Process for making ceramic dental crowns
Assignee: Individual
•
Filing: 1993-06-15
•
Granted: 1994-09-13
•
Expires: 2013-06-15
Abstract
Abstract A process for making artificial porcelain teeth or laboratory fabricated dental crowns includes casting or molding a plurality of tooth-shaped unfired shells from ceramic powder and a resin, acrylic, wax or starch in liquid form and molded and hardened into shapes of predetermined tooth contours. These dried powder like, thin and highly characterized outside shells of a general tooth shape are then merged into a full porcelain powder buildup of the tooth shape by using conventional porcelain powders mixed into a paste, conventionally, as a filling medium completing the buildup of tooth or crown form. This form is then placed into a furnace and heated to purge undesired resin, acrylic, wax or starch and other extraneous material, and then it is baked conventionally to further purge same and obtain an artificial tooth or crown in the most desirable form possible for the technician who then finalizes the contour by grinding and polishing or glazing same conventionally. The powder like dried shell may be used with a substructure or glass core or refractory die. The process preferably includes the provision of determining the proper color of porcelain powders to use to arrive at the final color of the tooth or crown even before firing and baking the shell and filling medium.
Inventors
- 👤 Kenneth S. Braiman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 21:10
CPC Classifications
A; A61; A61C; A61C13/00; A61C13/0003; A61C5/00; A61C5/20; A61C5/70; A61C5/77
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
227 words
A process for making a ceramic dental crown comprising the steps of: A. molding approximate tooth-shaped unfired thin powder shells representative of various teeth from a hardenable liquid mixture of ceramic powder and a predetermined small amount of at least one member of the group consisting of i) acrylic powders dissolved in a polyacrylic monomer, ii) liquid resin iii) heated waxes iv) watered starches into shapes of a generally sturdy matrix having approximate predetermined tooth shapes and having highly detailed anatomical contours of various teeth; B. selecting one of the unfired powder shells of approximate predetermined tooth contours having the greatest similarities to the crown desired for a particular patient; C. applying a paste buildup of conventional porcelain powders to the selected one of the unfired powder shells to fill same into a more detailed fit molding to a conventional substructure; D. purging the selected paste buildup and one powder shell by heating same which purges extraneous material therefrom; E. baking the purged selected one buildup and shell under vacuum in a conventional manner to eliminate one member of the group in step A and obtain a solid homogenous ceramic crown; F. grinding the baked crown to its final shape in a conventional manner; and G. finishing the ground baked crown to its final shape and appearance in a conventional manner to produce the final ceramic crown.
Claim 2
Dependent Claim
227 words
A process for making a ceramic dental crown comprising the steps of: A. molding approximate tooth-shaped unfired thin powder shells representative of various teeth from a hardenable liquid mixture of ceramic powder and a predetermined small amount of at least one member of the group consisting of i) acrylic powders dissolved in a polyacrylic monomer, ii) liquid resin iii) heated waxes iv) watered starches into shapes of a generally sturdy matrix having approximate predetermined tooth shapes and having highly detailed anatomical contours of various teeth; B. selecting one of the unfired powder shells of approximate predetermined tooth contours having the greatest similarities to the crown desired for a particular patient; C. applying a paste buildup of conventional porcelain powders to the selected one of the unfired powder shells to fill same into a more detailed fit molding to a conventional substructure; D. purging the selected paste buildup and one powder shell by heating same which purges extraneous material therefrom; E. baking the purged selected one buildup and shell under vacuum in a conventional manner to eliminate one member of the group in step A and obtain a solid homogenous ceramic crown; F. grinding the baked crown to its final shape in a conventional manner; and G. finishing the ground baked crown to its final shape and appearance in a conventional manner to produce the final ceramic crown.
Claim 3
Dependent Claim
23 words
The process of claim 1 wherein step D is performed at about 600 degrees-1200 degrees F. for a time period of 2-15 minutes.
Claim 4
Dependent Claim
98 words
The process of claim 1 further comprising the steps of: H) selecting a fired form of a tooth-shaped thin shell substantially identical to the unfired selected one of the shells in step B; I) placing the selected fired form onto a number of different colored fired base forms which are complemental with and fit onto the selected fired form with the use of a clear filler therebetween; J) determining the proper color from one of the colored fired base forms of the paste to be applied in step C under the tooth-shaped thin shell selected in step A.
Claim 5
Dependent Claim
14 words
The process of claim 3 wherein glycerin is the clear filler in step I.
Claim 6
Dependent Claim
47 words
The process of claim 1 wherein step C includes the step of adding a plurality of predetermined sized ceramic beads which are covered by the paste build up to assure sufficient amount of properly colored paste build up being applied beneath the selected one of the shells.
