US5326713A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Buried contact process
Assignee: Taiwan Semiconductor Manufacturing Co TSMC Ltd
•
Filing: 1992-09-04
•
Granted: 1994-07-05
•
Expires: 2012-09-04
Abstract
Abstract A method of forming a buried contact to a source/drain junction or other active device region in a silicon substrate. A silicon oxide layer is formed over the silicon substrate. A first polysilicon layer is formed over the silicon oxide layer. A resist mask having an opening over the planned said buried contact is formed and the first polysilicon layer is isotropically etched to form a tapered opening to said underlying silicon oxide which opening undercuts the resist mask. The silicon oxide layer is anisotropically etched using the same resist mask which results in an opening to the silicon substrate corresponding to the resist pattern opening while leaving a silicon oxide border uncovered with the first polysilicon layer. A second polysilicon layer is deposited over the first polysilicon layer, the opening to the silicon substrate and the border of uncovered silicon oxide. The planned buried contact region is covered with a resist mask. Openings are formed to the planned source and drain regions wherein at least one of the source and drain regions is adjacent to the opening of the planned buried contact. The resist mask is removed. Ions are implanted through the second polysilicon layer in the opening to the silicon substrate to form the source and drain regions. The structure is heated to cause the formation of the buried region under the buried contact by outdiffusion from the buried contact layer.
Inventors
- 👤 Jin-Yuan Lee
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 23:28
CPC Classifications
H; H10; H10D; H10D64/00; H10D64/01; H10D64/011; H10D64/0111; H10D64/0113; Y; Y10; Y10S; Y10S438/00; Y10S438/965
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
238 words
The method of forming a buried contact to source/drain regions in a silicon substrate comprising: forming a silicon oxide layer over said silicon substrate; forming a first polysilicon layer over said silicon oxide layer; providing a resist mask having an opening over the planned said buried contact and isotropically etching said first polysilicon layer to form a tapered opening to said underlying silicon oxide which opening undercuts said resist mask; anisotropically etching said silicon oxide layer using the said resist mask which results in an opening to said silicon substrate corresponding to the planned said buried contact while leaving a silicon oxide border uncovered with said first polysilicon layer; depositing a second polysilicon layer over said first polysilicon layer, the opening to said silicon substrate and said border of uncovered silicon oxide; masking the planned said buried contact with a resist mask; forming openings to the planned said source and drain regions wherein at least one of said source and drain regions is adjacent to said opening of the planned buried contact; removing said resist mask; implanting ions through said second polysilicon layer in said opening to said silicon substrate to form said source and drain regions; and heating the structure to cause the formation of a buried region under said buried contact by outdiffusion from the first and second polysilicon layers and to make electrical contact to at least one of said adjacent source and drain regions.
Claim 2
Independent Claim
238 words
The method of forming a buried contact to source/drain regions in a silicon substrate comprising: forming a silicon oxide layer over said silicon substrate; forming a first polysilicon layer over said silicon oxide layer; providing a resist mask having an opening over the planned said buried contact and isotropically etching said first polysilicon layer to form a tapered opening to said underlying silicon oxide which opening undercuts said resist mask; anisotropically etching said silicon oxide layer using the said resist mask which results in an opening to said silicon substrate corresponding to the planned said buried contact while leaving a silicon oxide border uncovered with said first polysilicon layer; depositing a second polysilicon layer over said first polysilicon layer, the opening to said silicon substrate and said border of uncovered silicon oxide; masking the planned said buried contact with a resist mask; forming openings to the planned said source and drain regions wherein at least one of said source and drain regions is adjacent to said opening of the planned buried contact; removing said resist mask; implanting ions through said second polysilicon layer in said opening to said silicon substrate to form said source and drain regions; and heating the structure to cause the formation of a buried region under said buried contact by outdiffusion from the first and second polysilicon layers and to make electrical contact to at least one of said adjacent source and drain regions.
Claim 3
Dependent Claim
20 words
The method of claim 1 wherein the thickness of said silicon oxide layer is between about 80 and 250 Angstroms.
Claim 4
Dependent Claim
20 words
The method of claim 1 wherein the thickness of said first polysilicon layer is between about 1000 and 4000 Angstroms.
Claim 5
Dependent Claim
24 words
The method of claim 1 wherein said etching of said first polysilicon layer is a reactive ion isotropic dry etch using SF 6 /He.
