US5362513A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of manufacturing a pattern of conductive fine-line films and setting ink used for the same
Assignee: Panasonic Holdings Corp
•
Filing: 1991-05-10
•
Granted: 1994-11-08
•
Expires: 2011-05-10
Abstract
Abstract A pattern forming method comprises at least a lower pattern forming step for printing a setting ink on a substrate, a setting step for setting the setting ink, an upper layer pattern forming step for forming a metalo-organic compound paste layer on the lower layer pattern by a printing method, and a firing step for firing at high temperature to remove the lower layer pattern. In the upper layer pattern forming step, the metalo-organic compound paste is printed so that the metalo-organic compound paste may be divided on the hardened setting ink so as to fill up gaps of the lower layer pattern. Otherwise the metalo-organic compound paste is printed on the hardened setting ink, and the metalo-organic compound paste is mechanically cut off, before the metalo-organic compound paste is dried, on the hardened setting ink, thereby forming an upper layer pattern. The setting ink comprises a thermo-setting resin, a setting agent, and an organic solvent, with an amount of nonvolatile materials of 50 to 70 wt. %, or comprises a carbon powder, a thermo-setting resin, a setting agent and an organic solvent, with an amount of nonvolatile materials of 60 to 80 wt. %.
Inventors
- 👤 Mikinari Shimada
- 👤 Hirotoshi Watanabe
- 👤 Satoru Fujii
- 👤 Masato Hagino
- 👤 Masahide Tsukamoto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 23:38
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/10; H05K3/12; H05K3/1275; H05K3/02; H05K3/04; H05K3/046; H05K3/048; H05K1/00; H05K1/02; H05K1/09; H05K1/092; H05K2203/00; H05K2203/01; H05K2203/0104; H05K2203/0113; H05K2203/0143; H05K2203/0195; H05K2203/05; H05K2203/0502; H05K2203/0534; H05K2203/12; H05K2203/121
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
152 words
A method of manufacturing a pattern of conductive fine-line films, comprising the steps of: printing a setting ink on a substrate to form a lower layer pattern so that exposed portions of the substrate separated by the lower pattern remain on the substrate, the setting ink being removable by firing at high temperature; setting the setting ink of the lower layer pattern; printing a metalo-organic compound paste layer on said substrate on which the lower pattern has been formed to form an upper layer pattern so that all of the exposed portions of the substrate and at least a part of the lower layer pattern are covered by the upper layer pattern; and firing at high temperature to remove the lower layer pattern and a portion of the upper layer pattern covering the lower layer pattern leaving the remaining portion of the upper layer pattern as a conductive pattern on a substrate.
Claim 2
Independent Claim
152 words
A method of manufacturing a pattern of conductive fine-line films, comprising the steps of: printing a setting ink on a substrate to form a lower layer pattern so that exposed portions of the substrate separated by the lower pattern remain on the substrate, the setting ink being removable by firing at high temperature; setting the setting ink of the lower layer pattern; printing a metalo-organic compound paste layer on said substrate on which the lower pattern has been formed to form an upper layer pattern so that all of the exposed portions of the substrate and at least a part of the lower layer pattern are covered by the upper layer pattern; and firing at high temperature to remove the lower layer pattern and a portion of the upper layer pattern covering the lower layer pattern leaving the remaining portion of the upper layer pattern as a conductive pattern on a substrate.
Claim 3
Dependent Claim
62 words
A method of claim 1, wherein in the step of printing the metalo-organic compound paste layer, the metalo-organic compound paste layer is formed such that portions of the upper layer pattern, which respectively cover adjacent exposed portions of the substrate divided by a part of the lower layer pattern, are separated from each other on said part of the lower layer pattern.
Claim 4
Dependent Claim
17 words
A method of claim 1, wherein printing is performed by intaglio offset printing method using an intaglio.
Claim 5
Dependent Claim
12 words
A method of claim 3, wherein the intaglio is a glass intaglio.
Claim 6
Dependent Claim
36 words
A method of claim 1, wherein the setting ink comprises a carbon powder, an epoxy resin, a setting agent, and an organic solvent, with an amount of nonvolatile materials ranging from 60 to 80 wt. %.
Claim 7
Dependent Claim
31 words
A method of claim 5, wherein the organic solvent of the setting ink comprises at least one of butyl carbitol acetate, σ-terpineol, n-butyl carbitol, 2,2,4-trimethyl-1, 3-hydroxypentyl-iso-butylate, 2-butoxy ethanol, and 2-ethoxy ethanol.
Claim 8
Dependent Claim
51 words
A method of claim 5, wherein a particle diameter of carbon powder is 1 μm or less, an average molecular weight of the epoxy resin is 450 to 5,000, the setting agent is dicyandiamide, and a ratio by weight of the epoxy resin to the organic solvent is 1.0 or more.
Claim 9
Dependent Claim
20 words
A method of claim 5, wherein a viscosity of the setting ink is 100 to 150 Pa.s at 25° C.
