Solventless or high solids-containing silicone pressure sensitive adhesive compositions

Claim 2

An article of manufacture comprising a solid support carrying on at least one surface thereof an organopolysiloxane composition curable to produce a pressure sensitive adhesive having high tack and high peel adhesion, consisting essentially of by weight; (A) from about 50 to about 75 parts by weight of a toluene soluble, resinous copolymer comprising R 3 SiO 1/2 units and SiO 4/2 units wherein R is a monovalent hydrocarbon radical having from 1 to about 6 carbon atoms, wherein the resinous copolymer comprises from about 0.2% to about 5.0% by weight, based on the total weight of the copolymer, of hydroxyl radicals, at least 95% of all R groups being an alkyl group, the total number of R radicals that are alkenyl radicals being 0-0.5% of all R radicals, the molar ratio of R 3 SiO 1/2 units to SiO 4/2 units being from about 0.6 to about 0.9 inclusive; (B) an alkenyl-terminated polydiorganosiloxane having a viscosity of from about 10 to about 500 centipoise at 25° C. and having the general formula R.sup.2 R.sup.1.sub.2 SiO(R.sup.3.sub.2 SiO).sub.m SiR.sup.1.sub.2 R.sup.2 ( 1) wherein each R 1 is independently an alkyl group having from 1 to about 10 carbons atoms or an aryl group, R 2 is an alkenyl group having from 1 to about 10 carbon atoms, each R 3 is independently R 1 or R 2 , with the proviso that at least 99.5% of all R 3 radicals are R 1 , "m" is a number in the range of from about 1 to about 300; (C) a hydride-terminated organohydrogenpolysiloxane compatible with the mixture of (A) and (B) and having a viscosity of from about 10 to about 1,000 centipoise at 25° C. and having the general formula R.sup.4.sub.2 HSiO(R.sup.5.sub.2 SiO).sub.a SiHR.sup.4.sub.2 ( 11) wherein each R 4 is independently an alkyl group having from 1 to about 10 carbons atoms or an aryl group, and each R 5 is hydrogen or R 4 , with the proviso that at least 99.5% of all R 5 radicals are R 4 , "a" is a number in the range of from 1 to about 500, there being at least two silicon-bonded hydrogen atoms per molecule of (C), no silicon atom bearing more than one silicon-bonded hydrogen atom; the total of (B) and (C) being from about 25 to about 50 parts by weight; the total of (A), (B), and (C) being 100 parts by weight; the molar ratio of silicon-bonded hydrogen groups in (C) to silicon-bonded alkenyl groups in (A) and (B) being in the range of from about 1.2:1 to about 15.0:1; (D) a catalytic amount of hydrosilation catalyst; and (E) from 0 to about 40% by weight of an organic solvent.

Claim 3

An article of manufacture of claim 1 wherein the composition on at least one surface thereof is cured.

Claim 4

A pressure sensitive adhesive tape of claim 1 wherein the composition on at least one surface thereof is cured.

Claim 5

A pressure sensitive adhesive tape according to claim 3 wherein the flexible support is an impregnated glass cloth, a polyester polymer, a polyimide polymer, or a chemically treated fluorocarbon polymer support.

Claim 6

An article according to claim 1 wherein the amount of organic solvent (E) is from about 0 to about 20% by weight.

Claim 7

An article according to claim 1 wherein the amount of organic solvent (E) is 0% by weight

Claim 8

An article according to claim 1 wherein the ratio of silicon-bonded hydrogen atoms in (C) to olefinically unsaturated radicals in the total of (A) and (B) is in the range of from about 1.25:1 to about 6:1.

Claim 9

An article according to claim 7 wherein the ratio of silicon-bonded hydrogen atoms in (C) to olefinically unsaturated radicals in the total of (A) and (B) is in the range of from about 1.35:1 to about 4.5:1.

Claim 10

An article according to claim 1 wherein R is a monovalent hydrocarbon radical having from 1 to about 6 carbons and selected from the group consisting essentially of alkyl radicals; cycloaliphatic radicals; olefinic radicals; and phenyl radicals.

