Higher heat degradable polymer alloys
Assignee: Camelot Technologies Inc
•
Filing: 1991-10-03
•
Granted: 1994-04-05
•
Expires: 2011-10-03
Abstract
Abstract The thermal properties, such as heat distortion temperature of biodegradable polymers, such as polylactic acid, polyglycolides, polybutyric acid and copolymers of butyric and valeric acid, may be increased by blending them with a polymer having Tg from 75° C. to 200° C. and a Hildebrand parameter (σ) of not more than 3 MPA 1/2 different from the biopolymer.
Inventors
- 👤 Speros P. Nemphos
- 👤 Gregory B. Kharas
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 18:39
CPC Classifications
C; C08; C08L; C08L67/00; C08L67/04
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
309 words
A polymer alloy having a Tg of not less than 62° C. comprising: (i) from 50 to 75 weight % of one or more polymers having a molecular weight from 60,000 to 100,000 comprising repeating units of the formula: --OCR.sup.1 R.sup.2 (CR.sup.3 R.sup.4).sub.n CO-- I and --OCH(CH.sub.3)CH.sub.2 CO-- II wherein Formula 1, R 1 , R 2 , R 3 , and R 4 are independently selected from the group consisting of a hydrogen atom and a C 1-4 alkyl radical, and n is 0 or an integer from 1 to 5, provided that when n is 1 and R 2 , R 3 , and R 4 are hydrogen, R 1 can not be a methyl radical; and (ii) from 50 to 25 weight % of one or more polymers having a Tg from 75° C. to 175° C. and a difference in the range of Hildebrand parameters (σ) from those of for the polymers of component (i) of not more than 2 MPA 1/2 selected from the group of polymers consisting of: (a) polycarbonates; (b) polymers comprising: (i) from 40 to 95 weight % of one or more C 8-12 vinyl aromatic monomers which are unsubstituted or substituted by a C 1-4 alkyl radical; (ii) from 5 to 40 weight % of an anhydride of a C 4-6 ethylenically unsaturated dicarboxylic acid; and (iii) from 0 to 50 weight % of one or more C 1-4 alkyl or hydroxy alkyl acrylates or methacrylates; and (c) acrylate polymers comprising: (i) from 100 to 50 weight % of one or more C 1-6 alkyl or hydroxy alkyl acrylates or methacrylates; and (ii) from 0 to 50 weight % of one or more C 8-12 vinyl aromatic monomers which are unsubstituted or substituted by a C 1-4 alkyl radical, which acrylate polymers have been imidized to from 10% to 95%.
Claim 2
Dependent Claim
309 words
A polymer alloy having a Tg of not less than 62° C. comprising: (i) from 50 to 75 weight % of one or more polymers having a molecular weight from 60,000 to 100,000 comprising repeating units of the formula: --OCR.sup.1 R.sup.2 (CR.sup.3 R.sup.4).sub.n CO-- I and --OCH(CH.sub.3)CH.sub.2 CO-- II wherein Formula 1, R 1 , R 2 , R 3 , and R 4 are independently selected from the group consisting of a hydrogen atom and a C 1-4 alkyl radical, and n is 0 or an integer from 1 to 5, provided that when n is 1 and R 2 , R 3 , and R 4 are hydrogen, R 1 can not be a methyl radical; and (ii) from 50 to 25 weight % of one or more polymers having a Tg from 75° C. to 175° C. and a difference in the range of Hildebrand parameters (σ) from those of for the polymers of component (i) of not more than 2 MPA 1/2 selected from the group of polymers consisting of: (a) polycarbonates; (b) polymers comprising: (i) from 40 to 95 weight % of one or more C 8-12 vinyl aromatic monomers which are unsubstituted or substituted by a C 1-4 alkyl radical; (ii) from 5 to 40 weight % of an anhydride of a C 4-6 ethylenically unsaturated dicarboxylic acid; and (iii) from 0 to 50 weight % of one or more C 1-4 alkyl or hydroxy alkyl acrylates or methacrylates; and (c) acrylate polymers comprising: (i) from 100 to 50 weight % of one or more C 1-6 alkyl or hydroxy alkyl acrylates or methacrylates; and (ii) from 0 to 50 weight % of one or more C 8-12 vinyl aromatic monomers which are unsubstituted or substituted by a C 1-4 alkyl radical, which acrylate polymers have been imidized to from 10% to 95%.