Claim 7
Dependent Claim
186 words
A process for making a ceramic dental crown from a plurality of molded approximate tooth-shaped thin unfired but rigid ceramic powder shells having detailed anatomical contours representative of various teeth comprising the steps of: A. selecting from the plurality of molded thin shells containing ceramic powders one having the size and shape and desired enamel color according to the crown desired of a particular patient according to an impression made by the dentist; B. applying a paste buildup of conventional porcelain powders under the selected one of the thin powder shells to fill same into a more detailed fit matching the prep form from the impression made by the dentist; C. firing the selected paste buildup and one powder shell with filler dentine therein to remove extraneous material therefrom; D. baking the fired one shell under vacuum in a conventional manner to obtain a baked ceramic crown; E. grinding the baked crown to its final shape in a conventional manner; and F. polishing or glazing the final shaped tooth or crown in a conventional manner to obtain the ceramic crown to be sent to the dentist.
Claim 8
Dependent Claim
186 words
A process for making a ceramic dental crown from a plurality of molded approximate tooth-shaped thin unfired but rigid ceramic powder shells having detailed anatomical contours representative of various teeth comprising the steps of: A. selecting from the plurality of molded thin shells containing ceramic powders one having the size and shape and desired enamel color according to the crown desired of a particular patient according to an impression made by the dentist; B. applying a paste buildup of conventional porcelain powders under the selected one of the thin powder shells to fill same into a more detailed fit matching the prep form from the impression made by the dentist; C. firing the selected paste buildup and one powder shell with filler dentine therein to remove extraneous material therefrom; D. baking the fired one shell under vacuum in a conventional manner to obtain a baked ceramic crown; E. grinding the baked crown to its final shape in a conventional manner; and F. polishing or glazing the final shaped tooth or crown in a conventional manner to obtain the ceramic crown to be sent to the dentist.
Claim 9
Dependent Claim
60 words
The process of claim 6 wherein the plurality of molded thin powder shells containing ceramic powders are castings prepared from a hardenable liquid mixture of the ceramic powders and a predetermined small amount of at least one member from the group consisting of: i) acrylic powders dissolved in a polyacrylic monomer, ii) liquid resin iii) heated waxes iv) watered starches.
Claim 10
Dependent Claim
23 words
The process of claim 6 wherein step C is performed at about 600 degrees-1200 degrees F. for a time period of 2-15 minutes.
Claim 11
Dependent Claim
97 words
The process of claim 6 further comprising the steps of: G) selecting a fired form of a tooth-shaped thin shell substantially identical to the selected one of the unfired shells in step A; H) placing the selected fired form onto a number of different colored fired base forms which are complemental with and fits onto the selected fired form with the use of a clear filler therebetween; I) determining the proper color from one of the colored base forms of the paste to be applied in step B to the selected one thin shell from step A.
Claim 12
Dependent Claim
40 words
The process of claim 9 wherein step H includes applying glycerin as the clear filler between the selected fired form and the colored fixed base form to blend into one perceived color that can be predictably duplicated if fired together.
Claim 13
Dependent Claim
133 words
The process of making ceramic dental crowns comprising the steps of: A. fabricating various crown shapes and sizes; B. preparing a liquid hardenable mixture of ceramic powders and a predetermined small amount of at least one member from the group consisting of: i) acrylic powders dissolved in a polyacrylic monomer, ii) liquid resin iii) heated waxes iv) watered starches; C. pouring the mixture into the molds to obtain various crown thin powder shells having detailed anatomical contours; D. using a selected one of the various crown thin powder shells as a form under which to fill with a paste buildup of conventional porcelain powders, fire and finish in a conventional manner to provide a ceramic crown to the dentist corresponding to an impression made by the dentist of a particular patient's needed crown.
Claim 14
Dependent Claim
133 words
The process of making ceramic dental crowns comprising the steps of: A. fabricating various crown shapes and sizes; B. preparing a liquid hardenable mixture of ceramic powders and a predetermined small amount of at least one member from the group consisting of: i) acrylic powders dissolved in a polyacrylic monomer, ii) liquid resin iii) heated waxes iv) watered starches; C. pouring the mixture into the molds to obtain various crown thin powder shells having detailed anatomical contours; D. using a selected one of the various crown thin powder shells as a form under which to fill with a paste buildup of conventional porcelain powders, fire and finish in a conventional manner to provide a ceramic crown to the dentist corresponding to an impression made by the dentist of a particular patient's needed crown.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-09-12 | 1998-03-14 | 1998-09-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-09-12 | 2002-03-14 | 2002-09-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-09-12 | 2006-03-14 | 2006-09-13 | $7700.00 | Window Closed / Lapsed |