Treatment of metallic surfaces using radiofrequency plasma deposition and chemical attachment of bioactive agents
Assignee: Cordis Corp
•
Filing: 1992-12-11
•
Granted: 1994-08-09
•
Expires: 2012-12-11
Abstract
Abstract A treatment for metallic surfaces and devices having metallic surfaces is described. A film of heptafluorobutylmethacrylate (HFBMA) is applied to a surface by radiofrequency (RF) plasma deposition and subsequently treated with a biologically active agent. A water vapor RF plasma treatment of the HFBMA coating provides reactive groups thereon which can covalently bond to the biologically active agent. Alternatively, a spacer group can be bonded to the activated HFBMA and the biologically active agent can then be bonded to the spacer group. Devices coated according to the invention possess enhanced biocompatibility and the HFBMA coatings are durable even under severe crimping and expansion conditions.
Inventors
- 👤 Pallassana V. Narayanan
- 👤 Stephen M. Rowland
- 👤 Kimberly D. Stanley
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 20:58
CPC Classifications
A; A61; A61L; A61L33/00; A61L33/0005; A61L33/0011; A61L33/0041; A61L33/0029; A61L33/0094; Y; Y10; Y10S; Y10S530/00; Y10S530/81; Y10S530/812; Y10S530/815; Y10S530/816; Y10S623/00; Y10S623/92; Y10S623/921
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
90 words
A method for rendering biocompatible a metal surface of a medical device, comprising the steps of: coating said metal surface with a layer of heptafluorobutylmethacrylate monomer to form a polymer coating on said surface; treating said polymer coating with water vapor plasma to provide reactive groups thereon; and applying a biologically active agent to said polymer coating; the thus formed device being a biocompatible metallic member which, when implanted within a blood vessel, prevents substantial thrombus from occurring on its surface while not significantly interfering with endothelialization of said surface.
Claim 2
Independent Claim
90 words
A method for rendering biocompatible a metal surface of a medical device, comprising the steps of: coating said metal surface with a layer of heptafluorobutylmethacrylate monomer to form a polymer coating on said surface; treating said polymer coating with water vapor plasma to provide reactive groups thereon; and applying a biologically active agent to said polymer coating; the thus formed device being a biocompatible metallic member which, when implanted within a blood vessel, prevents substantial thrombus from occurring on its surface while not significantly interfering with endothelialization of said surface.
Claim 3
Dependent Claim
65 words
The method of claim 1 wherein the step of treating said polymer coating further includes applying a spacer molecule thereto, said spacer molecule forming a covalent linkage with said polymer coating; and said applying of said biologically active agent is performed after said spacer molecule is applied to said polymer coating, said biologically active agent and said spacer molecule also forming a covalent linkage therebetween.
Claim 4
Dependent Claim
51 words
The method of claim 1 wherein the step of coating said metal surface with a layer of heptafluorobutyl-methacrylate is accomplished using a radio frequency plasma deposition thereof; and the step of treating said polymer coating by water vapor is also accomplished by a radio frequency plasma treatment of said polymer coating.
Claim 5
Dependent Claim
48 words
The method of claim 1 wherein the step of applying a biologically active agent includes exposing the polymer coating to an aqueous heparin solution having a heparin concentration of between about 4.0 mg/ml and about 8.0 mg/ml for a period of between about 30 and about 90 minutes.
Claim 6
Dependent Claim
44 words
The method of claim 4 wherein the step of exposing the polymer coating to an aqueous heparin solution is accomplished in the presence of a carbodiimide compound in solution with said heparin and at a concentration approximately equal to the concentration of said heparin.
Claim 7
Dependent Claim
11 words
The method of claim 5 wherein said carbodiimide is N-(3-dimethylaminopropyl)-N'-ethylcarbodiimide hydrochloride.
Claim 8
Dependent Claim
50 words
The method of claim 2 wherein said spacer molecule is albumin, an alkyleneimine or an alkoxysilane and the step of applying a spacer molecule is accomplished by exposing said polymer coating to a solution of said spacer molecule for a period of between about two minutes and about thirty minutes.
Claim 9
Dependent Claim
40 words
The method of claim 7 wherein the step of applying a spacer molecular is accomplished by exposing the polymer coating to an aqueous solution of albumin or polyethyleneimine, said solution also including at least about 5.0 mg/ml of N-(3-dimethylaminopropyl)-N'-ethylcarbodiimide hydrochloride.
