Conditioning metal powder for injection molding
Assignee: National City Bank
•
Filing: 1992-04-03
•
Granted: 1994-05-24
•
Expires: 2012-04-03
Abstract
Abstract Tungsten and molybdenum powders are advantageously conditioned for metal injection molding by fluid energy milling the powder prior to batching. A preferred method of conditioning, jet milling, has been found to beneficially effect the particle characteristics to render the metal powder more suitable for injection molding.
Inventors
- 👤 David N. Meendering
- 👤 Deepak Malhotra
- 👤 Linda K. Baltich
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 09:04
CPC Classifications
B; B22; B22F; B22F3/00; B22F3/22; B22F3/225; B22F9/00; B22F9/02; B22F9/04; B22F2998/00
Claims Analysis
Total Claims: 30
Claim 1
Independent Claim
43 words
A process for providing a metal powder feedstock, comprising: A. providing an as-received metal powder having a non-spherical particle shape; and B. conditioning the as-received metal powder using a fluid energy mill effective to provide a metal powder feedstock suitable for injection molding.
Claim 2
Dependent Claim
43 words
A process for providing a metal powder feedstock, comprising: A. providing an as-received metal powder having a non-spherical particle shape; and B. conditioning the as-received metal powder using a fluid energy mill effective to provide a metal powder feedstock suitable for injection molding.
Claim 3
Dependent Claim
16 words
The process as defined by claim 1, wherein the metal is tungsten, molybdenum, or mixtures thereof.
Claim 4
Dependent Claim
24 words
The process as defined by claim 2, wherein the conditioned powder has a distribution of particle sizes of 100% less than about 20 μm.
Claim 5
Dependent Claim
25 words
The process as defined by claim 2, wherein the conditioned powder has a mean particle size ranging between about 0.1 μm and about 10 μm.
Claim 6
Dependent Claim
14 words
The process as defined by claim 2, wherein the conditioning step includes jet milling.
Claim 7
Dependent Claim
31 words
The process as defined by claim 1, wherein the conditioned metal powder feedstock is characterized by a mixing torque of not more than about 2.5 N-m under standardized torque measurement conditions.
Claim 8
Dependent Claim
49 words
In a process for injection molding metal powder which includes the steps of batching the powder with a binder to produce a feedstock and injection molding the feedstock, an improvement which comprises conditioning a metal powder consisting essentially of tungsten and/or molybdenum by fluid energy milling prior to batching.
Claim 9
Dependent Claim
49 words
In a process for injection molding metal powder which includes the steps of batching the powder with a binder to produce a feedstock and injection molding the feedstock, an improvement which comprises conditioning a metal powder consisting essentially of tungsten and/or molybdenum by fluid energy milling prior to batching.
Claim 10
Dependent Claim
88 words
A process for injection molding a metal powder consisting essentially of molybdenum and/or tungsten, comprising: A. conditioning an as-received metal powder having an average particle size of less than about 15 μm by subjecting said as-received metal powder to fluid energy milling; B. batching the conditioned powder with a fluid selected from the group consisting of vehicles, binders, and solvents; C. injection molding the batched powder into a desired green shape; D. debinding the molded green shape to produce a green article; and E. densifying the green article.
Claim 11
Dependent Claim
88 words
A process for injection molding a metal powder consisting essentially of molybdenum and/or tungsten, comprising: A. conditioning an as-received metal powder having an average particle size of less than about 15 μm by subjecting said as-received metal powder to fluid energy milling; B. batching the conditioned powder with a fluid selected from the group consisting of vehicles, binders, and solvents; C. injection molding the batched powder into a desired green shape; D. debinding the molded green shape to produce a green article; and E. densifying the green article.
Claim 12
Dependent Claim
13 words
The process as defined by claim 7, wherein the milling is jet milling.
Claim 13
Dependent Claim
19 words
The process as defined by claim 7, further comprising the step of screening the milled powder prior to batching.
Claim 14
Dependent Claim
95 words
In a process for injection molding a metal powder slurry including the steps of providing a metal powder, batching the powder with a vehicle, molding the batched powder to form a green article, and sintering the green article, the improvement which comprises the steps of providing a powder consisting essentially of tungsten or molybdenum and having an average particle size of less than about 10 μm, and conditioning the powder in a fluid energy mill prior to batching so that the conditioned powder exhibits a standardized torque measurement of not more than about 2.5 N-m.
