US5294094A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method and apparatus for heat treating metal castings
Assignee: Consolidated Engineering Co Inc
•
Filing: 1992-11-20
•
Granted: 1994-03-15
•
Expires: 2012-11-20
Abstract
Abstract An improved method and apparatus for heat treating metal castings with sand cores provides for removal of the sand core and recovery of the sand core material for reuse. The method and apparatus eliminate the need for removing the sand core from the casting prior to heat treatment and thus eliminate the labor, expense, and possible damage to the casting incidental to conventional core removal techniques such as chiseling and shaking. The method involves heating the casting with sand core therein to a temperature sufficient to burn off the binder component of the sand core. The sand comprising the sand core is then blown out of the casting by directing a flow of air over the workpiece. The sand thus dislodged is then collected for reuse. According to the disclosed apparatus, the castings are heated in a furnace having fans for directing a flow of aid over the workpieces. The sand dislodged from the castings falls into a trough in the lower portion of the furnace, where it is collected and conveyed to a central collection bin for reuse. In another aspect of the disclosed apparatus, the castings are subsequently immersed in a quench tank. The quench tank includes agitation means for agitating water over the castings to dislodge remaining sand. The sand falls to the bottom of the tank, where the sand and a portion of the water are removed from the tank. A major portion of the water is then removed from the sand so that the sand can be reused.
Inventors
- 👤 Paul M. Crafton
- 👤 Scott P. Crafton
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 16:08
CPC Classifications
B; B22; B22D; B22D29/00; B22D29/001; B22D29/003; B22D31/00; B22D31/002
Claims Analysis
Total Claims: 33
Claim 1
Independent Claim
165 words
A method for heat treating a casting having a sand core, said sand core comprising sand particles bound together by a binder material, and said sand core defining a cavity within said casting, said method comprising the steps of: introducing said metal casting with said sand core into a furnace heated to a temperature in excess of the combustion temperature of said binder material; providing an oxygen-rich atmosphere within said heated furnace which comprises in excess of 10% oxygen; containing said metal casting with said sand core within said heated furnace in said oxygen-rich atmosphere to permit said binder material to combust, whereby said sand particles comprising said sand core are loosened from said sand core; removing said loosened sand particles from said cavity; capturing clumps of sand core material which become dislodged from said casting prior to said binder material being combusted therefrom; and retaining said dislodged clumps of sand core material within said furnace to permit said binder material to be combusted therefrom.
Claim 2
Independent Claim
165 words
A method for heat treating a casting having a sand core, said sand core comprising sand particles bound together by a binder material, and said sand core defining a cavity within said casting, said method comprising the steps of: introducing said metal casting with said sand core into a furnace heated to a temperature in excess of the combustion temperature of said binder material; providing an oxygen-rich atmosphere within said heated furnace which comprises in excess of 10% oxygen; containing said metal casting with said sand core within said heated furnace in said oxygen-rich atmosphere to permit said binder material to combust, whereby said sand particles comprising said sand core are loosened from said sand core; removing said loosened sand particles from said cavity; capturing clumps of sand core material which become dislodged from said casting prior to said binder material being combusted therefrom; and retaining said dislodged clumps of sand core material within said furnace to permit said binder material to be combusted therefrom.
Claim 3
Dependent Claim
36 words
The method of claim 1, wherein said step of removing said loosened sand particles from said cavity comprises the step of continuously removing said loosened sand particles from said cavity as said binder material is combusted.
Claim 4
Dependent Claim
50 words
The method of claim 1, wherein said step of removing said loosened sand particles from said cavity comprises the step of directing a flow of air against said casting as said casting is contained within said furnace such that said flow of air dislodges loosened sand particles from said cavity.
Claim 5
Dependent Claim
48 words
The method of claim 3, wherein said step of directing a flow of air against said casting as said casting is contained within said furnace comprises the step of directing a flow of air against said casting at an airflow velocity in excess of 3,000 feet per minute.
Claim 6
Dependent Claim
50 words
The method of claim 1, wherein said step of removing said loosened sand particles from said cavity comprises the step of angling said metal casting within said furnace to permit at least a portion of said loosened sand particles to fall out of said casting under the force of gravity.
Claim 7
Dependent Claim
38 words
The method of claim 1, comprising the further step of angling said metal casting within said furnace such that at least a portion of said loosened said particles will fall out of said casting under force of gravity.