Claim 11

An article according to claim 9 wherein R is methyl.

Claim 12

An article according to claim 1 wherein R 1 and R 3 are each a methyl radical.

Claim 13

A composition according to claim 1 wherein R 2 is vinyl.

Claim 14

An article according to claim 1 wherein R 4 and R 5 are each a methyl radical.

Claim 15

An article according to claim 1 wherein the resinous copolymer (A) comprises from about 1.0% to about 3.0% by weight, based on the total weight of the copolymer, of hydroxyl radicals.

Claim 16

An article according to claim 14 wherein the resinous copolymer (A) comprises from about 1.5% to about 2.5% by weight, based on the total weight of the copolymer, of hydroxyl radicals.

Claim 17

An article according to claim 1 wherein (B) has a viscosity of from about 100 to about 300 centipoise at 25° C.

Claim 18

An article according to claim 1 wherein (C) has a viscosity of from about 20 to about 750 centipoise at 25° C.

Claim 19

An article according to claim 17 wherein (C) has a viscosity of from about 100 to about 400 centipoise at 25° C.

Claim 20

An article according to claim 1 wherein (A) is present in the amount of from about 50 to about 70 parts by weight.

Claim 21

An article according to claim 19 wherein (A) is present in the amount of from about 55 to about 62 parts by weight.

Claim 22

An article according to claim 1 wherein the total amount of (B) and (C) is from about 30 to about 50 parts by weight.

Claim 23

An article according to claim 21 wherein the total amount of (B) and (C) is from about 38 to about 45 parts by weight.

Claim 24

An article according to claim 1 wherein the hydrosilation catalyst is a platinum-containing catalyst.

Claim 25

An article according to claim 23 wherein the platinum-containing catalyst is a platinum complex catalyst stabilized in solution in excess tetramethyldivinyldisiloxane.

Claim 26

An article according to claim 1 wherein the curable composition further comprises an inhibitor for the hydrosilation catalyst.

Claim 27

An article according to claim 25 wherein the inhibitor is a dialkylmaleate.

Claim 28

An article according to claim 26 wherein the dialkylmaleate is dimethylmaleate.

Claim 29

An article according to claim 1 wherein (B) has a viscosity of about 10 to about 400 centipoise at 25° C.

Claim 30

A pressure sensitive adhesive tape comprising a flexible support carrying on at least one surface thereof an organopolysiloxane composition curable to produce a pressure sensitive adhesive having high tack and high peel adhesion, consisting essentially of weight; (A) from about 50 to about 75 parts by weight of a toluene soluble, resinous copolymer comprising R 3 SiO 1/2 units and SiO 4/2 units wherein R is a monovalent hydrocarbon radical having from 1 to about 6 carbon atoms, wherein the resinous copolymer comprises from about 0.2% to about 5.0% by weight, based on the total weight of the copolymer, of hydroxyl radicals, at least 95% of all R groups being an alkyl group, the total number of R radicals that are alkenyl radicals being 0-0.5% of all R radicals, the molar ratio of R 3 SiO 1/2 units to SiO 4/2 units being from about 0.6 to about 0.9 inclusive; (B) an alkenyl-terminated polydiorganosiloxane having a viscosity of from about 10 to about 500 centipoise at 25° C. and having the general formula R.sup.2 R.sup.1.sub.2 SiO(R.sup.3.sub.2 SiO).sub.m SiR.sup.1.sub.2 R.sup.2 ( 1) wherein each R 1 is independently an alkyl group having from 1 to about 10 carbon atoms or an aryl group, R 2 is an alkenyl group having from 1 to about 10 carbon atoms, each R 3 is independently R 1 or R 2 with the proviso that at least 99.5% of all R 3 radicals are R 1 , "m" is a number in the range of from about 1 to about 300; (C) a hydride-terminated organohydrogenpolysiloxane compatible with the mixture of (A) and (B) and having a viscosity of from about 10 to about 1,000 centipoise at 25° C. and having the general formula R.sup.4.sub.2 HSiO(R.sup.5.sub.2 SiO).sub.a SiHR.sup.4.sub.2 ( 11) wherein each R 4 is independently an alkyl group having from 1 to about 10 carbon atoms or an aryl group, and each R 5 is hydrogen or R 4 , with the proviso that at least 99.5% of all R 5 radicals are R 4 , "a" is a number in the range of from 1 to about 500, there being at least two silicon-bonded hydrogen atoms per molecule of (C), no silicon atom bearing more than one silicon-bonded hydrogen atom; the total of (B) and (C) being from about 25 to about 50 parts by weight; the total of (A), (B), and (C) being 100 parts by weight; the molar ratio of silicon-bonded hydrogen groups in (C) to silicon-bonded alkenyl groups in (A) and (B) being in the range of from about 1.2:1 to about 15.0:1; (D) a catalytic amount of a hydrosilation catalyst; and (E) from 0 to about 40% by weight of an organic solvent.