Claim 3
Dependent Claim
34 words
The polymer alloy according to claim 1, wherein component (i) is present in an amount from 50 to 70 weight % and component (ii) is present in amount from 50 to 30 weight %.
Claim 4
Dependent Claim
95 words
The polymer alloy according to claim 2, wherein said polycarbonate is based on one or more poly phenols selected from the group consisting of hydroquinone, resorcinol and polyphenols of the formula ##STR5## wherein R 1 , R 2 , R 3 , and R 4 are independently selected from the group consisting of a hydrogen atom, a chlorine atom, a bromine atom, and a C 1-4 alkyl radical; and X is a bond or divalent radical selected from the group consisting of C 1-10 alkylene radicals, C 2-8 alkenylene radicals, and C 6-8 cycloalkylene radicals.
Claim 5
Dependent Claim
30 words
The polymer alloy according to claim 3 wherein said polycarbonate is based on a diphenol selected from the group consisting of 4,4'dihydroxydiphenyl; 2,2-bis-(4-hydroxyphenyl) propane; 2,4-bis-(4-hydroxyphenyl)-2-methylbutane; 1,1-bis(4-hydroxyphenyl)-cyclohexane; β,β-bis-(4-hydroxyphenyl)-p-diisopropylbenzene; 2,2-bis-(3-chloro-4-hydroxyphenyl)propane; 2,2-bis-(3,5-dichloro-4-hydroxyphenyl) propane.
Claim 6
Dependent Claim
61 words
The polymer alloy according to claim 2, wherein in component (ii) (b) said vinyl aromatic monomer is selected from the group consisting of styrene, α-methyl styrene, and t-butyl styrene; said anhydride is maleic anhydride; and said C 1-4 alkyl or hydroxy alkyl acrylate or methacrylate is selected from the group consisting of methyl acrylate, ethyl acrylate, methyl methacrylate, and ethyl acrylate.
Claim 7
Dependent Claim
46 words
The polymer alloy according to claim 2, wherein in component (ii) (c) said C 1-4 alkyl acrylate or methacrylate is present in an amount from 100 to 70 weight % and said vinyl aromatic monomer is present in an amount from 0 to 30 weight %.
Claim 8
Dependent Claim
52 words
The polymer alloy according to claim 6, wherein said C 1-4 alkyl or hydroxy alkyl acrylate or methacrylate is selected from the group consisting of methyl acrylate, ethyl acrylate, methyl methacrylate and methyl methacrylate; and said vinyl aromatic monomer is selected from the group consisting of styrene, c-methyl styrene and t-butyl styrene.
Claim 9
Dependent Claim
39 words
The polymer alloy according to claim 2 wherein component (i) is a homopolymer of Formula I wherein n is 0 and one of R 1 or R 2 is a methyl radical and the other is a hydrogen atom.
Claim 10
Dependent Claim
42 words
The polymer alloy according to claim 2, wherein component (i) is a copolymer comprising from 0.1 to 40 mole percent of units of Formula I wherein n is an integer and from 99.9 to 60 mole percent of units of Formula II.
Claim 11
Dependent Claim
61 words
The polymer alloy according to claim 9, wherein component (i) is a copolymer comprising from 5 to 30 mole percent of units of Formula I wherein n is 1 and R 1 is an ethyl radical and R 2 , R 3 , and R 4 are hydrogen atoms and from 95 to 70 mole percent of units of Formula II.
References Cited (Backward Citations)
US3336267A
Cited
US4246374A
Cited
US4477654A
Cited
US4569969A
Cited
US4631311A
Cited
US5061281A
Cited
US5066772A
Cited
WO1990001521A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-04-04 | 1997-10-04 | 1998-04-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-04-04 | 2001-10-04 | 2002-04-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-04-04 | 2005-10-04 | 2006-04-05 | $7700.00 | Window Closed / Lapsed |