Nitrogen plasma treatment to prevent field device leakage in VLSI processing
Assignee: Taiwan Semiconductor Manufacturing Co TSMC Ltd
•
Filing: 1992-01-24
•
Granted: 1994-08-02
•
Expires: 2012-01-24
Abstract
Abstract A method for forming multiple layer metallurgy, spin-on-glass multilayer metallurgy for a one micrometer or less feature size integrated circuit with substantially free field inversion, that is the positive charge between the first via layer and the SOG is described. A semiconductor substrate having a pattern of field effect device source/drain regions therein with a pattern of gate dielectric and gate electrode structures associated therewith and a pattern of field isolation structures at least partially within semiconductor substrate electrically separating certain of these source/drain regions from one another are provided. A passivation layer is formed over the surfaces of said patterns. Then the multilayer metallurgy is formed thereover by opening a pattern of openings through the passivation layer to at least some of the source/drain regions, depositing and patterning a first metallurgy layer in contact with the pattern of openings, forming a first via dielectric layer over the pattern of first metallurgy layer, exposing the first silicon oxide via dielectric layer to a nitrogen plasma, forming a spin-on-glass layer over the via dielectric layer and curing the layer, forming a second via dielectric layer over the spin-on-glass layer, forming a pattern of openings in the second via layer, the spin-on-glass layer, and the first via layer, and depositing and patterning a second metallurgy layer through the openings to make electrical contact with the first metallurgy layer.
Inventors
- 👤 Kwang-Ming Lin
- 👤 Lih-Shyig Tsai
- 👤 Jiunn-Jyi Lin
- 👤 Yung-Haw Liaw
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 15:10
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/071; H10W20/092; H10W20/093; H10W20/096; H10W20/097
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
239 words
A method for forming multiple metal, spin-on-glass multilayer metallurgy for a one micrometer or less feature size integrated circuit without field inversion comprising: providing a semiconductor substrate having a pattern of field effect device source/drain regions therein with a pattern of gate dielectric and gate electrode structures associated therewith and a pattern of field isolation structures at least partially within said semiconductor substrate electrically separating certain of these source/drain regions from one another; forming a passivation layer over the surfaces of said patterns; and forming said multilayer metallurgy thereover by: opening a pattern of openings through said passivation layer to at least some of said source/drain regions, depositing and patterning a first metallurgy layer in contact with said pattern of openings; forming a first silicon oxide via dielectric layer over said pattern of first metallurgy layer; exposing said first silicon oxide dielectric layer to a nitrogen containing plasma containing no hydrogen ions at a temperature of less than about 450° C.; forming a spin-on-glass layer over said via dielectric layer and curing the layer; forming a second silicon oxide via dielectric layer over said spin-on-glass layer; forming a pattern of openings in said second via layer, said spin-on-glass layer, and said first via layer; and depositing and patterning a second metallurgy layer in contact with said pattern of openings to make electrical contact with said first metallurgy layer wherein said multilevel metallurgy integrated circuit without field inversion is completed.
Claim 2
Independent Claim
239 words
A method for forming multiple metal, spin-on-glass multilayer metallurgy for a one micrometer or less feature size integrated circuit without field inversion comprising: providing a semiconductor substrate having a pattern of field effect device source/drain regions therein with a pattern of gate dielectric and gate electrode structures associated therewith and a pattern of field isolation structures at least partially within said semiconductor substrate electrically separating certain of these source/drain regions from one another; forming a passivation layer over the surfaces of said patterns; and forming said multilayer metallurgy thereover by: opening a pattern of openings through said passivation layer to at least some of said source/drain regions, depositing and patterning a first metallurgy layer in contact with said pattern of openings; forming a first silicon oxide via dielectric layer over said pattern of first metallurgy layer; exposing said first silicon oxide dielectric layer to a nitrogen containing plasma containing no hydrogen ions at a temperature of less than about 450° C.; forming a spin-on-glass layer over said via dielectric layer and curing the layer; forming a second silicon oxide via dielectric layer over said spin-on-glass layer; forming a pattern of openings in said second via layer, said spin-on-glass layer, and said first via layer; and depositing and patterning a second metallurgy layer in contact with said pattern of openings to make electrical contact with said first metallurgy layer wherein said multilevel metallurgy integrated circuit without field inversion is completed.
Claim 3
Dependent Claim
25 words
The method of claim 1 wherein said passivation layer is composed of a composite layer of silicon oxide and a thicker layer of borophosphosilicate glass.
Claim 4
Dependent Claim
30 words
The method of claim 2 wherein said thickness of said silicon oxide is between about 800 to 1400 Angstroms and said borophophosilicate glass is between about 2000 to 8000 Angstroms.
