Diamond-coated hard material and a process for the production thereof
Assignee: Sumitomo Electric Industries Ltd
•
Filing: 1992-07-17
•
Granted: 1994-12-06
•
Expires: 2012-07-17
Abstract
Abstract PCT No. PCT/JP92/00919 Sec. 371 Date Apr. 27, 1993 Sec. 102(e) Date Apr. 27, 1993 PCT Filed Jul. 17, 1992 PCT Pub. No. WO93/02022 PCT Pub. Date Feb. 4, 1993.This invention relates to a diamond-coated hard material and a process for the production of the same. The feature of the diamond-coated hard material consists in that in a diamond-coated hard material comprising a substrate of a tungsten carbide-based cemented carbide having a diamond-coated layer provided on the surface of the substrate, a surface-modified layer containing no binder phase or containing a binder phase in a proportion of less than in the interior part of the substrate is present on the outermost surface of the substrate. This hard material can be produced by converting the substrate material into a sintered or heat treated surface or skin and then coating with diamond. The diamond-coated hard material of the present invention has such a high wear resistance and excellent bonding strength to the substrate that it can favorably be applied to various tools, parts, grinding wheels, etc.
Inventors
- 👤 Naoya Omori
- 👤 Mitsunori Kobayashi
- 👤 Toshio Nomura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 04:20
CPC Classifications
C; C23; C23C; C23C30/00; C23C30/005; C22; C22C; C22C1/00; C22C1/04; C22C1/05; C22C1/051; B; B22; B22F; B22F2201/00; B22F2201/02; B22F2201/04; B22F2207/00; B22F2207/01; B22F2207/03; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/12021; Y10T428/12028; Y10T428/12049; Y10T428/12056; Y10T428/12146
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
116 words
A diamond-coated hard material comprising a substrate of a tungsten carbide-based cemented carbide containing a hard phase consisting of tungsten carbide, or a hard phase consisting of a solid solution of tungsten carbide and at least one of carbides, nitrides and carbonitrides of Group 4B, 5B and 6B elements, exclusive of tungsten, of the Periodic Table, a binder phase, and unavoidable impurities; a surface-modified layer formed on the surface of the substrate; and a diamond- or diamond-like carbon-coated layer, wherein the surface-modified layer consists of binder phase-free tungsten and/or tungsten carbide, or a binder phase-containing tungsten and/or tungsten carbide in which the proportion of binder phase is less than in the interior part of the substrate.
Claim 2
Dependent Claim
116 words
A diamond-coated hard material comprising a substrate of a tungsten carbide-based cemented carbide containing a hard phase consisting of tungsten carbide, or a hard phase consisting of a solid solution of tungsten carbide and at least one of carbides, nitrides and carbonitrides of Group 4B, 5B and 6B elements, exclusive of tungsten, of the Periodic Table, a binder phase, and unavoidable impurities; a surface-modified layer formed on the surface of the substrate; and a diamond- or diamond-like carbon-coated layer, wherein the surface-modified layer consists of binder phase-free tungsten and/or tungsten carbide, or a binder phase-containing tungsten and/or tungsten carbide in which the proportion of binder phase is less than in the interior part of the substrate.
Claim 3
Dependent Claim
136 words
A diamond-coated hard material comprising a substrate of a tungsten carbide-based cemented carbide having a diamond-coated layer provided on the surface of the substrate, in which a hard phase exists on the surface of the substrate in a proportion larger than that in the interior part of the substrate, the hard phase being composed of (1) WC and/or (2) at least one solid solution of WC and at least one of carbides, nitrides, carbonitrides, oxides, borides, borocarbides, boronitrides and borocarbonitrides of Group 4B, 5B and 6B elements, exclusive of W, of the Periodic Table and/or (3) at least one of carbides, nitrides, carbonitrides, oxides, borides, borocarbides, boronitrides and borocarbonitrides of Group 4B, 5B and 6B elements, exclusive of W, of the Periodic Table or at least one solid solution of at least two of these compounds.
