Solvent-free, cold-setting organosiloxane composition and its use
Assignee: Suzuki Sangyo Co Ltd
•
Filing: 1992-08-12
•
Granted: 1994-03-08
•
Expires: 2012-08-12
Abstract
Abstract A solvent-free, cold-setting ternary organosiloxane composition is disclosed, which contains (A) liquid organopolysiloxane, (B) a cross-linking agent, and (C) a curing catalyst, said organopolysiloxane (A) being constituted by organosilicon group of X--Si (wherein X represents a hydrogen atom or a monovalent hydrocarbyl group) and functional side chain of OR (wherein R represents a hydrogen atom, a C 1 -C 5 alkyl group or an acyl group), said cross-linking agent (B) being one or more organometallic compounds selected from the group consisting of an organoaluminum compound, an organoboron compound, an organosilicon compound, an organotitanium compound and an organozirconium compound having at least one functional group selected from among an alkoxy group, an acyloxy group and an oxime group, and said curing catalyst (C) being a metal-containing organic compound, with the total contents of the metal elements of the ternary composition being 40% by weight or more in terms of MO y/2 (wherein M represents aluminum, boron, silicon, titanium or zirconium, and y represents a valency of the metal element). A transparent film, a coating material, a binder and a structure formed by using same are also disclosed.
Inventors
- 👤 Hiroyuki Naito
- 👤 Tomio Suzuki
- 👤 Kimie Watanabe
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 18:10
CPC Classifications
C; C08; C08K; C08K5/00; C08K5/0008; C08K5/0025; C08K5/55; Y; Y10; Y10S; Y10S528/00; Y10S528/901
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
153 words
A solvent-free, cold-setting ternary organosiloxane composition, which contains (A) liquid organopolysiloxane, (B) a cross-linking agent, and (C) a curing catalyst, said organopolysiloxane (A) constituted by a organosilicon group of X--Si wherein X represents a hydrogen atom or a monovalent hydrocarbyl group and functional side chain of OR wherein R represents a hydrogen atom, a C 1 -C 5 alkyl group or an acyl group, said cross-linking agent (B) being at least one of an organoboron compound or an organosilicon compound having at least one functional group selected from the group consisting of an alkoxy group, an acyloxy group and an oxime group, and said curing catalyst (C) being a metal-containing organic compound, with the total content of the metal elements of the ternary composition being 40% by weight or more in terms of MO y/2 wherein M represents aluminum, boron, silicon, titanium or zirconium, and y represents a valency of the metal elements.
Claim 2
Dependent Claim
153 words
A solvent-free, cold-setting ternary organosiloxane composition, which contains (A) liquid organopolysiloxane, (B) a cross-linking agent, and (C) a curing catalyst, said organopolysiloxane (A) constituted by a organosilicon group of X--Si wherein X represents a hydrogen atom or a monovalent hydrocarbyl group and functional side chain of OR wherein R represents a hydrogen atom, a C 1 -C 5 alkyl group or an acyl group, said cross-linking agent (B) being at least one of an organoboron compound or an organosilicon compound having at least one functional group selected from the group consisting of an alkoxy group, an acyloxy group and an oxime group, and said curing catalyst (C) being a metal-containing organic compound, with the total content of the metal elements of the ternary composition being 40% by weight or more in terms of MO y/2 wherein M represents aluminum, boron, silicon, titanium or zirconium, and y represents a valency of the metal elements.
Claim 3
Dependent Claim
107 words
The solvent-free, cold-setting ternary organosiloxane composition as described in claim 1, wherein said liquid organosiloxane (A) is a low molecular weight polysiloxane comprising one or more of the compounds represented by the following general formula (1): ##STR2## wherein R 1 represents a hydrogen atom or a C 1 to C 5 alky or acyl group, R 2 to R 6 , which may be the same or different, each represents a hydrogen atom, OR 1 or a monovalent hydrocarbyl group, and n represents a number smaller than 15, and having a silicon content of 50% by weight or more calculated on the basis of SiO 2 .
Claim 4
Dependent Claim
47 words
The solvent-free, cold-setting ternary organosiloxane composition as described in claim 1 or 2, wherein said liquid organopolysiloxane (A) contains a dissolved powdery silicon resin having functional side chains of OR wherein R represents a hydrogen atom or a C 1 to C 5 alkyl or acyl group.
Claim 5
Dependent Claim
45 words
The solvent-free, cold-setting ternary organosiloxane composition as described in claim 2, wherein said liquid organopolysiloxane (A) further contains dissolved therein a thermoplastic organic resin of a linear organic compound having carboxyl groups in an amount of not more than 30% by weight of the composition.
Claim 6
Dependent Claim
92 words
The solvent-free, cold-setting ternary organosiloxane composition as described in claim 4, wherein said cross-linking agent (B) is one or more organometallic compounds represented by the following general formula (2) or (3): R.sub.p.sup.7 ·(OR.sup.1).sub.3-p ( 2) R.sub.m.sup.7 Si·(OR.sup.1).sub.4-m ( 3) wherein R 1 represents a hydrogen atom, a C 1 -C 5 alkyl or acyl group, or an oxime group, R 7 represents a hydrogen atom, OR 1 or a monovalent hydrocarbyl group, p represents an integer of 0, 1 or 2, and m represents an integer of 0, 1, 2 or 3.
