Polymer mixture for producing films

Claim 2

A polymer mixture consisting essentially of thermoplastically processable starch, at least one polyolefin, at least one vinyl compound carrying an anhydride substituent and an esterification product of the starch and the anhydride containing vinyl compound.

Claim 3

The polymer mixture in accordance with claim 1, characterized in that said vinyl compound is a terpolymer of ethylene, acrylate and maleic acid anhydride.

Claim 4

The polymer mixture in accordance with claim 2, characterized in that prior to mixing so as to form said esterification product, the polymer mixture contains up to 70% by weight of said thermoplastically processable starch, 10-90% by weight polyolefin and 1-35% by weight of said terpolymer.

Claim 5

The polymer mixture in accordance with claim 3, characterized in that said percentages are 40-70% by weight thermoplastically processable starch containing at least one plasticizing agent selected from the group consisting of glycerin, urea, and amino alcohol, sorbitol, succinic acid anhydride and mixtures thereof, 10-40% by weight of at least one member of the group consisting of polyethylene and polypropylene and 10-35% by weight of said terpolymer.

Claim 6

The polymer mixture in accordance with claim 4, characterized in that said percentages are 20-35% by weight of polyolefin and 15-25% by weight of terpolymer.

Claim 7

The polymer mixture in accordance with claim 2, characterized in that said terpolymer contains 80-95% by weight ethylene, 5-15% acrylate and 0.2-1% by weight maleic acid anhydride.

Claim 8

The polymer mixture in accordance with claim 6, characterized in that said acrylate is acrylic acid methyl ester, acrylic acid ethyl ester, or a mixture thereof.

Claim 9

A process for the production of a polymer mixture, consisting essentially of starch and a polyolefin, in accordance with claim 1, characterized in that natural starch or a derivative thereof is mixed with 15% by weight to 40% by weight of at least one essentially anhydrous plasticizing agent selected from the group consisting of glycerine, urea, an amino alcohol, sorbitol, succinic acid anhydride and mixtures thereof, for the production of thermoplastically processable starch, whereafter the same, at a temperature of between 165° C. to 210° C., is mixed in the melt with a polyolefin and an ethylene/acrylate/maleic acid anhydride terpolymer, whereby maleic acid anhydride groups in the polymer are esterified by means of free hydroxyl groups in the starch.

Claim 10

A process, in accordance with claim 8, characterized in that up to 70% by weight of thermoplastically processable starch is mixed in an extruder or kneader with 10% by weight to 40% by weight of at least one of polyethylene and polypropylene and 10% by weight to 35% by weight of an ethylene/acrylate/maleic acid anhydride terpolymer, whereby during the mixing process the total mechanical energy created amounts to approximately 0.4 kWh/kg.

Claim 11

A process, in accordance with claim 8 characterized in that natural starch or a derivative thereof having a moisture content of less than 1% is homogenized with said plasticizing agent at a temperature of 160° C. to 190° C. in an extruder or kneader, whereupon in a further extrusion or in the same extruder in a further step, mixing with at least one of polyethylene and polypropylene and said terpolymer takes place.

Claim 12

A process, in accordance with the claim 8, characterized in that the natural starch or a derivative thereof is pre-mixed with said plasticizing agent essentially at room temperature or at a raised temperature, whereupon the starch will swell, forming a dry granulate which subsequently will be used for further working and for mixing with said polyethylene or polypropylene, as well as with the terpolymer.

Claim 13

A process, in accordance with claim 8, characterized in that an ethylene/acrylate/maleic acid anhydride terpolymer is used which is obtained by working-up of 80% by weight to 95% by weight of ethylene, 1% by weight to 15% by weight of at least one of acrylic acid methyl ester and acrylic acid ethyl ester, as well as 0.1% by weight to 15% by weight of maleic acid anhydride.

Claim 14

A film, consisting of at least one single ply, consisting essentially of a polymer mixture in accordance with claim 1.

Claim 15

A process in accordance with claim 8 for the production of a single or multi-ply film comprising at least one ply consisting of a polymer mixture characterized in that the polymer mixture produced is processed into a film by means of an extrusion selected from the group consisting of wide-mouth extrusion, blow extrusion and co-extrusion.

Claim 16

A process in accordance with claim 14, characterized in that the mixture is co-extruded to produce a two-ply or multi-ply film.

Claim 17

A process in accordance with claim 8, for the production of a foam comprising a polymer mixture characterized in that prior to its extrusion a propelling agent or an organic acid, is added to the polymer mixture.

Claim 18

A moulded body or extrudate, consisting essentially of a polymer mixture in accordance with claim 1.