Method of producing polyurethane injection molded in-line skate wheels
Assignee: S&W Plastics Inc
•
Filing: 1993-05-14
•
Granted: 1994-05-17
•
Expires: 2013-05-14
Abstract
Abstract A method of producing injection molded in-line skate wheels is disclosed. The method includes heating an injection molding unit suitable for injecting molten polyurethane, placing a thermoplastic polyether type polyurethane into the unit and heating the polyurethane until it is molten or at about 380° to about 460° F. A polyurethane hub is placed in a mold whereby the mold and hub are of shapes and sizes suitable for producing in-line skate wheels. The hub-containing mold is heated to about 50° to about 100° F. in order to prevent the molten polyurethane from prematurely hardening. Once the mold is heated, about 46 to about 50 g of polyurethane is injected into the mold at about 75 to about 100 psi. The polyurethane is cooled to about 120° to about 130° F. to allow the polyurethane to harden and the resulting wheel is removed from the mold.
Inventors
- 👤 Stanley W. Gonsior
- 👤 Dennis L. Hvam
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 12:56
CPC Classifications
B; B29; B29C; B29C45/00; B29C45/14; B29C45/1459; A; A63; A63C; A63C17/00; A63C17/22; A63C17/223; B29K; B29K2705/00; B29K2705/02; Y; Y10; Y10S; Y10S152/00; Y10S152/18
Claims Analysis
Total Claims: 37
Claim 1
Independent Claim
87 words
A method of producing injection molded in-line skate wheels, comprising the steps of: placing a polymeric material containing a portion of polyether type polyurethane into an injecting unit suitable for injecting molten polyurethane, heating said unit until said polymeric material is molten, placing a hub into a wheel mold, heating said hub-containing wheel mold to prevent the injected polymeric material from prematurely hardening, injecting said molten polymeric material into said mold under pressure, cooling said wheel mold containing injected molten polymeric material to harden said polymeric material.
Claim 2
Independent Claim
87 words
A method of producing injection molded in-line skate wheels, comprising the steps of: placing a polymeric material containing a portion of polyether type polyurethane into an injecting unit suitable for injecting molten polyurethane, heating said unit until said polymeric material is molten, placing a hub into a wheel mold, heating said hub-containing wheel mold to prevent the injected polymeric material from prematurely hardening, injecting said molten polymeric material into said mold under pressure, cooling said wheel mold containing injected molten polymeric material to harden said polymeric material.
Claim 3
Dependent Claim
22 words
The method of claim 1 wherein said hardened polymeric material is characterized by a Shore Hardness of about 72A to about 82A.
Claim 4
Dependent Claim
23 words
The method of claim 1 wherein said hardened polymeric material is characterized by a Bay Shore rebound of about 58 to about 62.
Claim 5
Dependent Claim
22 words
The method of claim 1 wherein said hardened polymeric material is characterized by a specific gravity of about 1.0 to about 1.2.
Claim 6
Dependent Claim
15 words
The method of claim 1 wherein said hub and said polymeric material are mechanically interlocked.
Claim 7
Dependent Claim
12 words
The method of claim 1 wherein said hub consists essentially of polyurethane.
Claim 8
Dependent Claim
15 words
The method of claim 6 wherein said hub and said polymeric material are chemically bonded.
Claim 9
Dependent Claim
24 words
The method of claim 1 wherein said polymeric material is heated to about 380° to about 410° F. prior to injecting said polymeric material.
Claim 10
Dependent Claim
23 words
The method of claim 1 wherein said hub-containing mold is heated from about 50° to about 100° F. before injecting said polymeric material.
Claim 11
Dependent Claim
34 words
The method of claim 1 wherein said molten polymeric material is injected at an initial boost pressure of from about 650 to about 750 psi and reduced to about 75 to about 100 psi.
Claim 12
Dependent Claim
20 words
The method of claim 1 wherein about 46 to about 50 g molten polymeric material is injected into said mold.
Claim 13
Dependent Claim
20 words
The method of claim 1 wherein said mold has a volume of about 4.7 to about 5.3 in 3 .
Claim 14
Dependent Claim
27 words
The method of claim 1 wherein said polymeric material is injected into said mold at an average of about 1.5 to about 2.5 in 3 per second.
Claim 15
Dependent Claim
30 words
The method of claim 1 further including the step of holding said molten polymeric material-containing mold under about 75 to about 100 psi for about 10 to about 20 seconds.
Claim 16
Dependent Claim
22 words
The method of claim 1 further including a step of injecting more molten polymeric material into said mold after said injecting step.