Claim 4
Dependent Claim
136 words
A diamond-coated hard material comprising a substrate of a tungsten carbide-based cemented carbide having a diamond-coated layer provided on the surface of the substrate, in which a hard phase exists on the surface of the substrate in a proportion larger than that in the interior part of the substrate, the hard phase being composed of (1) WC and/or (2) at least one solid solution of WC and at least one of carbides, nitrides, carbonitrides, oxides, borides, borocarbides, boronitrides and borocarbonitrides of Group 4B, 5B and 6B elements, exclusive of W, of the Periodic Table and/or (3) at least one of carbides, nitrides, carbonitrides, oxides, borides, borocarbides, boronitrides and borocarbonitrides of Group 4B, 5B and 6B elements, exclusive of W, of the Periodic Table or at least one solid solution of at least two of these compounds.
Claim 5
Dependent Claim
159 words
A diamond-coated hard material comprising a substrate of a tungsten carbide-based cemented carbide having a diamond-coated layer provided on the surface of the substrate, in which a surface-modified layer is present on the outermost surface of the substrate and the surface-modified layer contains no binder phase or contains a binder phase in a proportion of less than in the interior part of the substrate, and the surface-modified layer has a hard phase composed of (1) WC and/or (2) at least one solid solution of WC and at least one of carbides, nitrides, carbonitrides, oxides, borides, borocarbides, boronitrides and borocarbonitrides of Group 4B, 5B and 6B elements, exclusive of W, of the Periodic Table and/or (3) at least one of carbides, nitrides, carbonitrides, oxides, borides, borocarbides, boronitrides and borocarbonitrides of Group 4B, 5B and 6B elements, exclusive of W, of the Periodic Table or at least one solid solution of at least two of these compounds and (4) unavoidable impurities.
Claim 6
Dependent Claim
159 words
A diamond-coated hard material comprising a substrate of a tungsten carbide-based cemented carbide having a diamond-coated layer provided on the surface of the substrate, in which a surface-modified layer is present on the outermost surface of the substrate and the surface-modified layer contains no binder phase or contains a binder phase in a proportion of less than in the interior part of the substrate, and the surface-modified layer has a hard phase composed of (1) WC and/or (2) at least one solid solution of WC and at least one of carbides, nitrides, carbonitrides, oxides, borides, borocarbides, boronitrides and borocarbonitrides of Group 4B, 5B and 6B elements, exclusive of W, of the Periodic Table and/or (3) at least one of carbides, nitrides, carbonitrides, oxides, borides, borocarbides, boronitrides and borocarbonitrides of Group 4B, 5B and 6B elements, exclusive of W, of the Periodic Table or at least one solid solution of at least two of these compounds and (4) unavoidable impurities.
Claim 7
Dependent Claim
127 words
The diamond-coated hard material as claimed in any of claims 1 to 3 or 6, wherein the material of the substrate is a WC-based cemented carbide comprising a hard phase consisting of (1) WC and/or (2) at least one solid solution of WC and at least one of carbides, nitrides, carbonitrides, oxides, borides, borocarbides, boronitrides and borocarbonitrides of Group 4B, 5B and 6B elements, exclusive of W, of the Periodic Table and/or (3) at least one of carbides, nitrides, carbonitrides, oxides, borides, borocarbides, boronitrides and borocarbonitrides of Group 4B, 5B and 6B elements, exclusive of W, of the Periodic Table or at least one solid solution of at least two of these compounds, (4) a binder phase consisting of an iron group metal and (5) unavoidable impurities.
Claim 8
Dependent Claim
25 words
The diamond-coated hard material as claimed in any of claims 1 to 3, wherein the surface-modified layer has a thickness of 0.01 to 200 μm.
Claim 9
Dependent Claim
54 words
A diamond-coated hard material comprising a substrate of a tungsten carbide-based cemented carbide having a diamond-coated layer provided on the surface of the substrate, in which at least a part of the surface of the substrate is a sintered surface and the diamond-coated layer is formed on at least part of the sintered surface.
