Expandable coating composition

Claim 2

An expandable aqueous coating composition, comprising: an aqueous polymer emulsion binder, said binder comprising latex particles and said latex particles comprising a copolymer having a glass transition temperature of about -20° C. to about +60° C. and a weight average molecular weight of about 20,000 to about 500,000; and expandable particles, said expandable particles comprising a liquid blowing agent contained within a thermoplastic shell.

Claim 3

The composition of claim 1, wherein the composition comprises: from about 30 percent by weight to about 60 percent by weight water and from about 40 percent by weight to about 70 percent by weight solids, wherein the solids comprise: from about 20 parts by weight to about 95 parts by weight latex particles dispersed in the water; and from about 0.1 parts by weight to about 15 parts by weight expandable particles dispersed in the water.

Claim 4

The composition of claim 2, wherein the solids of the coating composition comprise: from about 30 parts by weight to about 90 parts by weight latex particles; from about 1 parts by weight to about 8 parts by weight expandable particles; and wherein the solids further comprise: about 2 parts by weight to about 30 parts by weight mineral pigment; and from about 0.001 parts by weight to about 2.0 parts by weight of a rheology modifier.

Claim 5

The coating of claim 1, wherein the latex particles comprise a copolymer of an ethylenically unsaturated carboxylic acid monomer and a monoethylenically unsaturated monomer.

Claim 6

The coating of claim 4, wherein the ethylenically unsaturated carboxylic acid monomer is selected from the group consisting of acrylic acid, methacrylic acid, crotonoic acid, iraconic acid, aconitic acid, atropic acid, maleic acid, fumaric acid, vinyl acetic acid, vinyl benzoic acid and mixtures thereof.

Claim 7

The coating of claim 4, wherein the monoethylenically unsaturated monomer is selected from the group consisting of ethylene, butadiene, methyl methacrylate, ethyl acrylate, butyl acrylate, butyl methacrylate, isodecyl acrylate, 2-ethyl hexyl acrylate, hydroxyethyl methacrylate, hydroxypropyl methacrylate, acrylamide, methacrylamide, acrylonitrile, vinyl acetate, vinyl propionate, vinyl versatate, vinyl toluene, styrene and mixtures thereof.

Claim 8

The coating of claim 1, wherein the copolymer includes from about 0.1 weight percent to about 10.0 weight percent monomeric units derived from the ethylenically unsaturated carboxylic acid monomer and about 90.0 weight percent to about 99.9 weight percent monomeric units derived from the ethylenically unsaturated comonomer.

Claim 9

The coating of claim 1, wherein the copolymer is self-crosslinkable and includes from about 0.25 weight percent to about 10.0 weight percent monomeric units derived from a latent crosslinker selected from the group consisting of methylol acrylamide, methylol methacrylamide, methyl acrylamidoglycolate methyl ether, acrylamidoglycolic acid and mixtures thereof.

Claim 10

The composition of claim 1, wherein the copolymer comprises a mixture of copolymers.

Claim 11

The composition of claim 1, wherein the copolymer is made by an aqueous emulsion polymerization process using from about 0.05 parts by weight to about 2.0 parts weight of an organosulfur chain transfer agent per 100 parts by weight monomeric reactants to control the molecular weight of the latex copolymer.

Claim 12

The composition of claim 1, wherein the latex particles further comprise a second copolymer and wherein the particles have an outer shell portion comprising the copolymer covering an inner core portion of the second copolymer.

Claim 13

The composition of claim 11, wherein the latex particles comprise from about 20 weight percent to about 80 weight percent core portion and about 20 weight percent to about 80 weight percent shell portion.

Claim 14

The composition of claim 11, wherein: the copolymer includes front about 0.1 weight percent to about 10 weight percent monomeric units derived from the ethylenically unsaturated carboxylic acid monomer and about 90 weight percent to about 99.9 weight percent monomeric units derived from the ethylenically unsaturated comonomer; and the second copolymer is crosslinked during synthesis and includes from about 0.1 weight percent to about 10 weight percent monomeric units derived from the ethylenically unsaturated carboxylic add monomer, about 80 weight percent to about 99.85 weight percent monomeric units derived from the ethylenically unsaturated comonomer and about 0.05 weight percent to about 10 weight percent of a crosslinking monomer having two or more ethylenically unsaturated sites per molecule.

Claim 15

The composition of claim 13, wherein the copolymer is crosslinkable and includes from about 0.25 weight percent to about 10.0 weight percent monomeric units derived from a latent crosslinker selected from the group consisting of methylol acrylamide, methylol methacrylamide, methyl acrylamidoglycolate methyl ether, acrylamidoglycolic acid and mixtures thereof.

Claim 16

The composition of claim 11, wherein the second copolymer has a glass transition temperature that is from about -20° C. to about +105° C. and is different from the glass transition temperature of the copolymer.

Claim 17

The composition of claim 11, wherein the second copolymer has a weight average molecular weight greater than about 500,000.