TiOx as an anti-reflection coating for metal lithography
Assignee: Industrial Technology Research Institute
•
Filing: 1992-05-18
•
Granted: 1994-02-15
•
Expires: 2012-05-18
Abstract
Abstract A new method of producing an anti-reflection coating is described. The reflective metal layer of an integrated circuit is covered with titanium. The titanium layer is oxidized. The resulting titanium oxide layer is the anti-reflection coating (ARC) of the present invention. This ARC layer is covered with photoresist. The photoresist layer is selectively exposed to light by directing light through a patterned mask to form a pattern on the photoresist layer. The metal layer is etched in accordance with the pattern. The remaining resist is stripped off. An inter-metal dielectric layer is deposited over the patterned first metal and titanium oxide layers. A second photoresist layer is deposited and selectively exposed to light through a second photomask. The titanium oxide layer again acts to limit the reflection of light off the first metal layer and through the transparent inter-metal dielectric. The exposed inter-metal layer is etched away to the underlying first metal layer. The remaining photoresist is removed. In-situ sputtering, performed to remove native metal oxide, also removes any of the remaining titanium oxide layer. This results in the desired pattern of openings in the inter-metal dielectric. A subsequent metal layer can be deposited, making contact with the first metal through the openings created in the inter-metal dielectric.
Inventors
- 👤 Chao-Ming Koh
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 03:02
CPC Classifications
H; H10; H10P; H10P76/00; H10P76/20; H10P76/204; H10P76/2041; H10P76/2043; G; G03; G03F; G03F7/00; G03F7/004; G03F7/09; G03F7/091; H10P50/00; H10P50/71; H10W; H10W20/00; H10W20/01; H10W20/031; Y; Y10; Y10S; Y10S430/00; Y10S430/151
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
126 words
A photolithographic method of patterning a reflective metal layer of a semiconductor circuit comprising: covering said reflective metal layer of an integrated circuit with a titanium layer having a thickness of between about 200 to 1000 Angstroms; oxidizing said titanium layer to less than about an absorption of 30 atomic percentage oxygen to form a uniform anti-reflective, conductive titanium oxide layer; covering said titanium oxide layer with a resist layer; selectively exposing said resist layer to light by directing light through a patterned mask to expose a pattern in said resist layer; developing said resist layer to form an etching mask; etching openings in said titanium oxide metal layers using said etching mask; and removing said etching mask to complete said patterning of said metal layer.
Claim 2
Dependent Claim
126 words
A photolithographic method of patterning a reflective metal layer of a semiconductor circuit comprising: covering said reflective metal layer of an integrated circuit with a titanium layer having a thickness of between about 200 to 1000 Angstroms; oxidizing said titanium layer to less than about an absorption of 30 atomic percentage oxygen to form a uniform anti-reflective, conductive titanium oxide layer; covering said titanium oxide layer with a resist layer; selectively exposing said resist layer to light by directing light through a patterned mask to expose a pattern in said resist layer; developing said resist layer to form an etching mask; etching openings in said titanium oxide metal layers using said etching mask; and removing said etching mask to complete said patterning of said metal layer.
Claim 3
Dependent Claim
13 words
The method of claim 1 wherein said metal layer is composed of aluminum.
Claim 4
Dependent Claim
13 words
The method of claim 1 wherein said titanium layer is formed by sputtering.
Claim 5
Dependent Claim
20 words
The method of claim 1 wherein the preferred thickness of said titanium layer is between about 200 and 1000 Angstroms.
Claim 6
Dependent Claim
34 words
The method of claim 1 wherein said oxidation of said titanium layer takes place within a vacuum chamber and the vacuum is less than about one Torr and only partially oxidizes said titanium layer.
Claim 7
Dependent Claim
41 words
The method of claim 1 wherein said oxidation continues until titanium is partially oxidized in an oxygen plasma to the point that the titanium oxide is still conductive and the time of said oxidation is between about 5 and 60 minutes.