Claim 10
Dependent Claim
92 words
A method of claim 5, wherein the setting ink to be used is defined as follows: the organic solvent comprises at least one of butyl carbitol acetate, σ-terpineol, n-butyl carbitol, 2,2,4-trimethyl-1,3-hydroxypentyl-isobutylate, 2-butoxy ethanol, and 2-ethoxy ethanol; a particle diameter of the carbon powder is 1 μm or less, an average molecular weight of the epoxy resin is 450 to 5,000, a ratio by weight of the epoxy resin to the organic solvent is 1.0 or more, the setting agent is dicyandiamide, and a viscosity is 100 to 150 Pa.s at 25° C.
Claim 11
Dependent Claim
144 words
A method of claim 5, wherein the setting ink comprises a carbon powder, an epoxy resin, a setting agent, and an organic solvent, with an amount of nonvolatile materials ranging from 60 to 80 wt. %; the organic solvent comprises at least of butyl carbitol acetate, σ-terpineol, n-butyl carbitol, 2,2,4-trimethyl-1, 3-hydroxypentyl-isobutylate, 2-butoxy ethanol, and 2-ethoxy ethanol; the carbon powder is graphite powder with a particle diameter of 1 μm or less; an average molecular weight of the epoxy resin is 450 to 5,000; a ratio by weight of the epoxy resin to the organic solvent is 1.0 or more; the setting agent is dicyandiamide; a viscosity of the setting ink is 100 to 150 Pa.s at 25° C.; and the metalo- organic compound paste contains a solvent by 30 wt. % or more and its viscosity is 3 to 10 Pa.s at 25° C.
Claim 12
Dependent Claim
145 words
A method of claim 1, wherein the step of printing the setting ink comprises: filling grooves on an intaglio with the setting ink, each of said grooves having a depth of 10 μm or more; pressing a cylindrical transfer roll onto the intaglio at a predetermined pressure while moving the cylindrical transfer roll relative to the intaglio at a relative moving speed of 40 mm/sec or less to transfer the setting ink in the grooves to the cylindrical transfer roll, the cylindrical transfer roll having an outermost layer of a thickness of 2 mm or less made of a silicone rubber elastic material which has a rubber hardness of 35 degrees or more according to JIS K 6301 which corresponds to Shore hardness A; and pressing the cylindrical transfer roll onto the substrate at said predetermined pressure to transfer the setting ink to the substrate.
Claim 13
Dependent Claim
158 words
A method of claim 1, wherein the step of printing the metalo-organic compound paste comprises: filling grooves of an intaglio with the metalo-organic compound paste, each of said grooves having a depth of 10 μm or more; pressing a cylindrical transfer roll onto the intaglio at a predetermined pressure while moving the cylindrical transfer roll relative to the intaglio at a relative moving speed of 40 mm/sec or less to transfer the metalo-organic compound paste in the grooves to the cylindrical transfer roll, the cylindrical transfer roll having an outermost layer of a thickness of 2 mm or less made of a silicone rubber elastic material which has a rubber hardness of 35 degrees or more according to JIS K 6301 which corresponds to Shore hardness A; and pressing the cylindrical transfer roll onto the substrate at said predetermined pressure to transfer the metalo-organic compound paste to the substrate on which the lower layer pattern has been formed.
Claim 14
Dependent Claim
67 words
A method of claim 1, wherein the step of printing the metalo-organic compound paste includes a step of cutting the upper layer pattern on the lower layer pattern such that portions of the upper layer pattern which respectively cover adjacent exposed portions of the substrate divided by a part of the lower layer pattern are separated from each other on said part of the lower layer pattern.
Claim 15
Dependent Claim
105 words
A method of claim 13, wherein the setting ink is printed in an intaglio offset printing method using a glass intaglio with a groove depth of 10 μm or more, and a cylindrical transfer roll whose outermost layer is made of a silicone rubber elastic material having a rubber hardness of 35 degrees or more (JIS K 6301 Shore hardness A) and a thickness of 2 mm or less, in printing conditions of an identical printing pressure on the intaglio and on the substrate, and a relative moving speed of the intaglio to the cylindrical transfer roll on the intaglio of 40 mm/sec or less.
Claim 16
Dependent Claim
143 words
A method of claim 13, wherein the setting ink comprises a carbon powder, an epoxy resin, a setting agent, and an organic solvent, with an amount of nonvolatile materials ranging from 60 to 80 wt. %; the organic solvent comprises at least one of butyl carbitol acetate, σ-terpineol, n-butyl carbitol, 2,2,4-trimethyl-1,3-hydroxypentyl-iso-butylate, 2-butoxy ethanol, and 2-ethoxy ethanol; the carbon powder is graphite powder with a particle diameter of 1 μm or less; an average molecular weight of the epoxy resin is 450 to 5,000; a ratio by weight of the epoxy resin to the organic solvent is 1.0 or more; the setting agent is dicyandiamide; a viscosity of the setting ink is 100 to 150 Pa.s at 25° C.; and the metalo-organic compound paste contains a solvent by 30 wt. % or more and its viscosity is 3 to 10 Pa.s at 25° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-11-07 | 1998-05-09 | 1998-11-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-11-07 | 2002-05-09 | 2002-11-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-11-07 | 2006-05-09 | 2006-11-08 | $7700.00 | Window Closed / Lapsed |