Method for the production of a radiographic screen
Assignee: Agfa Gevaert NV
•
Filing: 1992-12-01
•
Granted: 1994-03-22
•
Expires: 2012-12-01
Abstract
Abstract A method for the production of a radiographic screen comprising the following steps: 1) dispersing phosphor particles in an organic liquid in the presence of a charge controlling agent that charges said phosphor particles with a positive or negative net charge, 2) arranging said dispersion between a pair of electrodes, wherein one of said electrodes is or carries a conductive support of said radiographic screen, 3) applying and maintaining between said electrodes a sufficiently high direct current voltage to deposit charged phosphor particles onto said conductive support, and 4) separating said support carrying electrophoretically deposited phosphor particles from said organic liquid, wherein the dispersing of said phosphor particles proceeds by means of an organic surface active compound acting as dispersing agent for said phosphor particles, and said phosphor particles are electrostatically charged through adsorption thereon of ionic components of said organic surface active compound and/or through adsorption of cations or anions stemming from an ionic inorganic compound incorporated in said liquid.
Inventors
- 👤 Nikolaas De Jaeger
- 👤 Guy Damen
- 👤 Gerhard Winter
- 👤 Jan Van Havenbergh
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 08:42
CPC Classifications
G; G21; G21K; G21K4/00; C; C09; C09K; C09K11/00; C09K11/02; C09K11/025; C25; C25D; C25D13/00; H; H01; H01J; H01J9/00; H01J9/20; H01J9/22; H01J9/221; H01J9/225; G21K2004/06
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
158 words
A method for producing a radiographic screen comprising the following steps: 1) dispersing phosphor particles in an organic liquid in the presence of a charge controlling agent that charges said phosphor particles with a positive or negative net charge, wherein the dispersing of said phosphor particles is carried out in a polar anhydrous organic liquid by means of an organic surface active compound being a member selected from the group consisting of an alkyl aryl polyether sulphate, an organic phosphorate, a phosphate ester and a phospholipid, and said phosphor particles are thereby electrostatically charged, 2) arranging said dispersion between a pair of electrodes, wherein one of said electrodes is or carries a conductive support of said radiographic screen, 3) applying and maintaining between said electrodes a sufficiently high direct current voltage to deposit charged phosphor particles forming a phosphor layer onto said conductive support, and 4) separating said support carrying electrophoretically deposited phosphor particles from said organic liquid.
Claim 2
Independent Claim
158 words
A method for producing a radiographic screen comprising the following steps: 1) dispersing phosphor particles in an organic liquid in the presence of a charge controlling agent that charges said phosphor particles with a positive or negative net charge, wherein the dispersing of said phosphor particles is carried out in a polar anhydrous organic liquid by means of an organic surface active compound being a member selected from the group consisting of an alkyl aryl polyether sulphate, an organic phosphorate, a phosphate ester and a phospholipid, and said phosphor particles are thereby electrostatically charged, 2) arranging said dispersion between a pair of electrodes, wherein one of said electrodes is or carries a conductive support of said radiographic screen, 3) applying and maintaining between said electrodes a sufficiently high direct current voltage to deposit charged phosphor particles forming a phosphor layer onto said conductive support, and 4) separating said support carrying electrophoretically deposited phosphor particles from said organic liquid.
Claim 3
Dependent Claim
28 words
Method according to claim 1, wherein said phosphor particles are electrophoretically deposited in the presence of an organic resin binder or an organic resin binder formed in situ.
Claim 4
Dependent Claim
19 words
Method according to claim 1, wherein said phosphor particles are electrophoretically deposited in the presence of a drying oil.
Claim 5
Dependent Claim
18 words
Method according to claim 3, wherein said phosphor particles are electrophoretically deposited in the presence of linseed oil.
Claim 6
Dependent Claim
19 words
Method according to claim 1, wherein the dispersed phosphor particles have a zeta-potential ranging from 15 to 150 mV.
Claim 7
Dependent Claim
34 words
Method according to claim 1, wherein said organic liquid is a polar anhydrous organic liquid having a volume resistivity of at least 10 5 Ohm.cm, and dielectric constant lower than 40 at 20° C.
Claim 8
Dependent Claim
36 words
Method according to claim 1, wherein said organic liquid is at least one member selected from the group consisting of 1-propanol, 2-propanol, 1-butanol, 2-methyl-1-propanol, 2-butanol, dimethyl ketone, methyl ethyl ketone, lower alkyl esters, and mixtures thereof.
Claim 9
Dependent Claim
30 words
Method according to claim 1, wherein said surface active compound provides to said phosphor particles a positive net charge whereby said particles deposit on said support which is a cathode.
Claim 10
Dependent Claim
32 words
Method according to claim 1, wherein said surface active compound is present in said organic liquid in a weight percentage of 0.1 to 5 based on the weight of the phosphor particles.
Claim 11
Dependent Claim
51 words
Method according to claim 1, wherein said phosphate ester is an organic phosphoric acid mono- and diester represented by the following structural formulae: ##STR2## wherein alkyl is a C15 to C20 alkyl group, n is from 15 to 20, and n 1 and n 2 together are from 15 to 20.
Claim 12
Dependent Claim
48 words
Method according to claim 1, wherein the electrophoretically deposited phosphor particles are fixed together and adhered to said conductive support by a natural, semi-synthetic or synthetic polymer originally dissolved or dispersed in said organic liquid and left in contact with said phosphor particles after evaporation of said liquid.
Claim 13
Dependent Claim
26 words
Method according to claim 1, wherein after the electrophoretic deposition a pressure is applied to the phosphor layer to increase packing density of the phosphor particles.
Claim 14
Dependent Claim
17 words
Method according to claim 1, wherein said phosphor layer is covered or coated with a protective topcoat.
References Cited (Backward Citations)
US2851408A
Cited
SU457120A1
Cited
US3714011A
Cited
US4482447A
Cited
US4910407A
Cited
JPH03147228A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-03-21 | 1997-09-20 | 1998-03-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-03-21 | 2001-09-20 | 2002-03-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-03-21 | 2005-09-20 | 2006-03-22 | $7700.00 | Window Closed / Lapsed |