Claim 6
Dependent Claim
27 words
The method of claim 1 wherein the said etching of said silicon oxide layer is a reactive ion anisotropic dry etch using CF 4 /CHF 3 .
Claim 7
Dependent Claim
21 words
The method of claim 1 wherein the thickness of said second layer of polysilicon is between about 300 and 1000 Angstroms.
Claim 8
Dependent Claim
32 words
The method of claim 1 wherein said outdiffusion formation of said buried region comprises conditions 850° to 950° C. in a nitrogen atmosphere with a small percentage of oxygen for wafer monitoring.
Claim 9
Independent Claim
234 words
The method of forming a buried contact to active device regions in a silicon substrate comprising: forming a silicon oxide layer over said silicon substrate; forming a first polysilicon layer over said silicon oxide layer; providing a resist mask having an opening over the planned said buried contact and isotropically etching said first polysilicon layer to form a tapered opening to said underlying silicon oxide which opening undercuts said resist mask; anisotropically etching said silicon oxide layer using the said resist mask which results in an opening to said silicon substrate corresponding to the planned said buried contact while leaving a silicon oxide border uncovered with said first polysilicon layer; depositing a second polysilicon layer over said first polysilicon layer, the opening to said silicon substrate and said border of uncovered silicon oxide; masking the planned said buried contact with a resist mask; forming openings to the planned said active device regions wherein at least one of said device regions is adjacent to said opening of the planned buried contact; removing said resist mask; implanting ions through said second polysilicon layer in said opening to said silicon substrate to form said active device regions; and heating the structure to cause the formation of a buried region under said buried contact by outdiffusion from the first and second polysilicon layers and to make electrical contact to at least one of said adjacent active device regions.
Claim 10
Independent Claim
234 words
The method of forming a buried contact to active device regions in a silicon substrate comprising: forming a silicon oxide layer over said silicon substrate; forming a first polysilicon layer over said silicon oxide layer; providing a resist mask having an opening over the planned said buried contact and isotropically etching said first polysilicon layer to form a tapered opening to said underlying silicon oxide which opening undercuts said resist mask; anisotropically etching said silicon oxide layer using the said resist mask which results in an opening to said silicon substrate corresponding to the planned said buried contact while leaving a silicon oxide border uncovered with said first polysilicon layer; depositing a second polysilicon layer over said first polysilicon layer, the opening to said silicon substrate and said border of uncovered silicon oxide; masking the planned said buried contact with a resist mask; forming openings to the planned said active device regions wherein at least one of said device regions is adjacent to said opening of the planned buried contact; removing said resist mask; implanting ions through said second polysilicon layer in said opening to said silicon substrate to form said active device regions; and heating the structure to cause the formation of a buried region under said buried contact by outdiffusion from the first and second polysilicon layers and to make electrical contact to at least one of said adjacent active device regions.
Claim 11
Dependent Claim
20 words
The method of claim 8 wherein the thickness of said silicon oxide layer is between about 80 and 250 Angstroms.
Claim 12
Dependent Claim
20 words
The method of claim 8 wherein the thickness of said first polysilicon layer is between about 1000 and 4000 Angstroms.
Claim 13
Dependent Claim
24 words
The method of claim 8 wherein said etching of said first polysilicon layer is a reactive ion isotropic dry etch using SF 6 /HE.
Claim 14
Dependent Claim
27 words
The method of claim 8 wherein the said etching of said silicon oxide layer is a reactive ion anisotropic dry etch using CF 4 /CHF 3 .
Claim 15
Dependent Claim
21 words
The method of claim 8 wherein the thickness of said second layer of polysilicon is between about 300 and 1000 Angstroms.
Claim 16
Dependent Claim
32 words
The method of claim 8 wherein said outdiffusion formation of said buried region comprises conditions 850° to 950° C. in a nitrogen atmosphere with a small percentage of oxygen for wafer monitoring.
References Cited (Backward Citations)
US3750268A
Cited
JPS53147473A
Cited
JPS5457881A
Cited
JPS592191A
Cited
JPS60170974A
Cited
US5030584A
Cited
US5049514A
Cited
US5214295A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-07-04 | 1998-01-03 | 1998-07-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-07-04 | 2002-01-03 | 2002-07-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-07-04 | 2006-01-03 | 2006-07-05 | $7700.00 | Window Closed / Lapsed |