Method for removing sulfur from superalloy articles to improve their oxidation resistance
Assignee: RTX Corp
•
Filing: 1993-04-14
•
Granted: 1994-09-13
•
Expires: 2013-04-14
Abstract
Abstract Superalloy articles are made more oxidation resistant by a process which includes heat treating the article in the presence of foreign chemical species, at a temperature at which the foreign chemical species reacts with and modifies any oxide film present on the article surface. The heat treatment is best carried out at a temperature above the gamma prime solvus temperature of the article and below the incipient melting temperature of the article. Alternatively, the heat treatment may be carried out within the range defined by the incipient melting temperature of the article and about 150° C. below the incipient melting temperature of the article. At such temperatures the foreign chemical species reacts with and modifies the oxide film on the article surface. Sulfur is then able to diffuse through such modified film, and a more oxidation resistant component is produced.
Inventors
- 👤 William P. Allen
- 👤 Norman S. Bornstein
- 👤 Stephen Chin
- 👤 Michael DeCrescente
- 👤 David N. Duhl
- 👤 Donald R. Parille
- 👤 Roscoe A. Pike
- 👤 John G. Smeggil
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 03:22
CPC Classifications
C; C22; C22F; C22F1/00; C22F1/10; C21; C21D; C21D3/00; C21D3/02; C22B; C22B9/00; C22B9/14; C22F1/02
Claims Analysis
Total Claims: 47
Claim 1
Independent Claim
59 words
A method for removing sulfur from a solid nickel-base superalloy article, said article having a normally occurring alumina surface film, comprising the step of heating the article in the presence of a source of magnesium at a temperature at which magnesium in the source reacts with the alumina film thereby enabling said sulfur to diffuse out of the article.
Claim 2
Independent Claim
59 words
A method for removing sulfur from a solid nickel-base superalloy article, said article having a normally occurring alumina surface film, comprising the step of heating the article in the presence of a source of magnesium at a temperature at which magnesium in the source reacts with the alumina film thereby enabling said sulfur to diffuse out of the article.
Claim 3
Dependent Claim
18 words
The method of claim 1, wherein the article is embedded in the magnesium source during the heating step.
Claim 4
Dependent Claim
20 words
The method of claim 1, wherein the article is in out-of-contact relation with the magnesium source during the heating step.
Claim 5
Dependent Claim
23 words
The method of claim 1, wherein a coating comprising the magnesium source is applied to the article surface prior to the heating step.
Claim 6
Dependent Claim
11 words
The method of claim 4, wherein the coating is a slurry.
Claim 7
Dependent Claim
12 words
The method of claim 1, wherein the magnesium source is pure magnesium.
Claim 8
Dependent Claim
15 words
The method of claim 1, wherein the magnesium source is a compound which contains magnesium.
Claim 9
Dependent Claim
38 words
The method of claim 1, wherein the article is heated to a temperature within the range defined by the incipient melting temperature of the article and about 100° C. below the gamma prime solvus temperature of the article.
Claim 10
Dependent Claim
36 words
The method of claim 1, wherein the article is heated to temperature within the range defined by the incipient melting temperature of the article and about 150° C. below the incipient melting temperature of the article.
Claim 11
Dependent Claim
15 words
The method of claim 1, wherein the heating step is carried out in a vacuum.
Claim 12
Dependent Claim
16 words
The method of claim 1, wherein the heating step is carried out in a hydrogen atmosphere.
Claim 13
Dependent Claim
17 words
The method of claim 1, wherein the heating step is carried out in an inert gas atmosphere.
Claim 14
Independent Claim
92 words
A method for removing sulfur from a solid nickel base superalloy article, comprising the steps of embedding the article in powder particles which comprises source of magnesium, and then heating embedded the article in vacuum or in a hydrogen or inert gas atmosphere to a temperature within the range defined by the melting temperature of the article and about 100° C. below the gamma prime solvus temperature of the article for a period of time sufficient to reduce the sulfur in the article to below about 5 parts per million, by weight.
