US5389581A
Expired / Lapsed
US
⏱️ 0.0 years remaining
High density TEOS-based film for intermetal dielectrics
Assignee: Intel Corp
•
Filing: 1993-05-25
•
Granted: 1995-02-14
•
Expires: 2013-05-25
Abstract
Abstract A method of forming a device and the device itself that utilizes a high density plasma-enhanced TEOS-based intermetal dielectric is disclosed. The high density is accomplished though the use of higher RF power and higher oxygen flow rate so that the TEOS is more completely oxidized. The higher density intermetal dielectric absorbs water from air slower than a standard intermetal dielectric film. This lower water absorbance reduces the amount of water in the device and reduces hot electron induced device degradation.
Inventors
- 👤 Philip Freiberger
- 👤 Ragupathy V. Giridhar
- 👤 Brett Huff
- 👤 Farhad K. Moghadam
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 06:00
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/69; H10P14/692; H10P14/6921; H10P14/69215; H10W; H10W20/00; H10W20/01; H10W20/071; H10P14/63; H10P14/6326; H10P14/6328; H10P14/6334; H10P14/6336
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
158 words
A method of forming a semiconductor device which comprises the steps of: (a) providing a substrate with a first interconnection metal layer; (b) forming a dielectric layer directly on said first interconnection layer, said dielectric layer being formed by a method including using a plasma-enhanced reaction, said reaction being performed at a radio frequency of approximately 13.56 MHz, with a flow rate of an oxygen containing chemical and a flow rate of tetraethyl orthosilicate (TEOS) such that an equivalent atomic flow rate of oxygen in said oxygen containing chemical on a mole basis is between two times said flow rate of TEOS on a mole basis and about six times said flow rate of TEOS on a mole basis; and (c) forming a second interconnection layer directly on said dielectric layer produced by said method, said dielectric layer produced by said method being the sole dielectric layer separating said second interconnection layer from said first interconnection metal layer.
Claim 2
Independent Claim
158 words
A method of forming a semiconductor device which comprises the steps of: (a) providing a substrate with a first interconnection metal layer; (b) forming a dielectric layer directly on said first interconnection layer, said dielectric layer being formed by a method including using a plasma-enhanced reaction, said reaction being performed at a radio frequency of approximately 13.56 MHz, with a flow rate of an oxygen containing chemical and a flow rate of tetraethyl orthosilicate (TEOS) such that an equivalent atomic flow rate of oxygen in said oxygen containing chemical on a mole basis is between two times said flow rate of TEOS on a mole basis and about six times said flow rate of TEOS on a mole basis; and (c) forming a second interconnection layer directly on said dielectric layer produced by said method, said dielectric layer produced by said method being the sole dielectric layer separating said second interconnection layer from said first interconnection metal layer.
Claim 3
Dependent Claim
25 words
The method of claim 1 wherein said oxygen containing chemical is selected from the group consisting of oxygen, ozone, nitrous oxide, and any combination thereof.
Claim 4
Dependent Claim
31 words
The method of claim 2 wherein said TEOS flow rate is between about 400 and about 600 SCCM and said oxygen flow rate is between about 400 and about 1800 SCCM.
Claim 5
Dependent Claim
31 words
The method of claim 2 wherein said TEOS flow rate is between about 400 and about 600 SCCM and said ozone flow rate is between about 266 and about 1200 SCCM.
Claim 6
Dependent Claim
32 words
The method of claim 2 wherein said TEOS flow rate is between about 400 and about 600 SCCM and said nitrous oxide flow rate is between about 800 and about 3600 SCCM.
Claim 7
Dependent Claim
26 words
The method of claim 1 wherein said reaction takes place at an RF power, said RF power being between about 450 watts and about 500 watts.
Claim 8
Dependent Claim
34 words
The method of claim 1 wherein said dielectric has an HF etch rate between about 1.4 and about 1.7 times greater than an HF etch rate of silicon dioxide thermally grown from monocrystalline silicon.
Claim 9
Independent Claim
172 words
A method of forming a semiconductor device, including a PECVD oxide layer as an IMD, wherein said method comprises the steps of: (a) providing a substrate with a first interconnection metal layer; (b) forming a dielectric layer directly on said first interconnection metal layer, said dielectric layer being formed by a method including using a plasma-enhanced reaction including a combination of a flow rate of an oxygen containing chemical and a flow rate of TEOS such that an equivalent atomic flow rate of oxygen in said oxygen containing chemical on a mole basis is between two times said flow rate of TEOS on a mole basis and about six times said flow rate of TEOS on a mole basis, said reaction being performed at a radio frequency of approximately 13.56 MHz and at an RF power; and (c) forming a second interconnection layer directly on said dielectric layer, said dielectric layer produced by said method and being the sole dielectric layer separating said second interconnection layer from said first interconnection metal layer.
Claim 10
Independent Claim
172 words
A method of forming a semiconductor device, including a PECVD oxide layer as an IMD, wherein said method comprises the steps of: (a) providing a substrate with a first interconnection metal layer; (b) forming a dielectric layer directly on said first interconnection metal layer, said dielectric layer being formed by a method including using a plasma-enhanced reaction including a combination of a flow rate of an oxygen containing chemical and a flow rate of TEOS such that an equivalent atomic flow rate of oxygen in said oxygen containing chemical on a mole basis is between two times said flow rate of TEOS on a mole basis and about six times said flow rate of TEOS on a mole basis, said reaction being performed at a radio frequency of approximately 13.56 MHz and at an RF power; and (c) forming a second interconnection layer directly on said dielectric layer, said dielectric layer produced by said method and being the sole dielectric layer separating said second interconnection layer from said first interconnection metal layer.
Claim 11
Dependent Claim
25 words
The method of claim 8 wherein said oxygen containing chemical is selected from the group consisting of oxygen, ozone, nitrous oxide, and any combination thereof.
Claim 12
Dependent Claim
31 words
The method of claim 9 wherein said TEOS flow rate is between about 400 and about 600 SCCM and said oxygen flow rate is between about 400 and about 1800 SCCM.
Claim 13
Dependent Claim
31 words
The method of claim 9 wherein said TEOS flow rate is between about 400 and about 600 SCCM and said ozone flow rate is between about 266 and about 1200 SCCM.
Claim 14
Dependent Claim
32 words
The method of claim 9 wherein said TEOS flow rate is between about 400 and about 600 SCCM and said nitrous oxide flow rate is between about 800 and about 3600 SCCM.
Claim 15
Dependent Claim
34 words
The method of claim 10 wherein said dielectric has an HF etch rate between about 1.4 and about 1.7 times greater than an HF etch rate of silicon dioxide thermally grown from monocrystalline silicon.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-02-13 | 1998-08-15 | 1999-02-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-02-13 | 2002-08-15 | 2003-02-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-02-13 | 2006-08-15 | 2007-02-14 | $7700.00 | Window Closed / Lapsed |