Method of manufacturing an optical fibre
Assignee: Plasma Optical Fibre BV
•
Filing: 1992-08-28
•
Granted: 1994-06-14
•
Expires: 2012-08-28
Abstract
Abstract An optical fibre is manufactured by stretching a rod-shaped initial preform, after which a cladding tube is melted on the initial preform and the final preform thus obtained is drawn into an optical fibre. A narrow and hot softening zone is used to stretch the initial preform, which softening zone is obtained, for example, by means of a plasma torch 2. By virtue thereof, the stretching process can be controlled in a rapid and simple manner.
Inventors
- 👤 Antonius H. E. Breuls
- 👤 Andries H. Van Bergen
- 👤 Henrikus L. M. Jansen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 22:53
CPC Classifications
C; C03; C03B; C03B37/00; C03B37/01; C03B37/012; C03B37/01205; C03B37/01225; C03B37/0124; C03B23/00; C03B23/04; C03B23/047
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
156 words
In a method of manufacturing an optical fiber, in which method a rod-shaped initial preform having a core and a cladding surrounding this core is manufactured, the refractive index of the cladding being lower than that of the core, said method comprising stretching the initial preform by creating a softening zone in the initial preform, moving the softening zone longitudinally along the initial preform, melting at least one cladding tube on the initial preform and drawing the final preform into an optical fiber, wherein the improvement comprises that in stretching the initial preform a narrow and hot softening zone is used whose dimension in the longitudinal direction of the initial preform is less than 5 cm and in which the maximum temperature is at least 2300° C., and in that to obtain the softening zone an energy-supply device is used which causes no or almost no convective gas stream at the location of the initial preform.
Claim 2
Dependent Claim
156 words
In a method of manufacturing an optical fiber, in which method a rod-shaped initial preform having a core and a cladding surrounding this core is manufactured, the refractive index of the cladding being lower than that of the core, said method comprising stretching the initial preform by creating a softening zone in the initial preform, moving the softening zone longitudinally along the initial preform, melting at least one cladding tube on the initial preform and drawing the final preform into an optical fiber, wherein the improvement comprises that in stretching the initial preform a narrow and hot softening zone is used whose dimension in the longitudinal direction of the initial preform is less than 5 cm and in which the maximum temperature is at least 2300° C., and in that to obtain the softening zone an energy-supply device is used which causes no or almost no convective gas stream at the location of the initial preform.
Claim 3
Dependent Claim
43 words
A method as claimed in claim 1, in which the dimension of the softening zone in the longitudinal direction of the initial preform is less than 3 cm and in which the highest temperature in the softening zone is at least 2400° C.
Claim 4
Dependent Claim
19 words
A method as claimed in claim 2, characterized in that a plasma torch is used as the energy-supply device.
Claim 5
Dependent Claim
20 words
A method as claimed in claim 2, characterized in that a laser light source is used as the energy-supply device.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-06-13 | 1997-12-13 | 1998-06-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-06-13 | 2001-12-13 | 2002-06-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-06-13 | 2005-12-13 | 2006-06-14 | $7700.00 | Window Closed / Lapsed |