Abstract A heat conductive aluminum nitride sintered body contains 100 parts by weight of aluminum nitride, at least 0.005 parts by weight and not more than 0.5 parts by weight of carbon, at least 0.01 parts by weight and not more than 15 parts by weight of a rare earth aluminum oxide in terms of the simple substance of a rare earth element, and at least 0.01 parts by weight and not more than 15 parts by weight of at least one element selected from a group of compounds containing elements belonging to the groups IVB, VB and VIB of the periodic table in terms of the simple substance of the element. Heat conductivity of the aluminum nitride sintered body is at least 100 W/m*K and not more than 270 W/m*K at the ordinary temperature. According to a method of preparing such an aluminum nitride sintered body, at least 0.01 parts by weight and not more than 5 parts by weight of carbon, at least 0.01 parts by weight and not more than 15 parts by weight of an oxide of a rare earth element, and at least 0.01 parts by weight and not more than 15 parts by weight of an oxide, a carbide or a nitride of an element belonging to the group IVB, VB or VIB of the periodic table are added to 100 parts by weight of aluminum nitride. A compact of this mixture is fired in a nonoxidizing atmosphere under a temperature of at least 1500 degrees C. and not more than 2100 degrees C.
A method of preparing a heat conductive colored aluminum nitride sintered body, comprising the steps of: mixing at least 0.01 parts by weight and not more than 15 parts by weight of an oxide of a rare earth element in terms of the simple substance of said rare earth element, and at least 0.01 parts by weight and not more than 15 parts by weight of at least one element selected from a group consisting of oxides, carbides and nitrides of elements belonging to the groups IVB, VB and VIB of the periodic table in terms of the simple substance of said element and 100 parts by weight of aluminum nitride, thereby obtaining a mixture; shaping said mixture into a compact; and firing said compact in a non-oxidizing atmosphere containing at least 10 volume percent and not more than 100 volume percent of hydrocarbon gas selected from the group consisting of methane gas, ethylene gas, acetylene gas, propane gas and butane gas under a temperature of at least 1500° C. and not more than 2100° C., said hydrocarbon gas eliminating oxygen by chemical reaction, whereby said aluminum nitride sintered body has a uniformly distributed dark color within the range of gray to black and simultaneously a thermal conductivity within the range of 100 W/m·K to 270 W/m·K.
Claim 2
Independent Claim
217 words
A method of preparing a heat conductive colored aluminum nitride sintered body, comprising the steps of: mixing at least 0.01 parts by weight and not more than 15 parts by weight of an oxide of a rare earth element in terms of the simple substance of said rare earth element, and at least 0.01 parts by weight and not more than 15 parts by weight of at least one element selected from a group consisting of oxides, carbides and nitrides of elements belonging to the groups IVB, VB and VIB of the periodic table in terms of the simple substance of said element and 100 parts by weight of aluminum nitride, thereby obtaining a mixture; shaping said mixture into a compact; and firing said compact in a non-oxidizing atmosphere containing at least 10 volume percent and not more than 100 volume percent of hydrocarbon gas selected from the group consisting of methane gas, ethylene gas, acetylene gas, propane gas and butane gas under a temperature of at least 1500° C. and not more than 2100° C., said hydrocarbon gas eliminating oxygen by chemical reaction, whereby said aluminum nitride sintered body has a uniformly distributed dark color within the range of gray to black and simultaneously a thermal conductivity within the range of 100 W/m·K to 270 W/m·K.