Claim 31

A pressure sensitive adhesive tape comprising a flexible support carrying on at least one surface thereof an organopolysiloxane composition curable to produce a pressure sensitive adhesive having high tack and high peel adhesion, consisting essentially of weight; (A) from about 50 to about 75 parts by weight of a toluene soluble, resinous copolymer comprising R 3 SiO 1/2 units and SiO 4/2 units wherein R is a monovalent hydrocarbon radical having from 1 to about 6 carbon atoms, wherein the resinous copolymer comprises from about 0.2% to about 5.0% by weight, based on the total weight of the copolymer, of hydroxyl radicals, at least 95% of all R groups being an alkyl group, the total number of R radicals that are alkenyl radicals being 0-0.5% of all R radicals, the molar ratio of R 3 SiO 1/2 units to SiO 4/2 units being from about 0.6 to about 0.9 inclusive; (B) an alkenyl-terminated polydiorganosiloxane having a viscosity of from about 10 to about 500 centipoise at 25° C. and having the general formula R.sup.2 R.sup.1.sub.2 SiO(R.sup.3.sub.2 SiO).sub.m SiR.sup.1.sub.2 R.sup.2 ( 1) wherein each R 1 is independently an alkyl group having from 1 to about 10 carbon atoms or an aryl group, R 2 is an alkenyl group having from 1 to about 10 carbon atoms, each R 3 is independently R 1 or R 2 with the proviso that at least 99.5% of all R 3 radicals are R 1 , "m" is a number in the range of from about 1 to about 300; (C) a hydride-terminated organohydrogenpolysiloxane compatible with the mixture of (A) and (B) and having a viscosity of from about 10 to about 1,000 centipoise at 25° C. and having the general formula R.sup.4.sub.2 HSiO(R.sup.5.sub.2 SiO).sub.a SiHR.sup.4.sub.2 ( 11) wherein each R 4 is independently an alkyl group having from 1 to about 10 carbon atoms or an aryl group, and each R 5 is hydrogen or R 4 , with the proviso that at least 99.5% of all R 5 radicals are R 4 , "a" is a number in the range of from 1 to about 500, there being at least two silicon-bonded hydrogen atoms per molecule of (C), no silicon atom bearing more than one silicon-bonded hydrogen atom; the total of (B) and (C) being from about 25 to about 50 parts by weight; the total of (A), (B), and (C) being 100 parts by weight; the molar ratio of silicon-bonded hydrogen groups in (C) to silicon-bonded alkenyl groups in (A) and (B) being in the range of from about 1.2:1 to about 15.0:1; (D) a catalytic amount of a hydrosilation catalyst; and (E) from 0 to about 40% by weight of an organic solvent.

Claim 32

A pressure sensitive adhesive tape according to claim 29 wherein the flexible support is an impregnated glass cloth, a polyester polymer, a polyimide polymer, or a chemically treated fluorocarbon polymer support.