Integration of high performance submicron CMOS and dual-poly non-volatile memory devices using a third polysilicon layer
Assignee: Atmel Corp
•
Filing: 1993-02-19
•
Granted: 1994-08-23
•
Expires: 2013-02-19
Abstract
Abstract An apparatus and method for integrating a submicron CMOS device and a non-volatile memory, wherein a thermal oxide layer is formed over a semiconductor substrate and a two layered polysilicon non-volatile memory device formed thereon. A portion of the thermal oxide is removed by etching, a thin gate oxide and a third layer of polysilicon having a submicron depth is deposited onto the etched region. The layer of polysilicon is used as the gate for the submicron CMOS device. In so doing a submicron CMOS device may be formed without subjecting the device to the significant re-oxidation required in formation processes for dual poly non-volatile memory devices such as EPROMs and EEPROMs, and separate device optimization is achieved.
Inventors
- 👤 Bradley J. Larsen
- 👤 Todd A. Randazzo
- 👤 Donald A. Erickson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 18:33
CPC Classifications
H; H10; H10B; H10B41/00; H10B41/30; H10B41/40; H10B41/42; H10D; H10D84/00; H10D84/90; H10D84/903; H10D84/907
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
290 words
A method for forming a submicron transistor adjacent to a non-volatile memory transistor comprising the steps of: providing a semiconductor substrate of a first conductivity type, forming a non-volatile memory transistor on a first region of said semiconductor substrate, including forming a first gate oxide layer on said substrate, forming a first polysilicon layer on said first gate oxide layer, forming a second gate oxide layer on said polysilicon layer, selectively etching said gate oxide and polysilicon layers to leave a pair of polysilicon gates stacked above a section of said first region, said gates separated from each other by said second gate oxide layer and separated from said substrate by said first gate oxide layer, forming doped regions of a second conductivity type in said first region proximate to said pair of gates, forming a thermal oxide layer over said non-volatile memory device and said semiconductor substrate, removing said thermal oxide from a second region of said substrate, said second region separated from said first region by a field oxide region, forming a third gate oxide layer over said second region of said substrate, forming a third layer of polysilicon over said non-volatile memory device and said third gate oxide layer, selectively removing said third layer of polysilicon such that said third layer of polysilicon is removed from everywhere except for atop a portion said second region, forming a submicron CMOS transistor, including implanting dopants of said second conductivity type into said second region of said substrate adjacent to said portion under said third layer of polysilicon, forming metallized contacts to said submicron CMOS transistor and said non-volatile memory transistor, and covering said semiconductor substrate including said submicron CMOS transistor and said non-volatile memory transistor with a protective coating.
Claim 2
Independent Claim
290 words
A method for forming a submicron transistor adjacent to a non-volatile memory transistor comprising the steps of: providing a semiconductor substrate of a first conductivity type, forming a non-volatile memory transistor on a first region of said semiconductor substrate, including forming a first gate oxide layer on said substrate, forming a first polysilicon layer on said first gate oxide layer, forming a second gate oxide layer on said polysilicon layer, selectively etching said gate oxide and polysilicon layers to leave a pair of polysilicon gates stacked above a section of said first region, said gates separated from each other by said second gate oxide layer and separated from said substrate by said first gate oxide layer, forming doped regions of a second conductivity type in said first region proximate to said pair of gates, forming a thermal oxide layer over said non-volatile memory device and said semiconductor substrate, removing said thermal oxide from a second region of said substrate, said second region separated from said first region by a field oxide region, forming a third gate oxide layer over said second region of said substrate, forming a third layer of polysilicon over said non-volatile memory device and said third gate oxide layer, selectively removing said third layer of polysilicon such that said third layer of polysilicon is removed from everywhere except for atop a portion said second region, forming a submicron CMOS transistor, including implanting dopants of said second conductivity type into said second region of said substrate adjacent to said portion under said third layer of polysilicon, forming metallized contacts to said submicron CMOS transistor and said non-volatile memory transistor, and covering said semiconductor substrate including said submicron CMOS transistor and said non-volatile memory transistor with a protective coating.
Claim 3
Dependent Claim
43 words
The method as recited in claim 1 further comprising oxidizing said pair of gates, prior to forming said thermal oxide layer over said non-volatile memory device, whereby charge retention characteristics of said gates are enhanced without impairing performance of said submicron CMOS transistor.
Claim 4
Dependent Claim
22 words
The method as recited in claim 1 wherein forming said non-volatile memory trnasistor further comprises the steps of forming an EPROM transistor.
Claim 5
Dependent Claim
22 words
The method as recited in claim 1 wherein forming said non-volatile memory transistor further comprises the steps of forming an EEPROM transistor.
Claim 6
Dependent Claim
23 words
The method as recited in claim 1 wherein forming said submicron CMOS transistor comprises the steps of forming a submicron CMOS N-channel transistor.
Claim 7
Dependent Claim
23 words
The method as recited in claim 1 wherein forming said submicron CMOS transistor comprises the steps of forming a submicron CMOS P-channel transistor.
