Method of forming SI-O containing coatings
Assignee: Dow Silicones Corp
•
Filing: 1993-09-13
•
Granted: 1994-06-14
•
Expires: 2013-09-13
Abstract
Abstract Disclosed is a method for forming improved Si--O containing coatings on electronic substrate. The method comprises converting hydrogen silsesquioxane resin into a Si--O containing ceramic coating in the presence of hydrogen gas. The resultant coatings have improved properties such as stable dielectric constants.
Inventors
- 👤 David S. Ballance
- 👤 Keith W. Michael
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 19:13
CPC Classifications
C; C09; C09D; C09D183/00; C09D183/04; C04; C04B; C04B35/00; C04B35/622; C04B35/62222; C08; C08G; C08G77/00; C08G77/04; C08G77/12; C23; C23C; C23C18/00; C23C18/02; C23C18/12; C23C18/1204; C23C18/1208; C23C18/1212; C23C18/122; C23C18/125; C23C18/1279
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
73 words
A method of forming an Si--O containing ceramic coating on an electronic substrate comprising: applying a coating comprising hydrogen silsesquioxane resin on an electronic substrate; and heating the coated substrate in a pyrolysis atmosphere at a temperature sufficient to convert the hydrogen silsesquioxane resin coating to an Si--O containing ceramic coating wherein hydrogen gas is introduced into the pyrolysis atmosphere during conversion of the hydrogen silsesquioxane resin to the Si--O containing ceramic coating.
Claim 2
Independent Claim
73 words
A method of forming an Si--O containing ceramic coating on an electronic substrate comprising: applying a coating comprising hydrogen silsesquioxane resin on an electronic substrate; and heating the coated substrate in a pyrolysis atmosphere at a temperature sufficient to convert the hydrogen silsesquioxane resin coating to an Si--O containing ceramic coating wherein hydrogen gas is introduced into the pyrolysis atmosphere during conversion of the hydrogen silsesquioxane resin to the Si--O containing ceramic coating.
Claim 3
Dependent Claim
39 words
The method of claim 1 wherein the hydrogen silsesquioxane resin is applied to the substrate by a process which comprises coating the substrate with a solution comprising a solvent and the hydrogen silsesquioxane resin and then evaporating the solvent.
Claim 4
Dependent Claim
32 words
The method of claim 1 wherein the coated substrate is heated at a temperature in the range of between about 50° C. and about 1000° C. for less than about 6 hours.
Claim 5
Dependent Claim
32 words
The method of claim 1 wherein the hydrogen silsesquioxane resin contains polymeric species such that at least 75% of the polymeric species have a molecular weight between about 1200 and about 100,000.
Claim 6
Dependent Claim
80 words
The method of claim 1 wherein the hydrogen silsesquioxane resin containing coating also contains modifying ceramic oxide precursors comprising a compound containing an element selected from the group consisting of titanium, zirconium, aluminum, tantalum, vanadium, niobium, boron and phosphorous wherein the compound contains at least one hydrolyzable substituent selected from the group consisting of alkoxy or acyloxy and the compound is present in an amount such that the silica coating contains 0.1 to 30 percent by weight modifying ceramic oxide.
Claim 7
Dependent Claim
43 words
The method of claim 1 wherein the hydrogen silsesquioxane resin containing coating also contains a platinum, rhodium or copper catalyst in an amount of between about 5 and about 1000 ppm platinum, rhodium or copper based on the weight of hydrogen silsesquioxane resin.
Claim 8
Dependent Claim
36 words
The method of claim 1 wherein the pyrolysis atmosphere also contains a gas selected from the group consisting of air, O 2 , oxygen plasma, ozone, an inert gas, ammonia, amines, moisture, and N 2 O.
Claim 9
Dependent Claim
28 words
The method of claim 1 wherein the hydrogen gas in the pyrolysis atmosphere is in a concentration in the range of about 1 to about 30 volume percent.
Claim 10
Dependent Claim
27 words
The method of claim 1 wherein the hydrogen gas in the pyrolysis atmosphere is in a concentration of less than or equal to about 5 volume percent.
Claim 11
Dependent Claim
75 words
In a method of forming an Si--O containing ceramic coating on an electronic substrate comprising applying a coating comprising hydrogen silsesquioxane resin on an electronic substrate and heating the coated substrate in a pyrolysis atmosphere at a temperature sufficient to convert the hydrogen silsesquioxane resin coating to an Si--O containing ceramic coating, the improvement comprises: introducing hydrogen gas into the pyrolysis atmosphere during conversion of the hydrogen silsesquioxane resin to the Si--O containing ceramic coating.
Claim 12
Dependent Claim
75 words
In a method of forming an Si--O containing ceramic coating on an electronic substrate comprising applying a coating comprising hydrogen silsesquioxane resin on an electronic substrate and heating the coated substrate in a pyrolysis atmosphere at a temperature sufficient to convert the hydrogen silsesquioxane resin coating to an Si--O containing ceramic coating, the improvement comprises: introducing hydrogen gas into the pyrolysis atmosphere during conversion of the hydrogen silsesquioxane resin to the Si--O containing ceramic coating.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-06-13 | 1997-12-13 | 1998-06-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-06-13 | 2001-12-13 | 2002-06-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-06-13 | 2005-12-13 | 2006-06-14 | $7700.00 | Window Closed / Lapsed |