Claim 7
Dependent Claim
24 words
The solvent-free, cold-setting ternary organosiloxane agent (B) is mixed in an amount of up to 50% by weight based on said liquid organopolysiloxane (A).
Claim 8
Dependent Claim
24 words
The solvent-free, cold-setting ternary organosiloxane agent (B) is mixed in an amount of up to 50% by weight based on said liquid organopolysiloxane (A).
Claim 9
Dependent Claim
75 words
The solvent-free, cold-setting ternary organosiloxane composition as described in claim 6, wherein said liquid organopolysiloxane (A), or said liquid organopolysiloxane (A) and said cross-linking agent (B), have been subjected to a temperature not higher than 100 ° C. for not shorter than 10 minutes in the absence of water to thereby remove contained silanol groups, and then combined with said curing catalyst (C), so as to be capable of being stored in a one-pack form.
Claim 10
Dependent Claim
33 words
The solvent-free, cold-setting ternary organosiloxane composition as described in claim 7, wherein said curing catalyst (C) is one or more of metal-containing organic compounds, with the metal being zinc, cobalt, aluminum or tin.
Claim 11
Dependent Claim
70 words
The solvent-free, cold-setting ternary organosiloxane composition as described in claim 8, wherein said curing catalyst (C) is in a blocked form of being unable to catalyze the reaction, with the blocking being attained with at least one keto-enol tautomer compound selected from the group consisting of alkyl group- or trifluoro group-containing β-keto-acids, β-diketone compounds and malonic esters in an amount of up to 50% by weight of the curing catalyst.
Claim 12
Dependent Claim
53 words
The solvent-free, cold-setting ternary organosiloxane composition as described in claim 8, wherein said curing catalyst (C) is retarded with one or more alcohols selected from the group consisting of monohydric alcohols and polyhydric alcohols in an amount of up to 50% by weight of the curing catalyst to thereby retard the catalytic reaction.
Claim 13
Dependent Claim
34 words
The solvent-free, cold-setting ternary organosiloxane composition as described in claim 9, wherein said blocked curing catalyst (C) is contained in an amount of up to 10% by weight based on said liquid organopolysiloxane (A).
Claim 14
Dependent Claim
33 words
A transparent film, which comprises a cured polymer containing polysiloxane bonds as a main chain formed by bringing the solvent-free, cold setting ternary organopolysiloxane composition according to claim 11 into contact with moisture.
Claim 15
Dependent Claim
64 words
A coating material, which comprises a cured composite formed by bringing into contact with moisture a mixture of 100 parts by weight of the solvent-free, cold-setting ternary organopolysiloxane composition described in claim 12, and 1 to 400 parts by weight of one or more materials selected from the group consisting of activating agents, fillers, and colorants, to thereby form main chain of polysiloxane bonds.
Claim 16
Dependent Claim
49 words
The coating material as described in claim 13, wherein said fillers, said liquid organopolysiloxane (A), have been subjected to heating to a temperature of 100° C. or less in the absence of water to thereby remove contained water or silanol groups, and then combined with said curing catalyst (C).
Claim 17
Dependent Claim
42 words
The coating material as described in claim 13, which contains activating agents, said activating agents being a powder of at least one material selected from the group consisting of compounds containing boric acid, compounds containing chromic acid and compounds containing phosphoric acid.
Claim 18
Dependent Claim
63 words
A binder which comprises a cured composite formed by bringing into contact with moisture a mixture of 100 parts by weight of the solvent-free, cold-setting ternary organopolysiloxane composition described in claim 11, and 1 to 500 parts by weight of one or more materials selected from the group consisting of activating agents, fillers, and colorants, to thereby form main chain of polysiloxane bonds.
Claim 19
Dependent Claim
56 words
The binder as described in claim 16, wherein said fillers, said liquid organopolysiloxane (A), said cross-linking agent (B) or a mixture thereof have been subjected to heating to a temperature of 100° C. or less in the absence of water to thereby remove contained water or silanol groups, and then combined with said curing catalyst (C).
Claim 20
Dependent Claim
41 words
The binder as described in claim 16, which contains activating agents, said activating agents being a powder of at least one material selected from the group consisting of compounds containing boric acid, compounds containing chromic acid and compounds containing phosphoric acid.
Claim 21
Dependent Claim
47 words
A structure which is formed by bringing into contact with moisture a mixture of 100 parts by weight of the mixture described in claim 13, and 1 to 2,000 parts by weight of reinforcing materials, to thereby produce a composite polymer containing as main chain polysiloxane bonds.
Claim 22
Dependent Claim
13 words
A structure as described in claim 19, wherein the reinforcing materials include aggregates.
Claim 23
Dependent Claim
57 words
A structure which is formed by bringing into contact with moisture a mixture of 100 parts by weight of the fluid or plastic mixture described in claim 16 and 1 to 2,000 parts by weight of one or more of reinforcing materials, aggregates and moldings to thereby produce a composite polymer containing as main chain polysiloxane bonds.
References Cited (Backward Citations)
US3294739A
Cited
US3647917A
Cited
JPS5794057A
Cited
US4517352A
Cited
JPS6051756A
Cited
JPH0368676A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-03-07 | 1997-09-06 | 1998-03-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-03-07 | 2001-09-06 | 2002-03-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-03-07 | 2005-09-06 | 2006-03-08 | $7700.00 | Window Closed / Lapsed |