Claim 17
Dependent Claim
25 words
The method of claim 1 wherein said method including said steps of injecting said polymeric material is complete in about 45 to about 65 seconds.
Claim 18
Dependent Claim
11 words
The in-line skate wheel produced by the method of claim 1.
Claim 19
Dependent Claim
28 words
The method of claim 1 wherein said injected molten polymeric material is cooled to between about 120° and about 130° F. before removing said wheel from said mold.
Claim 20
Dependent Claim
31 words
The method of claim 1 wherein said wheel mold has at least 2 entry ports and said molten polymeric material is injected into said mold through at least 2 entry ports.
Claim 21
Dependent Claim
20 words
The method of claim 19 wherein said molten polymeric material is injected into said wheel mold through 3 entry ports.
Claim 22
Dependent Claim
15 words
The method of claim 1 wherein said polymeric material is a thermoplastic polyether type polyurethane.
Claim 23
Dependent Claim
11 words
The method of claim 21 wherein said polyurethane is Estanee® 58881.
Claim 24
Independent Claim
52 words
A method of producing in-line skate wheels, comprising the steps of: injecting molten thermoplastic polyether type polyurethane having a Bay Shore rebound of about 60 into a mold containing a hub, said hub and said mold having a shape and size suitable for in-line skate wheels, and allowing said polyurethane to harden.
Claim 25
Independent Claim
52 words
A method of producing in-line skate wheels, comprising the steps of: injecting molten thermoplastic polyether type polyurethane having a Bay Shore rebound of about 60 into a mold containing a hub, said hub and said mold having a shape and size suitable for in-line skate wheels, and allowing said polyurethane to harden.
Claim 26
Dependent Claim
20 words
The method of claim 22 wherein said polyurethane is characterized by a Shore Hardness of about 78A to about 82A.
Claim 27
Dependent Claim
23 words
The method of claim 22 wherein said hub is comprised of polyurethane and said hub polyurethane and said injected polyurethane are chemically bonded.
Claim 28
Dependent Claim
19 words
The method of claim 22 further comprising the step of: mechanically interlocking said hub and said injection molded polyurethane.
Claim 29
Dependent Claim
26 words
The method of claim 22 wherein said method comprising the steps of injecting and hardening said polyurethane is complete in about 45 to about 65 seconds.
Claim 30
Dependent Claim
11 words
The in-line skate wheel produced by the method of claim 22.
Claim 31
Dependent Claim
31 words
The method of claim 22 wherein said wheel mold is characterized by at least 2 entry ports and said polyurethane is injected into said mold through at least 2 entry ports.
Claim 32
Dependent Claim
18 words
The method of claim 22 wherein said polyurethane is injected into said wheel mold through 3 entry ports.
Claim 33
Independent Claim
94 words
A method of producing injection molded in-line skate wheels, comprising: providing an injector unit charged with molten polyether type polyurethane, heating said polyurethane to between about 380° and about 430° F., placing a hub into a wheel mold, heating said hub-containing mold to between about 50° and about 110° F., injecting about 46 to about 50 g of said molten polyurethane at about 75 to about 100 psi into said mold, cooling said polyurethane to between about 120° and about 130° F. to harden said polyurethane, and removing said molded polyurethane from said mold.
Claim 34
Independent Claim
94 words
A method of producing injection molded in-line skate wheels, comprising: providing an injector unit charged with molten polyether type polyurethane, heating said polyurethane to between about 380° and about 430° F., placing a hub into a wheel mold, heating said hub-containing mold to between about 50° and about 110° F., injecting about 46 to about 50 g of said molten polyurethane at about 75 to about 100 psi into said mold, cooling said polyurethane to between about 120° and about 130° F. to harden said polyurethane, and removing said molded polyurethane from said mold.
Claim 35
Dependent Claim
31 words
The method of claim 30 wherein said wheel mold is characterized by at least 2 entry ports and said polyurethane is injected into said mold through at least 2 entry ports.
Claim 36
Dependent Claim
18 words
The method of claim 31 wherein said polyurethane is injected into said wheel mold through 3 entry ports.
Claim 37
Dependent Claim
11 words
The method of claim 30 wherein said polyurethane is Estanee® 58881.
References Cited (Backward Citations)
US3689091A
Cited
US4699432A
Cited
US4909523A
Cited
US5028058A
Cited
US5048848A
Cited
US4844491A
Cited
US5133591A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-05-16 | 1997-11-15 | 1998-05-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-05-16 | 2001-11-15 | 2002-05-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-05-16 | 2005-11-15 | 2006-05-17 | $7700.00 | Window Closed / Lapsed |