Claim 15
Independent Claim
92 words
A method for removing sulfur from a solid nickel base superalloy article, comprising the steps of embedding the article in powder particles which comprises source of magnesium, and then heating embedded the article in vacuum or in a hydrogen or inert gas atmosphere to a temperature within the range defined by the melting temperature of the article and about 100° C. below the gamma prime solvus temperature of the article for a period of time sufficient to reduce the sulfur in the article to below about 5 parts per million, by weight.
Claim 16
Independent Claim
94 words
A method for removing sulfur from a nickel base superalloy article, comprising the steps of arranging the article in out-of-contact relation with a source of magnesium, and then heating the article, and the magnesium source, in vacuum or in a hydrogen or inert gas atmosphere to a temperature within the range defined by the incipient melting temperature of the article and about 100° C. below the gamma prime solvus temperature of the article for a period of time sufficient to reduce the sulfur in the article to below 5 parts per million, by weight.
Claim 17
Independent Claim
94 words
A method for removing sulfur from a nickel base superalloy article, comprising the steps of arranging the article in out-of-contact relation with a source of magnesium, and then heating the article, and the magnesium source, in vacuum or in a hydrogen or inert gas atmosphere to a temperature within the range defined by the incipient melting temperature of the article and about 100° C. below the gamma prime solvus temperature of the article for a period of time sufficient to reduce the sulfur in the article to below 5 parts per million, by weight.
Claim 18
Independent Claim
94 words
A method for removing sulfur from a nickel base superalloy article, comprising the steps of applying a coating which includes a source of magnesium to the article surface, and then heating the coated article in a vacuum or in a hydrogen or inert gas atmosphere to a temperature within the range defined by the incipient melting temperature of the article and about 100° C. below the gamma prime solvus temperature of the article for a period of time sufficient to reduce the sulfur in the article to below 5 parts per million, by weight.
Claim 19
Independent Claim
94 words
A method for removing sulfur from a nickel base superalloy article, comprising the steps of applying a coating which includes a source of magnesium to the article surface, and then heating the coated article in a vacuum or in a hydrogen or inert gas atmosphere to a temperature within the range defined by the incipient melting temperature of the article and about 100° C. below the gamma prime solvus temperature of the article for a period of time sufficient to reduce the sulfur in the article to below 5 parts per million, by weight.
Claim 20
Independent Claim
99 words
A method for removing sulfur from a nickel base superalloy article, comprising the step of heating the article in the presence of a foreign chemical species, said foreign chemical species being effective in modifying any oxide present on the article surface at elevated temperatures to allow sulfur to diffuse out of the article, and then heating the article to a temperature at which the sulfur present in the article becomes mobile and said foreign chemical species reacts with the oxide present on the article surface to modify said oxide to allow said sulfur to diffuse out of the article.
Claim 21
Independent Claim
99 words
A method for removing sulfur from a nickel base superalloy article, comprising the step of heating the article in the presence of a foreign chemical species, said foreign chemical species being effective in modifying any oxide present on the article surface at elevated temperatures to allow sulfur to diffuse out of the article, and then heating the article to a temperature at which the sulfur present in the article becomes mobile and said foreign chemical species reacts with the oxide present on the article surface to modify said oxide to allow said sulfur to diffuse out of the article.
Claim 22
Dependent Claim
29 words
The method of claim 16, wherein said foreign chemical species includes metallic cations and segregates to the surface oxide's grain boundaries thereby promoting increased sulfur diffusion, at elevated temperatures.
Claim 23
Dependent Claim
33 words
The method of claim 17, wherein said elevated temperatures are within the range defined by the incipient melting temperature of the article and approximately 150° C. below the melting temperature of the article.
Claim 24
Dependent Claim
34 words
The method of claim 17, wherein said elevated temperatures are within the range defined by the melting temperature of the article and about 100° C. below the gamma prime solvus temperature of the article.
Claim 25
Dependent Claim
27 words
The method of claim 17, wherein said foreign chemical species exhibits a vapor pressure between about 10 -8 to about 10 -3 bar within said temperature range.