Claim 8
Dependent Claim
28 words
The method of claim 1, comprising the further step of collecting said portion of said sand particles dislodged from said casting and conveying it out of said furnace.
Claim 9
Dependent Claim
46 words
The method of claim 7, wherein said step of collecting said portion of said sand particles dislodged from said casting comprises the step of continuously collecting said portion of said sand particles as it is dislodged from said casting and conveying it out of said furnace.
Claim 10
Dependent Claim
59 words
The method of claim 1, wherein said step of introducing said metal casting with said sand core into a furnace heated to a temperature in excess of the combustion temperature of said binder material comprises the step of introducing said metal casting with said sand core into a furnace heated to a temperature in excess of approximately 850° F.
Claim 11
Dependent Claim
58 words
The method of claim 9, wherein said step of introducing said metal casting with said sand core into a furnace heated to a temperature in excess of approximately 850° F. comprises the step of introducing said metal casting with said sand core into a furnace heated to a temperature of between approximately 850° F. and approximately 1000° F.
Claim 12
Dependent Claim
56 words
The method of claim 10, wherein said step of introducing said metal casting with said sand core into a furnace heated to a temperature of between approximately 850° F. and approximately 1000° F. comprises the step of introducing said metal casting with said sand core into a furnace heated to a temperature of approximately 980° F.
Claim 13
Dependent Claim
51 words
The method of claim 1, wherein said steps of capturing and retaining said dislodged clumps of sand core material comprises the step of providing a screen disposed beneath said casting, said screen having openings therein which are not sufficiently large to pass clumps of sand core material of a predetermined size.
Claim 14
Dependent Claim
37 words
The method of claim 12, further comprising the step of causing clumps of sand material smaller than said predetermined size which pass through said screen to impact upon a surface so as to break up said clumps.
Claim 15
Dependent Claim
45 words
The method of claim 13, wherein said step of causing said clumps of material to impact upon a surface comprises the step of causing said clumps of material to impact upon a sloped surface and to tumble down said surface to break up said clumps.
Claim 16
Independent Claim
123 words
A method for heat treating a casting having a sand core which comprises sand particles bound together by a binder material, and wherein the sand core defines a cavity within the casting, said method comprising the following steps: introducing a casting, with a sand core substantially intact within a cavity of the casting, into a furnace heated to a temperature in excess of the combustion temperature of the binder material; providing an oxygenated atmosphere within the furnace; and containing the casting, with the sand core, within the oxygenated atmosphere in the furnace to permit the binder material to combust, whereby portions of the sand core are loosened from the sand core and fall from the cavity while the casting is in the furnace.
Claim 17
Independent Claim
123 words
A method for heat treating a casting having a sand core which comprises sand particles bound together by a binder material, and wherein the sand core defines a cavity within the casting, said method comprising the following steps: introducing a casting, with a sand core substantially intact within a cavity of the casting, into a furnace heated to a temperature in excess of the combustion temperature of the binder material; providing an oxygenated atmosphere within the furnace; and containing the casting, with the sand core, within the oxygenated atmosphere in the furnace to permit the binder material to combust, whereby portions of the sand core are loosened from the sand core and fall from the cavity while the casting is in the furnace.
Claim 18
Dependent Claim
54 words
The method of claim 15, further comprising the steps of: suspending, within the oxygenated atmosphere in the furnace, portions of the sand core which become dislodged from the casting prior to the binder being combusted from those portions of the sand core; and releasing previously suspended sand, once the binder is substantially combusted therefrom.
Claim 19
Dependent Claim
90 words
The method of claim 15, further comprising the steps of: providing a screen disposed beneath the casting and within the oxygenated atmosphere, wherein the screen has openings therein which are not sufficiently large to pass portions of the sand core of a predetermined size, and wherein the openings are sufficiently large to pass portions of the sand core which are less than the predetermined size; and suspending on the screen portions of the sand core which are larger than the predetermined size, to allow further combustion of binder material therefrom.
Claim 20
Dependent Claim
37 words
The method of claim 17, further comprising, at least, the step of causing portions of sand core which pass through the screen to impact upon a surface so as to break up the portions of sand core.
Claim 21
Dependent Claim
52 words
The method of claim 18, wherein the step of causing the portions of sand core to impact upon a surface comprises, at least, the step of causing the portions of sand core to impact upon a sloped surface and to tumble down the surface to break up the portions of sand core.
