Method for producing metal powders

Claim 3

The method according to claim 1, wherein said milling comprises solid state microblending, said carbon containing substance and said at least one alloying component comprise an alloying material and said method further comprises: providing a substantial portion of the carbon of said alloying material as a carbide; and pretreating said alloying material by heating said alloying material in at least one of: a vacuum, and an inert atmosphere, to remove oxygen from said alloying material and react free carbon in the alloying material.

Claim 4

The method according to claim 2, wherein said free carbon comprises at least one of: elemental carbon, and graphite.

Claim 5

The method according to claim 3, wherein said pretreating comprises pretreating said alloying material to substantially remove all of the free carbon from the alloying material.

Claim 6

The method according to claim 4, wherein said pretreating comprises pretreating solely said alloying material to substantially remove the oxygen and substantially remove all of the free carbon from the alloying material.

Claim 7

The method according to claim 5, wherein the base iron powder has a compressibility, said at least one alloying component comprises: vanadium, tungsten, molybdenum and chromium, and said method further comprises: providing at least some of the substantial portion of carbon as vanadium carbide; providing a substantial portion of the vanadium as vanadium carbide; providing each of the tungsten, the molybdenum and the chromium as one of: A) a carbided alloying component; B) a mixture of carbided alloying component and substantially carbon free alloying component, and C) substantially carbon free alloying component; and annealing said intermediate milled product to produce a metal composite powder having a compressibility similar to that of said base iron powder prior to milling.

Claim 10

The method according to claim 7, wherein said at least a first alloying substance comprises at least one additional alloying component, the steel alloy powder has a predetermined carbon content, the steel alloy powder has a predetermined alloy content of said at least one additional alloying component, and said method further comprises: providing the at least one additional alloying component as one of: A) a carbide alloying component, B) a mixture of carbide alloying component and substantially carbon free alloying component, and C) a substantially carbon free alloying component; providing an amount of each of: said carbide of the at least one alloying substance, and said carbide of the at least one additional alloying component, to provide a substantial portion of the predetermined carbon content; and providing an amount of each of: said carbide of the at least one additional alloying component, and said substantially carbon free alloying component, to provide the predetermined alloy content of the at least one additional alloying component.

Claim 11

The method according to claim 8, wherein said at least a first alloying substance comprises vanadium and said method further comprises: providing at least some of the substantial portion of carbon as vanadium carbide; providing substantially all of the vanadium as vanadium carbide; and wherein said pretreating of said at least a first alloying substance comprises pretreating a mixture of said vanadium carbide and said at least one additional alloying component to remove oxygen and free carbon from the mixture.

Claim 12

The method according to claim 9, wherein: said pretreating comprises: heating the mixture to a first predetermined temperature in at least one of: a vacuum, and an inert atmosphere, to remove oxygen from said mixture and permit reaction of the free carbon; and cooling the mixture; said base iron has a compressibility and said method further comprises the steps of: annealing the milled steel alloy powder to produce a powder having a compressibility approaching the compressibility of the base iron prior to said milling; formulation the steel alloy powder to produce a steel alloy powder for high speed steels; dry milling said high speed steel powder by solid state microblending, said solid state microblending comprises dry milling in a ball mill under an inert atmosphere to disperse and embed the at least one alloying component in the base iron; and said providing of said at least one additional alloying component comprises providing one of the following groups of alloying components: (D) chromium, tungsten and molybdenum, and (E) chromium, tungsten, molybdenum and cobalt.

Claim 13

The method according to claim 10, wherein: said pretreating comprises removing all of the free carbon from the mixture; said free carbon comprises at least one of: elemental carbon, and graphite; said heating the mixture to a first predetermined temperature comprises heating the mixture to about 1100° C. for 2.5 hours; said solid state microblending further comprises: milling in a gravity dependent ball mill with 3/16 inch steel balls at 35-37.5 rpm; milling under an argon atmosphere; milling said at least one alloying component for 1 hour; adding the base iron and milling for 16-20 hours; and annealing the milled powder in an inert atmosphere at a temperature between about 500° C. to about 1000° C. for a respective period of time from about 8 hours at the lower temperature to about 5 minutes at the higher temperature to thereby produce the steel powder having: compressibility similar to that of the base iron, flowability, and sinterability for producing a high speed steel product having a density greater than about 98% of maximum density after compaction and sintering; said method further comprises producing an alloy metal of one of the following steels: M2 steel, M42 steel, and T15 steel, by mixing said at least a first alloying component to provide one of the following compositions: ______________________________________ for the M2 steel: 5.7-6.0 wt. % tungsten 4.75-5.0 wt. % molybdenum 1.90-2.0 wt. % vanadium 3.80-4.0 wt. % chromium 0.00-5.0 wt. % Al.sub.2 O.sub.3 1.0 wt. % carbon balance iron; for the M42 steel: 1.6 wt. % tungsten 9.5 wt. % molybdenum 1.2 wt. % vanadium 3.75 wt. % chromium 8.0 wt. % cobalt 1.15 wt. % carbon balance iron; and for the T15 steel: 12.0-12.5 wt. % tungsten 0.0-1.0 wt. % molybdenum 5.0 wt. % vanadium 4.25-4.50 wt. % chromium 5.0 wt. % cobalt 1.65 wt. % carbon balance iron. ______________________________________

Claim 14

The method according to claim 7, wherein said steel alloy powder additionally comprises alumina and said method further comprises the step of: pretreating the alumina with ferrochromium prior to said milling to increase sinterability of the steel alloy powder and increase bonding with the metallic phase; and milling together the pretreated alumina, base iron, and said at least one alloying substance.