Claim 10
Dependent Claim
54 words
A diamond-coated hard material comprising a substrate of a tungsten carbide-based cemented carbide having a diamond-coated layer provided on the surface of the substrate, in which at least a part of the surface of the substrate is a sintered surface and the diamond-coated layer is formed on at least part of the sintered surface.
Claim 11
Dependent Claim
55 words
The diamond-coated hard material as claimed in any of claims 1 to 3, or 6 wherein at least a part of the surface of the substrate is a sintered surface and the diamond-coated layer is formed on at least part of the sintered surface, from the surface of which the binder phase has been removed.
Claim 12
Dependent Claim
74 words
A diamond-coated hard material comprising a substrate of a tungsten carbide-based cemented carbide having a diamond-coated layer provided on the surface of the substrate, in which the substrate is worked in an arbitrary shape and subjected to a heat treatment to convert at least a part of the substrate surface into a heat treated surface, and the diamond-coated layer is formed on at least a part or whole of the surface of the substrate.
Claim 13
Dependent Claim
74 words
A diamond-coated hard material comprising a substrate of a tungsten carbide-based cemented carbide having a diamond-coated layer provided on the surface of the substrate, in which the substrate is worked in an arbitrary shape and subjected to a heat treatment to convert at least a part of the substrate surface into a heat treated surface, and the diamond-coated layer is formed on at least a part or whole of the surface of the substrate.
Claim 14
Dependent Claim
74 words
The diamond-coated hard material as claimed in any of claims 1 to 3, or 6 wherein the substrate is worked in an arbitrary shape and subjected to a heat treatment to convert at least a part of the substrate surface into a heat treated surface, and the diamond-coated layer is formed on at least a part or whole of the heat treated surface, from the surface of which the binder phase has been removed.
Claim 15
Dependent Claim
40 words
The diamond-coated hard material as claimed in any of claims 1 to 3, or 6 wherein the surface roughness of the substrate surface to be coated with a diamond-coated layer is represented by an Rmax of at least 1.5 μm.
Claim 16
Dependent Claim
35 words
The diamond-coated hard material as claimed in any of claims 1 to 3, or 6 wherein in the substrate, the binder phase is substantially continuously or stepwise decreased from the interior part toward the surface.
Claim 17
Dependent Claim
31 words
The diamond-coated hard material as claimed in any of claims 1 to 3, or 6 wherein in the substrate, the hard phase has a grain diameter of at least 1 μm.
Claim 18
Dependent Claim
28 words
The diamond-coated hard material as claimed in any of claims 1 to 3, or 6 wherein the diamond-coated layer has 8 layer thickness of 0.5 to 300 μm.
Claim 19
Dependent Claim
32 words
The diamond-coated hard material as claimed in any of claims 1 to 3, or 6 wherein the surface roughness of the diamond-coated layer is represented by Rmax of at most 0.5 μm.
Claim 20
Dependent Claim
41 words
The diamond-coated hard material as claimed in any of claims 1 to 3, or 6 wherein the hardness of the surface part of the substrate, by Vickers hardness, is higher by at least 5% than that of the interior part thereof.
Claim 21
Dependent Claim
80 words
The diamond-coated hard material as claimed in any of claims 1 to 3, or 6 wherein in the diffraction curve by Cu-Aα line from the surface of the diamond-coated layer, the diffraction intensity ratio of (101) plane of tungsten carbide is smaller than that of (200) plane of the B1 solid solution of at least one of carbides, nitrides, carbonitrides, oxides, borides, borocarbides, boronitrides and borocarbonitrides of Group 4B, 5B and 6B elements exclusive of W of the Periodic Table.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-12-05 | 1998-06-06 | 1998-12-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-12-05 | 2002-06-06 | 2002-12-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-12-05 | 2006-06-06 | 2006-12-06 | $7700.00 | Window Closed / Lapsed |