Claim 5
Dependent Claim
15 words
The method of claim 1 wherein the source of said nitrogen ions is nitrogen gas.
Claim 6
Dependent Claim
17 words
The method of claim 1 wherein the time of said exposure is more than about 30 seconds.
Claim 7
Dependent Claim
33 words
The method of claim 4 wherein the said plasma is under a vacuum of less than about 20 torr. and the gas flow of said nitrogen is between about 500 to 5000 sccm.
Claim 8
Dependent Claim
33 words
The method of claim 1 wherein said spin-on-glass is a silicate type material and has an unetched thickness of between about 1500 to 3500 Angstroms when said second via layer is formed thereover.
Claim 9
Dependent Claim
33 words
The method of claim 1 wherein said spin-on-glass is a siloxane type material and has an unetched thickness of between about 1500 to 3500 Angstroms when said second via layer is formed thereover.
Claim 10
Dependent Claim
39 words
The method of claim 1 wherein said first metallurgy layer is aluminum and is between about 5000 to 10,000 Angstroms in thickness and said second metallurgy layer is aluminum and is between about 5000 to 11,000 Angstroms in thickness.
Claim 11
Independent Claim
195 words
A method for forming multiple metal, spin-on-glass multilayer metallurgy for a one micrometer or less feature size integrated circuit without field inversion on a semiconductor substrate having a pattern of device regions therein comprising: forming a passivation layer over the surfaces of said patterns; opening a pattern of openings through said passivation layer to at least some of said device regions which include source/drain regions, depositing and patterning a first metallurgy layer in contact with said pattern of openings; forming a first dielectric via layer over said pattern of first metallurgy layer; exposing said first silicon oxide dielectric layer to a nitrogen containing plasma containing no hydrogen ions at a temperature of less than about 450° C.; forming a spin-on-glass layer over said via dielectric layer and curing the layer; forming a silicon oxide second via dielectric layer over said spin-on-glass layer; forming a pattern of openings in said second via layer, said spin-on-glass layer and said first via layer; and depositing and patterning a second metallurgy layer in contact with said pattern of openings to make electrical contact with said first metallurgy layer wherein said multilevel metallurgy integrated circuit without field inversion is completed.
Claim 12
Independent Claim
195 words
A method for forming multiple metal, spin-on-glass multilayer metallurgy for a one micrometer or less feature size integrated circuit without field inversion on a semiconductor substrate having a pattern of device regions therein comprising: forming a passivation layer over the surfaces of said patterns; opening a pattern of openings through said passivation layer to at least some of said device regions which include source/drain regions, depositing and patterning a first metallurgy layer in contact with said pattern of openings; forming a first dielectric via layer over said pattern of first metallurgy layer; exposing said first silicon oxide dielectric layer to a nitrogen containing plasma containing no hydrogen ions at a temperature of less than about 450° C.; forming a spin-on-glass layer over said via dielectric layer and curing the layer; forming a silicon oxide second via dielectric layer over said spin-on-glass layer; forming a pattern of openings in said second via layer, said spin-on-glass layer and said first via layer; and depositing and patterning a second metallurgy layer in contact with said pattern of openings to make electrical contact with said first metallurgy layer wherein said multilevel metallurgy integrated circuit without field inversion is completed.
Claim 13
Dependent Claim
15 words
The method of claim 10 wherein the source of said nitrogen ions is nitrogen gas.
Claim 14
Dependent Claim
17 words
The method of claim 10 wherein the time of said exposure is more than about 30 seconds.
Claim 15
Dependent Claim
33 words
The method of claim 10 wherein the said plasma is under a vacuum of less than about 20 torr. and the gas flow of said nitrogen is between about 500 to 5000 sccm.
Claim 16
Dependent Claim
33 words
The method of claim 10 wherein said spin-on-glass is a silicate type material and has an unetched thickness of between about 1500 to 3500 Angstroms when said second via layer is formed thereover.
Claim 17
Dependent Claim
33 words
The method of claim 10 wherein said spin-on-glass is a siloxane type material and has an unetched thickness of between about 1500 to 3500 Angstroms when said second via layer is formed thereover.
Claim 18
Dependent Claim
39 words
The method of claim 10 wherein said first metallurgy layer is aluminum and is between about 5000 to 10,000 Angstroms in thickness and said second metallurgy layer is aluminum and is between about 5000 to 11,000 Angstroms in thickness.
Claim 19
Dependent Claim
18 words
The field effect device having a multiple metal spin-on-glass multilayer metallurgy made by the method of claim 10.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-08-01 | 1998-01-31 | 1998-08-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-08-01 | 2002-01-31 | 2002-08-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-08-01 | 2006-01-31 | 2006-08-02 | $7700.00 | Window Closed / Lapsed |