Assignee: Sumitomo Electric Industries Ltd
•
Filing: 1992-09-25
•
Granted: 1994-04-05
•
Expires: 2012-09-25
Abstract
Abstract In order to enable formation of a smooth and dense oxide superconducting film with no clear appearance of grain boundaries in a fine structure even at a high film forming rate, a laser ablation method is employed to apply a laser beam 2 to a target 1 containing components of an oxide superconductive material and deposit particles, which are thus scattered from the target 1, on a substrate 3, while gaseous oxygen is supplied from a gaseous oxygen inlet 7 toward laser plume 6, which is generated by the application of the laser beam 2, and to a portion of the target irradiated with said laser.
Inventors
- 👤 Noriyuki Yoshida
- 👤 Satoshi Takano
- 👤 Shigeru Okuda
- 👤 Noriki Hayashi
- 👤 Tsukushi Hara
- 👤 Kiyoshi Okaniwa
- 👤 Takahiko Yamamoto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 17:53
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/06; C23C14/08; C23C14/087; C23C14/0021; C23C14/22; C23C14/24; C23C14/28; H; H10; H10N; H10N60/00; H10N60/01; H10N60/0268; H10N60/0296; H10N60/0521; Y; Y10; Y10S; Y10S505/00; Y10S505/725; Y10S505/73; Y10S505/732; Y10S505/786
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
114 words
A method of preparing an oxide superconducting film, comprising the steps of: preparing a target containing components of an oxide superconductive material; arranging a substrate to be opposite to said target; applying a laser beam to said target, thereby generating a laser plume and scattering particles from said target; supplying gaseous oxygen toward said laser plume and to a portion of the target irradiated with said laser beam; and depositing said scattered particles on said substrate, thereby forming said oxide superconducting film on said substrate wherein the critical current density of said superconducting film is at least about 10 5 A/cm 2 at 77.3K with a film forming rate of at least 2,000 Å/min.
Claim 2
Independent Claim
114 words
A method of preparing an oxide superconducting film, comprising the steps of: preparing a target containing components of an oxide superconductive material; arranging a substrate to be opposite to said target; applying a laser beam to said target, thereby generating a laser plume and scattering particles from said target; supplying gaseous oxygen toward said laser plume and to a portion of the target irradiated with said laser beam; and depositing said scattered particles on said substrate, thereby forming said oxide superconducting film on said substrate wherein the critical current density of said superconducting film is at least about 10 5 A/cm 2 at 77.3K with a film forming rate of at least 2,000 Å/min.
Claim 3
Dependent Claim
26 words
A method of preparing an oxide superconducting film in accordance with claim 1, further comprising a step of enclosing said laser plume with a tubular member.
Claim 4
Dependent Claim
34 words
A method of preparing an oxide superconducting film in accordance with claim 1, further comprising a step of providing an electrode between said target and said substrate, thereby generating discharge plasma around said electrode.
Claim 5
Dependent Claim
26 words
A method of preparing an oxide superconducting film in accordance with claim 3, wherein said substrate is set at a temperature of less than 600° C.
References Cited (Backward Citations)
US5015492A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-04-04 | 1997-10-04 | 1998-04-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-04-04 | 2001-10-04 | 2002-04-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-04-04 | 2005-10-04 | 2006-04-05 | $7700.00 | Window Closed / Lapsed |