Claim 15
Dependent Claim
95 words
In a process for injection molding a metal powder slurry including the steps of providing a metal powder, batching the powder with a vehicle, molding the batched powder to form a green article, and sintering the green article, the improvement which comprises the steps of providing a powder consisting essentially of tungsten or molybdenum and having an average particle size of less than about 10 μm, and conditioning the powder in a fluid energy mill prior to batching so that the conditioned powder exhibits a standardized torque measurement of not more than about 2.5 N-m.
Claim 16
Dependent Claim
57 words
In a process for preparing a powder metal for injection molding by providing the powder and batching the powder with a fluid selected from the group consisting of vehicles, binders, and solvents, the improvement which comprises providing a powder consisting essentially of tungsten or molybdenum and milling the powder in a fluid energy mill prior to batching.
Claim 17
Dependent Claim
57 words
In a process for preparing a powder metal for injection molding by providing the powder and batching the powder with a fluid selected from the group consisting of vehicles, binders, and solvents, the improvement which comprises providing a powder consisting essentially of tungsten or molybdenum and milling the powder in a fluid energy mill prior to batching.
Claim 18
Dependent Claim
49 words
A process for providing a metal powder feedstock, comprising: A. providing an as-received metal powder having a non-spherical particle shape; and B. conditioning the as-received metal powder in a fluid enery mill effective to reduce the average particle size and provide a metal powder feedstock suitable for injection molding.
Claim 19
Dependent Claim
49 words
A process for providing a metal powder feedstock, comprising: A. providing an as-received metal powder having a non-spherical particle shape; and B. conditioning the as-received metal powder in a fluid enery mill effective to reduce the average particle size and provide a metal powder feedstock suitable for injection molding.
Claim 20
Dependent Claim
16 words
The process as defined by claim 13, wherein the metal is tungsten, molybdenum, or mixtures thereof.
Claim 21
Dependent Claim
23 words
The process as defined by claim 14, wherein the conditioned powder has a distribution of particle sizes of 100% less than 20 μm.
Claim 22
Dependent Claim
25 words
The process as defined by claim 14, wherein the conditioned powder has a mean partricle size ranging between about 0.1 μm and about 10 μm.
Claim 23
Dependent Claim
14 words
The process as defined by claim 14, wherein the conditioning step includes jet milling.
Claim 24
Dependent Claim
31 words
The process as defined by claim 13, wherein the conditioned metal powder feedstock is characterized by a mixing torque of not more than about 2.5 N-m under standardized torque measurement conditions.
Claim 25
Dependent Claim
79 words
A process for injection molding a metal powder consisting essentially of molybdenum and/or tungsten, comprising: A. conditioning an as-received metal powder having an average particle size of less than about 10 μm by fluid energy milling effective to decrease the average particle size; B. batching the conditioned powder with a binder; C. injection molding the batched powder into a desired green shape; D. debinding the molded green shape to produce a green article; and E. densifying the green article.
Claim 26
Dependent Claim
79 words
A process for injection molding a metal powder consisting essentially of molybdenum and/or tungsten, comprising: A. conditioning an as-received metal powder having an average particle size of less than about 10 μm by fluid energy milling effective to decrease the average particle size; B. batching the conditioned powder with a binder; C. injection molding the batched powder into a desired green shape; D. debinding the molded green shape to produce a green article; and E. densifying the green article.
Claim 27
Dependent Claim
15 words
The process as defined by claim 19, wherein the fluid energy milling is jet milling.
Claim 28
Dependent Claim
22 words
The process as defined by claim 8, wherein the average particle size of the as-received powder is less than about 10 μm.
Claim 29
Dependent Claim
15 words
The process as defined by claim 8, wherein the fluid energy milling is jet milling.
Claim 30
Dependent Claim
24 words
The process as defined by claim 8, further comprising the step of screening the fluid energy milled powder prior to the step of batching.
References Cited (Backward Citations)
US4369078A
Cited
US4784335A
Cited
US4929418A
Cited
US5063021A
Cited
US5007957A
Cited
US5095048A
Cited
US5091020A
Cited
US5137565A
Cited
US5124119A
Cited
US5126104A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-05-23 | 1997-11-22 | 1998-05-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-05-23 | 2001-11-22 | 2002-05-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-05-23 | 2005-11-22 | 2006-05-24 | $7700.00 | Window Closed / Lapsed |