Claim 26
Dependent Claim
31 words
The method of claim 16, wherein said foreign chemical species reacts with any surface oxide present to form a surface oxide containing compound thereby promoting increased sulfur diffusion at elevated temperatures.
Claim 27
Dependent Claim
33 words
The method of claim 21, wherein said elevated temperatures are within the range defined by the incipient melting temperature of the article and approximately 150° C. below the melting temperature of the article.
Claim 28
Dependent Claim
35 words
The method of claim 21, wherein said elevated temperatures are within the range defined by the incipient melting temperature of the article and about 100° C. below the gamma prime solvus temperature of the article.
Claim 29
Dependent Claim
27 words
The method of claim 21, wherein said foreign chemical species exhibits a vapor pressure between about 10 -8 to about 10 -3 bar within said temperature range.
Claim 30
Dependent Claim
23 words
The method of claim 16, wherein any surface oxide present on said article is soluble in said foreign chemical species at elevated temperatures.
Claim 31
Dependent Claim
34 words
The method of claim 25, wherein said elevated temperatures are within the range defined by the incipient melting temperature of the article and approximately 150° C. below the incipient melting temperature of the article.
Claim 32
Dependent Claim
35 words
The method of claim 25, wherein said elevated temperatures are within the range defined by the incipient melting temperature of the article and about 100° C. below the gamma prime solvus temperature of the article.
Claim 33
Dependent Claim
34 words
The method of claim 25, wherein said foreign chemical species exhibits a vapor pressure between about 10 -8 to about 10 -3 bar within said temperature range in order to promote vapor phase transport.
Claim 34
Dependent Claim
19 words
The method of claim 16, wherein the article is embedded in said foreign chemical species during the heating step.
Claim 35
Dependent Claim
21 words
The method of claim 16, wherein the article is in out-of-contact relation with said foreign chemical species during the heating step.
Claim 36
Dependent Claim
20 words
The method of claim 16, wherein the article is coated with said foreign chemical species prior to the heating step.
Claim 37
Dependent Claim
11 words
The method of claim 31, wherein said coating is a slurry.
Claim 38
Dependent Claim
15 words
The method of claim 16, wherein the heating step is carried out in a vacuum.
Claim 39
Dependent Claim
17 words
The method of claim 16, wherein the heating step is carried out in a hydrogen reducing atmosphere.
Claim 40
Dependent Claim
17 words
The method of claim 16, wherein the heating step is carried out in an inert gas atmosphere.
Claim 41
Dependent Claim
99 words
The method of claim 16, wherein said foreign chemical species is a material selected from the group consisting of AlN, Al 4C 3 , Li 2 O, Na 2 O, BaO, CaO, MgO, FeO, NiO, CoO, Y 2 O 3 , Gd 2 O 3 , SiO 2 , ZrO 2 , Cr 2 O 3 , Fe 2 O 3 , Ga 2 O 3 , Ni 2 Mg, NiMg 2 , Co 2 Mg, MgCl 2 , MgF 2 , MgAl 2 O 4 , MgZrAl 2 O 6 , Ta 2 O 5 , and Fe.
Claim 42
Independent Claim
156 words
A method for improving the oxidation resistance of a nickel base superalloy article, comprising the steps of embedding the article in a powdered foreign chemical species, said foreign chemical species being effective in modifying any oxide present on the article surface at elevated temperatures, and wherein said foreign chemical species exhibits a vapor pressure between about 10 -8 to about 10 -3 bar at a temperature within the range defined by the incipient melting temperature of the article and approximately 150° C. below the incipient melting temperature of the article, and then heating the embedded article in vacuum or in a hydrogen reducing or inert gas atmosphere to a temperature within said range for a period of time sufficient to allow the foreign chemical species to react with any oxide present on the article surface to modify said oxide to allow said sulfur to diffuse out of the article to reduce the sulfur in the article.