Claim 22
Dependent Claim
30 words
The method of claim 15, further comprising the step of directing airflow against the casting, while the casting is in the furnace, so as to dislodge sand from the casting.
Claim 23
Dependent Claim
45 words
The method of claim 20, wherein the step of directing airflow against the casting, while the casting is in the furnace, comprises, at least, the step of directing, from a plurality of directions, airflow against the casting so as to dislodge sand from the casting.
Claim 24
Dependent Claim
40 words
The method of claim 20, wherein the step of directing airflow against the casting, while the casting is in the furnace, comprises, at least, directing airflow against the casting at an airflow velocity in excess of 3,000 feet per minute.
Claim 25
Dependent Claim
47 words
The method of claim 15, wherein the step of providing an oxygenated atmosphere within the furnace comprises, at least, the step of controlling the oxygen content in the furnace so that a higher percent of oxygen is maintained where a higher percentage of the binder material combusts.
Claim 26
Dependent Claim
81 words
The method of claim 23, wherein the step of providing an oxygenated atmosphere within the furnace comprises, at least, conveying the casting through a plurality of zones within the furnace, controlling the oxygen content within the furnace to provide 13-17% oxygen in those zones in which a major portion of binder combustion takes place, and controlling the oxygen content within the furnace to provide 10-13% oxygen in the zones in which a major portion of binder combustion does not take place.
Claim 27
Dependent Claim
40 words
The method of claim 15, further comprising the step of angling the casting within the furnace such that at least a portion of the loosened portions of sand core will fall out of the casting under the force of gravity.
Claim 28
Dependent Claim
26 words
The method of claim 15, further comprising the step of collecting sand that has fallen from the cavity and conveying collected sand out of the furnace.
Claim 29
Dependent Claim
38 words
The method of claim 26, wherein the step of collecting sand and conveying collected sand comprises, at least, the step of continuously collecting sand that has fallen from the cavity and conveying collected sand out of the furnace.
Claim 30
Dependent Claim
61 words
The method of claim 15, wherein the step of introducing the casting, with the sand core substantially intact, into a furnace heated to a temperature in excess of the combustion temperature of the binder material comprises, at least, the step of introducing the casting, with the sand core substantially intact, into a furnace heated to a temperature of approximately 980° F.
Claim 31
Independent Claim
121 words
A method for manufacturing a casting comprising the following steps: producing a casting having a sand core which comprises sand particles bound together by a combustible binder material, wherein the sand core defines a cavity within the casting; prior to any substantial destruction to the sand core, introducing the casting into a furnace, wherein the furnace is heated to a temperature in excess of the combustion temperature of the binder material; providing an oxygenated atmosphere within the furnace; and containing the casting with the sand core within the furnace to permit the binder material to combust, whereby sand particles comprising the sand core are loosened from the sand core and fall from the cavity while the casting is in the furnace.
Claim 32
Independent Claim
121 words
A method for manufacturing a casting comprising the following steps: producing a casting having a sand core which comprises sand particles bound together by a combustible binder material, wherein the sand core defines a cavity within the casting; prior to any substantial destruction to the sand core, introducing the casting into a furnace, wherein the furnace is heated to a temperature in excess of the combustion temperature of the binder material; providing an oxygenated atmosphere within the furnace; and containing the casting with the sand core within the furnace to permit the binder material to combust, whereby sand particles comprising the sand core are loosened from the sand core and fall from the cavity while the casting is in the furnace.
Claim 33
Dependent Claim
39 words
The method of claim 29, wherein the step of introducing the casting into the furnace is performed prior to any mechanical shaking, intended to remove meaningful portions of the sand core, whereby mechanical shaking for core removal is avoided.
References Cited (Backward Citations)
SU234810A1
Cited
DE2307773A1
Cited
US3871438A
Cited
US4211274A
Cited
JPS5653867A
Cited
DE3206048A1
Cited
US4411709A
Cited
JPS5825860A
Cited
US4415444A
Cited
US4577671A
Cited
JPS59219410A
Cited
US4544013A
Cited
JPS6092040A
Cited
JPS6316853A
Cited
US4955425A
Cited
GB2230720A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-03-14 | 1997-09-13 | 1998-03-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-03-14 | 2001-09-13 | 2002-03-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-03-14 | 2005-09-13 | 2006-03-15 | $7700.00 | Window Closed / Lapsed |