Processes for producing a thermoelectric material and a thermoelectric element
Assignee: National Institute of Advanced Industrial Science and Technology
•
Filing: 1992-11-27
•
Granted: 1994-06-07
•
Expires: 2012-11-27
Abstract
Abstract A process for producing a thermoelectric material comprises molding a material powder comprising two or more elements selected from the group consisting of bismuth, tellurium, antimony and selenium and having average diameter in the range from 0.05 to 100 mu m and sintering the molded material powder with or without hot isostatic pressing. The material powder may be calcinated before the molding. A process for producing a thermoelectric element comprises cutting out pieces of a pillar-like shape from each of a p-type thermoelectric material and a n-type thermoelectric material, connecting the pieces cut out from the p-type thermoelectric material and the pieces cut out from the n-type thermoelectric material alternately with electrodes at the upper faces or the lower faces of the pieces and attaching insulating base plates to the surfaces of the electrodes. The p-type thermoelectric material and the n-type thermoelectric material are respectively produced by the process described above. The thermoelectric element has improved thermoelectric property, excellent stability of the thermoelectric property and excellent mechanical strength.
Inventors
- 👤 Takeo Tokiai
- 👤 Takashi Uesugi
- 👤 Kazuyuki Fukumoto
- 👤 Toshitaka Ohta
- 👤 Takenobu Kajikawa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 12:07
CPC Classifications
C; C22; C22C; C22C1/00; C22C1/04; B; B22; B22F; B22F1/00; H; H10; H10N; H10N10/00; H10N10/80; H10N10/85; H10N10/851; H10N10/852
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
50 words
A process for producing a thermoelectric material which comprises presintering a material powder comprising two or more elements selected from the group consisting of bismuth, tellurium, antimony and selenium and having an average diameter of 0.05 to 100 μm, molding the presintered material powder and sintering the molded material powder.
Claim 2
Dependent Claim
50 words
A process for producing a thermoelectric material which comprises presintering a material powder comprising two or more elements selected from the group consisting of bismuth, tellurium, antimony and selenium and having an average diameter of 0.05 to 100 μm, molding the presintered material powder and sintering the molded material powder.
Claim 3
Dependent Claim
54 words
A process for producing a thermoelectric material which comprises presintering a material powder comprising two or more elements selected from the group consisting of bismuth, tellurium, antimony and selenium and having an average diameter of 0.05 to 100 μm, molding the calcined material powder and sintering the molded material powder by hot isostatic pressing.
Claim 4
Dependent Claim
54 words
A process for producing a thermoelectric material which comprises presintering a material powder comprising two or more elements selected from the group consisting of bismuth, tellurium, antimony and selenium and having an average diameter of 0.05 to 100 μm, molding the calcined material powder and sintering the molded material powder by hot isostatic pressing.
Claim 5
Dependent Claim
57 words
The process for producing a thermoelectric material as claimed in claim 1 wherein the material powder comprises a solid solution powder which is selected from the group consisting of Bi 2 Te 3 , Sb 2 Te 3 and (Bi 2 Te 3 ) x (Sb 2 Te 3 ) y , wherein x+y=1, 0<x<1 and 0<y<1.
Claim 6
Dependent Claim
57 words
The process for producing a thermoelectric material as claimed in claim 2 wherein the material powder comprises a solid solution powder which is selected from the group consisting of Bi 2 Te 3 , Sb 2 Te 3 and (Bi 2 Te 3 ) 3 (SB 2 Te 3 ) y , wherein x+y=1, 0<x<1 and 0<y<1.
Claim 7
Dependent Claim
52 words
The process for producing a thermoelectric material as claimed in claim 1 wherein the material powder comprises a solid solution powder which is selected from the group consisting of Bi 2 Se 3 and (Bi 2 Te 3 ) x (Bi 2 Se 3 ) y , wherein x+y=1, 0<x<1 and 0<y<1.
Claim 8
Dependent Claim
52 words
The process for producing a thermoelectric material as claimed in claim 2 wherein the material powder comprises a solid solution powder which is selected from the group consisting of Bi 2 Se 3 and (Bi 2 Te 3 ) x (Bi 2 Se 3 ) y , wherein x+y=1, 0<x<1 and 0<y<1.
Claim 9
Dependent Claim
41 words
The process for producing a thermoelectric material as claimed in claim 1 wherein the presintering of the material powder is carried out at a temperature of 50 to 90% of the maximum temperature of the sintering of the molded material powder.
