Method for producing a scintillator ceramic
Assignee: Siemens AG
•
Filing: 1993-07-26
•
Granted: 1994-03-22
•
Expires: 2013-07-26
Abstract
Abstract For manufacturing a scintillator ceramic of a rare earth oxisulfide, a pigment powder is compressed by single-axis hot-pressing to form a ceramic member having at least 99.9% of the theoretic density, the pigment powder having the general formula (M 1 xLn x ) 2 O 2 S, whereby M denotes at least one element from the group Y, La and Gd, Ln represents at least one element from the group Eu, Ce, Pr, Tb, Yb, Dy, Sm and Ho, and whereby 1×10 -6 ≦x≦2×10 -1 , and the powder having a specific surface according to BET of at least 10 m -2 /g.
Inventors
- 👤 Juergen Leppert
- 👤 Wolfgang Rossner
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 07:38
CPC Classifications
G; G21; G21K; G21K4/00; C; C04; C04B; C04B35/00; C04B35/50; C04B35/515; C04B35/547; C09; C09K; C09K11/00; C09K11/08; C09K11/77; C09K11/7766; C09K11/7767; C09K11/7769; C09K11/7771; C09K11/7783; C09K11/7784; C09K11/7787; C09K11/7789; G21K2004/06
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
120 words
A method for producing a high-density scintillation ceramic of a rare earth oxisulfide, comprising the steps of: providing a pigment powder having the general formula (M.sub.1-x Ln.sub.x).sub.2 O.sub.2 S wherein M is at least one element selected from the group consisting of Y, La and Gd, Ln is at least one element selected from the group consisting of Eu, Ce, Pr, Tb, Yb, Dy, Sm and Ho and 1×10 -6 ≦×≦2×10 -1 , said powder having a specific surface of at least 10 m 2 /g determined with the gas absorption method according to BET; and compressing said pigment powder by single-axis hot-pressing to form a translucent ceramic member having a density of at least 99.9% of the theoretical density.
Claim 2
Independent Claim
120 words
A method for producing a high-density scintillation ceramic of a rare earth oxisulfide, comprising the steps of: providing a pigment powder having the general formula (M.sub.1-x Ln.sub.x).sub.2 O.sub.2 S wherein M is at least one element selected from the group consisting of Y, La and Gd, Ln is at least one element selected from the group consisting of Eu, Ce, Pr, Tb, Yb, Dy, Sm and Ho and 1×10 -6 ≦×≦2×10 -1 , said powder having a specific surface of at least 10 m 2 /g determined with the gas absorption method according to BET; and compressing said pigment powder by single-axis hot-pressing to form a translucent ceramic member having a density of at least 99.9% of the theoretical density.
Claim 3
Dependent Claim
46 words
A method as claimed in claim 1 wherein the step of providing a pigment powder is further defined by providing a pigment powder having a specific surface in the range from 20 through 30 m 2 /g determined with the gas absorption method according to BET.
Claim 4
Dependent Claim
79 words
A method as claimed in claim 1 comprising the additional step of, before compressing said pigment powder, of pre-pressing said pigment powder dry and cold at a pressure of 0.1 through 10 kN cm -2 , and wherein the step of compressing said pigment powder is further defined by compressing said pigment powder at a temperature in the range from 1000° through 1500° C. and at a pressure in the range from 0.1 through 20 kN cm -2 .
Claim 5
Dependent Claim
38 words
A method as claimed in claim 3 wherein the step of pre-pressing said pigment powder is further defined by pre-pressing said pigment powder at a pressure in the range of from 1 through 3 kN cm -2 .
Claim 6
Dependent Claim
34 words
A method as claimed in claim 3 wherein the step of compressing said pigment powder is further defined by compressing said pigment powder at a temperature in the range from 1100° through 1300° C.
Claim 7
Dependent Claim
37 words
A method as claimed in claim 3 wherein the step of compressing said pigment powder is further defined by compressing said pigment powder at a pressure in the range from 2 through 6 kN cm -2 .
Claim 8
Dependent Claim
60 words
A method as claimed in claim 3 comprising the additional step, after said pre-pressing said pigment powder and before compressing said pigment powder, of heating said pigment powder to a temperature in the range from 1000° through 1500° C. unpressurized and thereby sintering said pigment powder to a density in the range from 75% through 90% of said theoretical density.
Claim 9
Dependent Claim
41 words
A method as claimed in claim 1 wherein the step of providing said pigment powder is further defined by providing a pigment powder produced by chemical precipitation of a rare earth sulfite from acid aqueous solution followed by a thermal reduction.
Claim 10
Dependent Claim
27 words
A method as claimed in claim 1 wherein the step of compressing said pigment powder is further defined by compressing said pigment powder in an extrusion die.
Claim 11
Dependent Claim
49 words
A method as claimed in claim 9 wherein the step of compressing said pigment powder in an extrusion die is further defined by compressing said pigment powder in an extrusion die comprising materials selected from the group consisting of aluminum oxide, tantalum, tungsten, molybdenum, silicon carbide and silicon nitride.
Claim 12
Dependent Claim
33 words
A method as claimed in claim 1 comprising the additional step of adding at least one of a compression additive or a sintering aid to said pigment powder before compressing said pigment powder.
Claim 13
Dependent Claim
31 words
A method as claimed in claim 1 wherein the step of compressing said pigment powder is further defined by hot-pressing said pigment powder under a residual gas pressure below 10 pa.
Claim 14
Dependent Claim
41 words
A method as claimed in claim 1 wherein the step of compressing said pigment powder is further defined by compressing said pigment powder in a gas atmosphere comprising a gas selected from the group consisting of nitrogen, argon, helium and hydrogen.
Claim 15
Dependent Claim
24 words
A method as claimed in claim 1 comprising the additional step of forming said ceramic member for use in an x-ray computer tomography apparatus.
References Cited (Backward Citations)
US3502590A
Cited
US3878280A
Cited
GB1375052A
Cited
US4242221A
Cited
DE3629180A1
Cited
US4733088A
Cited
DE3702357A1
Cited
US4863882A
Cited
US4888121A
Cited
US5075267A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-03-21 | 1997-09-20 | 1998-03-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-03-21 | 2001-09-20 | 2002-03-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-03-21 | 2005-09-20 | 2006-03-22 | $7700.00 | Window Closed / Lapsed |