Claim 10
Dependent Claim
37 words
The method of claim 7 wherein the step of applying a spacer molecule is accomplished by exposing the polymer coating to a solution of trimethoxysilane in 95% ethanol for a period of at least about 3 minutes.
Claim 11
Dependent Claim
76 words
A medical device having a biocompatible antithrombogenic metallic surface, comprising: a metallic surface having a biologically active treatment adhered thereto; said biologically active treatment including a coating of heptafluorobutylmethacrylate polymer having reactive groups thereon, and a biologically active agent covalently bonded to said reactive groups; whereby the biocompatible metallic surface, when implanted within a blood vessel, substantially prevents thrombus formation thereon while avoiding any significant interference of the development of endothelialization of the biocompatable metallic surface.
Claim 12
Dependent Claim
76 words
A medical device having a biocompatible antithrombogenic metallic surface, comprising: a metallic surface having a biologically active treatment adhered thereto; said biologically active treatment including a coating of heptafluorobutylmethacrylate polymer having reactive groups thereon, and a biologically active agent covalently bonded to said reactive groups; whereby the biocompatible metallic surface, when implanted within a blood vessel, substantially prevents thrombus formation thereon while avoiding any significant interference of the development of endothelialization of the biocompatable metallic surface.
Claim 13
Dependent Claim
14 words
The medical device of claim 10 wherein said metallic surface is an endovascular stent.
Claim 14
Dependent Claim
51 words
The medical device of claim 10 wherein said biologically active agent is selected from the group consisting essentially of heparins, hirudin, hyaluronic acid, D-phenylalanyl-L-proyl-L-arginine chloromethyl ketone, vascular endothelial growth factor, gelatin, fibronectin, collagen, laminin, matrigel, victronectin, anti-β-FGF, meulinolin, enoxaparin, 5-fluorouracil, platelet growth factor antagonist, vasoconstrictors and vasodilators, and cellular adhesion promotors.
Claim 15
Dependent Claim
82 words
A medical device having a biocompatible antithrombogenic metallic surface, comprising: a metallic surface with a biologically compatible treatment adhered thereto; said biologically active treatment including a heptafluorobutylmethacrylate polymer coating adhered to said metallic surface, a spacer molecule covalently bonded to said polymer coating and a biologically active agent covalently bonded to said spacer molecule; whereby, the biocompatible metallic member, when implanted within a blood vessel, prevents substantial thrombus from occurring on its surface while not significantly interfering with endothelialization of said surface.
Claim 16
Dependent Claim
82 words
A medical device having a biocompatible antithrombogenic metallic surface, comprising: a metallic surface with a biologically compatible treatment adhered thereto; said biologically active treatment including a heptafluorobutylmethacrylate polymer coating adhered to said metallic surface, a spacer molecule covalently bonded to said polymer coating and a biologically active agent covalently bonded to said spacer molecule; whereby, the biocompatible metallic member, when implanted within a blood vessel, prevents substantial thrombus from occurring on its surface while not significantly interfering with endothelialization of said surface.
Claim 17
Dependent Claim
14 words
The medical device of claim 13 wherein said metallic surface is an endovascular stent.
Claim 18
Dependent Claim
23 words
The medical device of claim 13 wherein said spacer molecule is selected from a group consisting essentially of albumin, polyethyleneimine, and N-(2-aminoethyl-3-aminopropyl) trimethoxysilane.
Claim 19
Dependent Claim
51 words
The medical device of claim 13 wherein said biologically active agent is selected from the group consisting essentially of heparins, hirudin, hyaluronic acid, D-phenylalanyl--L-proyl-L-arginine chloromethyl ketone, vascular endothelial growth factor, gelatin, fibronectin, collagen, laminin, matrigel, victronectin, anti-β-FGF, meulinolin, enoxaparin, 5-fluorouracil, platelet growth factor antagonist, vasoconstrictors and vasodilators, and cellular adhesion promotors.
References Cited (Backward Citations)
US3639141A
Cited
US3549409A
Cited
US3826678A
Cited
GB1583008A
Cited
US4378435A
Cited
US4634762A
Cited
US5034265A
Cited
US4521564A
Cited
US5100689A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-08-08 | 1998-02-07 | 1998-08-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-08-08 | 2002-02-07 | 2002-08-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-08-08 | 2006-02-07 | 2006-08-09 | $7700.00 | Window Closed / Lapsed |