Claim 15

The method according to claim 12, wherein said pretreating of the alumina comprises: mixing the alumina with ferrochromium; and heating the alumina-ferrochromium mixture to a first predetermined temperature in a vacuum to produce the pretreated alumina.

Claim 16

The method according to claim 13, wherein said pretreating of the at least a first alloying substance comprises treating the at least a first alloying substance and the pretreated alumina to remove oxygen and free carbon from the at least a first alloying substance and the pretreated alumina, said treating comprising: heating the pretreated alumina and the at least a first alloying substance to a first predetermined temperature in at least one of: a vacuum, and an inert atmosphere, to remove oxygen and permit reaction of the free carbon; and cooling the mixture.

Claim 17

The method according to claim 14, wherein: said at least a first alloying substance comprises vanadium, tungsten, molybdenum, and chromium; said steel alloy powder comprises a predetermined content of each of: carbon, vanadium, tungsten, molybdenum, and chromium; said treating the at least a first alloying substance and the pretreated alumina comprises removing all of the free carbon from the alloying material; said free carbon comprises at least one of: elemental carbon, and graphite; said heating to a first predetermined temperature comprises heating to about 1093° C. for 2 hours; said heating the mixture to a second predetermined temperature comprises heating the mixture to about 1100° C. for 2.5 hours; and said solid state microblending further comprises: milling in a gravity dependent ball mill with 3/16 inch steel balls at 35-37.5 rpm; milling under an argon atmosphere; milling said at least one alloying element and said carbon for 1 hour; and adding the base iron and milling for 16-20 hours; and said method further comprises: providing a substantial portion of the vanadium content as vanadium carbide; providing at least some of the tungsten, molybdenum, and chromium content as carbides of the tungsten, molybdenum, and chromium; providing at least some of the substantial portion of the carbon content from the vanadium carbide; providing a remaining portion of the substantial portion of the carbon content from the carbide of at least one of the tungsten, molybdenum, and chromium; providing a remaining portion of the tungsten, molybdenum, and chromium content as substantially carbon free tungsten, molybdenum and chromium.

Claim 18

A high alloy metal powder for use in powder metallurgy for producing pressed and sintered metal parts and produced by the process according to claim 7.

Claim 19

A composite metal powder for use in powdered metallurgy for producing sintered products, said composite metal powder comprising: a base iron; carbided alloying components dispersed and embedded in the base iron by solid state microblending, said carbided alloying component for providing a substantial portion of a carbon content of the alloy of the sintered product; non-carbided alloying components dispersed and embedded in the base iron by solid state microblending, said non-carbided alloying components and said carbided alloying components for providing a non-carbon portion of the alloy of the sintered product; and wherein said carbided alloying components and said non-carbided alloying components are pretreated, separately from said base iron, to remove a substantial portion of oxygen and free carbon from said carbided alloying component and said non-carbided alloying component prior to said solid state microblending.

Claim 20

A composite metal powder for use in powdered metallurgy for producing sintered products, said composite metal powder comprising: a base iron; carbided alloying components dispersed and embedded in the base iron by solid state microblending, said carbided alloying component for providing a substantial portion of a carbon content of the alloy of the sintered product; non-carbided alloying components dispersed and embedded in the base iron by solid state microblending, said non-carbided alloying components and said carbided alloying components for providing a non-carbon portion of the alloy of the sintered product; and wherein said carbided alloying components and said non-carbided alloying components are pretreated, separately from said base iron, to remove a substantial portion of oxygen and free carbon from said carbided alloying component and said non-carbided alloying component prior to said solid state microblending.

Claim 21

The metal powder according to claim 19, wherein said free carbon comprises at least one of: elemental carbon; and graphite.

Claim 22

The metal powder according to claim 18, wherein said carbided alloying components and non-carbided alloying components have substantially all of the free carbon removed therefrom by the pretreatment prior to said solid state microblending.

Claim 23

The metal powder according to claim 19, wherein solely said carbided alloying components and non-carbided alloying components have substantially all of the free carbon removed therefrom by the pretreatment prior to said solid state microblending.

Claim 24

The metal powder according to claim 20, wherein said composite metal powder comprises an annealed powder of said base iron powder having said carbided alloying components and non-carbided alloying components dispersed and embedded therein, said annealed powder having been produced by heating said base iron powder having said carbided alloying components and non-carbided alloying components dispersed and embedded therein.

Claim 25

The metal powder according to claim 21, wherein said composite metal powder has a compressibility, flowability and sinterability to produce a sintered product having a density greater than about 98% of a maximum density.

Claim 26

The metal powder according to claim 22, wherein: said carbided alloying components and non-carbided alloying components comprise components of: tungsten, molybdenum, chromium, and vanadium; said metal powder comprises a high alloy metal powder for producing high speed steel products, said high alloy metal powder comprising one of: an M2 steel powder; an M42 steel powder; and a T15 steel powder.