Claim 43
Independent Claim
156 words
A method for improving the oxidation resistance of a nickel base superalloy article, comprising the steps of embedding the article in a powdered foreign chemical species, said foreign chemical species being effective in modifying any oxide present on the article surface at elevated temperatures, and wherein said foreign chemical species exhibits a vapor pressure between about 10 -8 to about 10 -3 bar at a temperature within the range defined by the incipient melting temperature of the article and approximately 150° C. below the incipient melting temperature of the article, and then heating the embedded article in vacuum or in a hydrogen reducing or inert gas atmosphere to a temperature within said range for a period of time sufficient to allow the foreign chemical species to react with any oxide present on the article surface to modify said oxide to allow said sulfur to diffuse out of the article to reduce the sulfur in the article.
Claim 44
Independent Claim
160 words
A method for improving the oxidation resistance of a nickel base superalloy article, comprising the steps of arranging the article in out-of-contact relation with a foreign chemical species, said foreign chemical species being effective in modifying any oxide present on the article surface at elevated temperatures, and wherein said foreign chemical species exhibits a vapor pressure between about 10 -8 to about 10 -3 bar at a temperature within the range defined by the incipient melting temperature of the article and approximately 150° C. below the melting temperature of the article, and the magnesium source, and then heating the article in vacuum or in a hydrogen or inert gas containing atmosphere to a temperature within said range for a period of time sufficient to allow the foreign chemical species to react with any oxide present on the article surface to modify said oxide to allow said sulfur to diffuse out of the article to reduce the sulfur in the article.
Claim 45
Independent Claim
160 words
A method for improving the oxidation resistance of a nickel base superalloy article, comprising the steps of arranging the article in out-of-contact relation with a foreign chemical species, said foreign chemical species being effective in modifying any oxide present on the article surface at elevated temperatures, and wherein said foreign chemical species exhibits a vapor pressure between about 10 -8 to about 10 -3 bar at a temperature within the range defined by the incipient melting temperature of the article and approximately 150° C. below the melting temperature of the article, and the magnesium source, and then heating the article in vacuum or in a hydrogen or inert gas containing atmosphere to a temperature within said range for a period of time sufficient to allow the foreign chemical species to react with any oxide present on the article surface to modify said oxide to allow said sulfur to diffuse out of the article to reduce the sulfur in the article.
Claim 46
Independent Claim
160 words
A method for improving the oxidation resistance of a nickel base superalloy article, comprising the steps of applying a coating which includes a foreign chemical species to the article surface, said foreign chemical species being effective in modifying any oxide present on the article surface at elevated temperatures, and wherein said foreign chemical species exhibits a vapor pressure between about 10 -8 to about 10 -3 bar at a temperature within the range defined by the incipent melting temperature of the article and approximately 150° C. below the incipient melting temperature of the article, and then heating the coated article in vacuum or in a hydrogen reducing or inert gas atmosphere to a temperature within said range for a period of time sufficient to allow the foreign chemical species to react with any oxide present on the article surface to modify said oxide to allow said sulfur to diffuse out of the article to reduce the sulfur in the article.
Claim 47
Independent Claim
160 words
A method for improving the oxidation resistance of a nickel base superalloy article, comprising the steps of applying a coating which includes a foreign chemical species to the article surface, said foreign chemical species being effective in modifying any oxide present on the article surface at elevated temperatures, and wherein said foreign chemical species exhibits a vapor pressure between about 10 -8 to about 10 -3 bar at a temperature within the range defined by the incipent melting temperature of the article and approximately 150° C. below the incipient melting temperature of the article, and then heating the coated article in vacuum or in a hydrogen reducing or inert gas atmosphere to a temperature within said range for a period of time sufficient to allow the foreign chemical species to react with any oxide present on the article surface to modify said oxide to allow said sulfur to diffuse out of the article to reduce the sulfur in the article.
References Cited (Backward Citations)
US1710846A
Cited
US2823139A
Cited
US3403058A
Cited
US3853540A
Cited
US3891425A
Cited
US4209348A
Cited
US4719080A
Cited
US4895201A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-09-12 | 1998-03-14 | 1998-09-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-09-12 | 2002-03-14 | 2002-09-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-09-12 | 2006-03-14 | 2006-09-13 | $7700.00 | Window Closed / Lapsed |