Claim 10
Dependent Claim
41 words
The process for producing a thermoelectric material as claimed in claim 2 wherein the presintering of the material powder is carried out at a temperature of 50 to 90% of the maximum temperature of the sintering of the molded material powder.
Claim 11
Dependent Claim
71 words
The process for producing a thermoelectric material as claimed in claim 1 wherein the presintering of the material powder is carried out at a temperature such that a temperature pattern of the presintering is formed by parallel transfer of a temperature pattern of the sintering to temperatures, measured by the Celsius scale, in a range of 50 to 90% of the sintering temperature or to temperatures slightly lower than said range.
Claim 12
Dependent Claim
34 words
The process for producing a thermoelectric material as claimed in claim 2 wherein the calcination of a material powder is carried out at a temperature close to the melting temperature of the material powder.
Claim 13
Dependent Claim
62 words
The process for producing a thermoelectric material as claimed in claim 2 wherein the sintering of the molded material powder with hot isostatic pressing is carried out at a temperature in the range from 200° to 800° C. for a time in the range from 0.5 to 30 hours under a pressure in the range from 1,000 to 8,000 kg/cm 2 .
Claim 14
Dependent Claim
145 words
A process for producing a thermoelectric element which comprises (a) cutting out pieces, each piece having an upper face and a lower face, of a pillar-like shape from each of a p-type thermoelectric material and an n-type thermoelectric material, (b) connecting the pieces cut out from the p-type thermoelectric material and the pieces cut out from the n-type thermoelectric material, alternately, with electrodes having surfaces at the upper faces or the lower faces of the pieces and (c) attaching insulating base plates to the surfaces of the electrodes, the p-type thermoelectric material and the n-type thermoelectric material being individually produced by presintering a material powder comprising two or more elements selected from the group consisting of bismuth, tellurium, antimony and selenium, copulverizing and mixing the calcined material powder, molding the copulverized and mixed material powder and sintering the molded material powder by hot isostatic pressing.
Claim 15
Dependent Claim
145 words
A process for producing a thermoelectric element which comprises (a) cutting out pieces, each piece having an upper face and a lower face, of a pillar-like shape from each of a p-type thermoelectric material and an n-type thermoelectric material, (b) connecting the pieces cut out from the p-type thermoelectric material and the pieces cut out from the n-type thermoelectric material, alternately, with electrodes having surfaces at the upper faces or the lower faces of the pieces and (c) attaching insulating base plates to the surfaces of the electrodes, the p-type thermoelectric material and the n-type thermoelectric material being individually produced by presintering a material powder comprising two or more elements selected from the group consisting of bismuth, tellurium, antimony and selenium, copulverizing and mixing the calcined material powder, molding the copulverized and mixed material powder and sintering the molded material powder by hot isostatic pressing.
Claim 16
Dependent Claim
41 words
The process for producing a thermoelectric material as claimed in claim 3 wherein the average diameter of the material powder is 0.05 to 30 μm; and the molding being carried out at a pressure of 0.2 to 20 ton/cm 2 .
Claim 17
Dependent Claim
41 words
The process for producing a thermoelectric material as claimed in claim 4 wherein the average diameter of the material powder is 0.05 to 30 μm; and the molding being carried out at a pressure of 0.2 to 20 ton/cm 2 .
Claim 18
Dependent Claim
49 words
The process for producing a thermoelectric element as claimed in claim 12 wherein the copulvering and mixing are carried out simultaneously in a planetary ball mill at a pulverizing powder of 5×10 6 to 2×10 7 kg·m·s -1 /kg for a period of time of 0.5 to 60 hours.
Claim 19
Dependent Claim
92 words
The process for producing a thermoelectric element as claimed in claim 12 wherein the p-type thermoelectric material has a composition of Bi.sub.(1-v) Sb v .Te 1 .5, wherein 0<v<0.95, the n-type thermoelectric material has a composition of Bi 2 Te 3 (1-v). Se 3v , wherein 0.05<v0.95, the pillar-like shape being a square shape with a length of 1 to 5 mm and a width of 1 to 2 mm; the electrodes having a thickness of 50 to 500 μm and the alumina plates having a thickness of 0.2 to 2 mm.
References Cited (Backward Citations)
US4902648A
Cited
US5108515A
Cited
JPH03108781A
Cited
JPH03165076A
Cited
JPH03233980A
Cited
US5168339A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-06-06 | 1997-12-06 | 1998-06-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-06-06 | 2001-12-06 | 2002-06-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-06-06 | 2005-12-06 | 2006-06-07 | $7700.00 | Window Closed / Lapsed |