used for alignment thereafter.
Claim 9
Dependent Claim
42 words
A method according to claim 1, wherein the semiconductor device is a memory device, the method further comprising the steps of: forming a memory cell in the deep diffusion; and forming a peripheral circuit on the semiconductor substrate excluding the deep diffusion.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-03-13 | 1998-09-12 | 1999-03-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-03-13 | 2002-09-12 | 2003-03-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-03-13 | 2006-09-12 | 2007-03-14 | $7700.00 | Window Closed / Lapsed |