Claim 8
Dependent Claim
28 words
The method as recited in claim 1 wherein said metallized contacts formed to said submicron CMOS transistor are formed contacting said source drain and gate of said transistor.
Claim 9
Dependent Claim
25 words
The method as recited in claim 1 wherein said thermal oxide is formed to a depth of approximately 300 angstroms over said non-volatile memory transistor.
Claim 10
Dependent Claim
22 words
The method as recited in claim 1 wherein said thermal oxide is removed from said first region using a wet HF etch.
Claim 11
Dependent Claim
28 words
The method as recited in claim 1 wherein said gate oxide layer is formed to a depth that is less than that of said first gate oxide layer.
Claim 12
Dependent Claim
24 words
The method as recited in claim 1 wherein said third gate oxide layer is formed to a depth of between 100 and 150 angstroms.
Claim 13
Dependent Claim
17 words
The method as recited in claim 1 further including forming a plurality of said non-volatile memory transistors.
Claim 14
Dependent Claim
17 words
The method as recited in claim 1 further including forming a plurality of said submicron CMOS transistors.
Claim 15
Independent Claim
161 words
A method of forming a CMOS memory cell comprising: forming a floating gate CMOS memory transistor, including forming a first gate oxide layer on said substrate, forming a first polysilicon layer on said first gate oxide layer, forming a second gate oxide layer on said first polysilicon layer, etching said polysilicon layers and said gate oxide layers to leave a stack of said layers atop said substrate between a source region and a drain region, subsequently forming a high performance CMOS transistor adjacent to said memory transistor, including forming a third gate oxide layer on said substrate spaced apart from said memory transistor by a field oxide region, forming a third polysilicon layer on said third gate oxide layer, etching said third polysilicon layer to leave a submicron gate separated from said memory transistor by a field oxide region, and doping said substrate proximate to said submicron gate, such that said high performance transistor can electrically communicate with said memory transistor.
Claim 16
Independent Claim
161 words
A method of forming a CMOS memory cell comprising: forming a floating gate CMOS memory transistor, including forming a first gate oxide layer on said substrate, forming a first polysilicon layer on said first gate oxide layer, forming a second gate oxide layer on said first polysilicon layer, etching said polysilicon layers and said gate oxide layers to leave a stack of said layers atop said substrate between a source region and a drain region, subsequently forming a high performance CMOS transistor adjacent to said memory transistor, including forming a third gate oxide layer on said substrate spaced apart from said memory transistor by a field oxide region, forming a third polysilicon layer on said third gate oxide layer, etching said third polysilicon layer to leave a submicron gate separated from said memory transistor by a field oxide region, and doping said substrate proximate to said submicron gate, such that said high performance transistor can electrically communicate with said memory transistor.
Claim 17
Dependent Claim
199 words
In a method of forming a CMOS memory cell with a three-layer polysilicon process, the improvement comprising: forming a floating gate CMOS memory transistor in a first time interval, including forming a first gate oxide layer on a substrate, forming a first polysilicon layer on said first gate oxide layer, forming a second gate oxide layer on said first polysilicon layer, forming a second polysilicon layer on said second gate oxide layer, etching said polysilicon and gate oxide layers to leave a sense gate disposed above a floating gate disposed above a channel between a source region and a drain region of said substrate, and forming a high performance CMOS transistor in a second time interval, after the first time interval, including forming a third gate oxide layer on a section of said substrate adjacent to said memory transistor, said section separated from said memory cell by a field oxide region, forming a third polysilicon layer on said third gate oxide layer, etching said third polysilicon layer to leave a gate atop said section, and doping said section around said gate to form electrically conductive regions, such that said high performance transistor can electrically communicate with said memory transistor.
Claim 18
Dependent Claim
199 words
In a method of forming a CMOS memory cell with a three-layer polysilicon process, the improvement comprising: forming a floating gate CMOS memory transistor in a first time interval, including forming a first gate oxide layer on a substrate, forming a first polysilicon layer on said first gate oxide layer, forming a second gate oxide layer on said first polysilicon layer, forming a second polysilicon layer on said second gate oxide layer, etching said polysilicon and gate oxide layers to leave a sense gate disposed above a floating gate disposed above a channel between a source region and a drain region of said substrate, and forming a high performance CMOS transistor in a second time interval, after the first time interval, including forming a third gate oxide layer on a section of said substrate adjacent to said memory transistor, said section separated from said memory cell by a field oxide region, forming a third polysilicon layer on said third gate oxide layer, etching said third polysilicon layer to leave a gate atop said section, and doping said section around said gate to form electrically conductive regions, such that said high performance transistor can electrically communicate with said memory transistor.
References Cited (Backward Citations)
US5194924A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-08-22 | 1998-02-21 | 1998-08-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-08-22 | 2002-02-21 | 2002-08-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-08-22 | 2006-02-21 | 2006-08-23 | $7700.00 | Window Closed / Lapsed |