Claim 8
Independent Claim
249 words
A method for making an integrated circuit comprising: forming a dielectric layer over a semiconductor substrate; forming over said dielectric layer a first metal layer which has a high reflectivity; covering said first metal layer with a layer of titanium having a thickness of between about 200 to 1000 Angstroms; partially oxidizing said titanium layer to less than about an absorption of 30 atomic percentage of oxygen which is an oxidation state that allows the titanium oxide formed by the oxidation to remain conductive; covering said titanium oxide layer with a first resist layer; selectively exposing said first resist layer to light by directing light through a patterned mask to expose a pattern in said first resist layer and developing said pattern in said first resist layer; etching openings in said titanium oxide first metal layers using said pattern in said first resist layer as an etching mask; removing said first resist layer etching mask; covering said patterned first metal and titanium oxide layers with an inter-metal insulating layer; covering said inter-metal insulating layer with a second resist layer; selectively exposing said second resist layer to light by directing light through a patterned mask to expose a pattern in said second resist layer and developing the resist to form an etching mask therein; etching openings in said inter-metal insulating layer using said etching mask; removing said etching mask; and depositing a second metal layer contacting said first metal layer through said patterned openings resulting in the desired integrated circuit.
Claim 9
Independent Claim
249 words
A method for making an integrated circuit comprising: forming a dielectric layer over a semiconductor substrate; forming over said dielectric layer a first metal layer which has a high reflectivity; covering said first metal layer with a layer of titanium having a thickness of between about 200 to 1000 Angstroms; partially oxidizing said titanium layer to less than about an absorption of 30 atomic percentage of oxygen which is an oxidation state that allows the titanium oxide formed by the oxidation to remain conductive; covering said titanium oxide layer with a first resist layer; selectively exposing said first resist layer to light by directing light through a patterned mask to expose a pattern in said first resist layer and developing said pattern in said first resist layer; etching openings in said titanium oxide first metal layers using said pattern in said first resist layer as an etching mask; removing said first resist layer etching mask; covering said patterned first metal and titanium oxide layers with an inter-metal insulating layer; covering said inter-metal insulating layer with a second resist layer; selectively exposing said second resist layer to light by directing light through a patterned mask to expose a pattern in said second resist layer and developing the resist to form an etching mask therein; etching openings in said inter-metal insulating layer using said etching mask; removing said etching mask; and depositing a second metal layer contacting said first metal layer through said patterned openings resulting in the desired integrated circuit.
Claim 10
Dependent Claim
13 words
The method of claim 7 wherein said metal layer is composed of aluminum.
Claim 11
Dependent Claim
13 words
The method of claim 7 wherein said titanium layer is formed by sputtering.
Claim 12
Dependent Claim
20 words
The method of claim 7 wherein the preferred thickness of said titanium layer is between about 200 and 1000 Angstroms.
Claim 13
Dependent Claim
27 words
The method of claim 7 wherein said oxidation of said titanium layer takes place within a vacuum chamber and the vacuum is less than about one Torr.
Claim 14
Dependent Claim
43 words
The method of claim 7 wherein said oxidation occurs in an oxygen plasma under the conditions of time between about 5 and 60 minutes, at a vacuum of between about 250 to 1000 mTorr and at a radio frequency power of 1300 watts.
Claim 15
Dependent Claim
15 words
The method of claim 7 wherein said inter-metal insulating layer is composed of silicon dioxide.
Claim 16
Dependent Claim
38 words
The method of claim 13 wherein said silicon dioxide layer is etched by a CHF 3 +O 2 etching system so that said silicon dioxide and titanium oxide are etched at a similar rate with this etching system.
Claim 17
Independent Claim
115 words
The method for reducing the light reflection from a reflective metal surface into a resist layer formed thereover comprising: covering said reflective metal surface with a titanium layer having a thickness of between about 200 to 1000 Angstroms; oxidizing said titanium layer to less than about an absorption of 30 atomic percentage of oxygen to form a uniform anti-reflective, conductive titanium oxide layer; covering said titanium oxide layer with a resist layer; selectively exposing said resist layer to light by directing light through a patterned mask to expose said resist layer; developing said resist layer to form an etching mask; etching openings in said metal layer using said etching mask; and removing said etching mask.
Claim 18
Independent Claim
115 words
The method for reducing the light reflection from a reflective metal surface into a resist layer formed thereover comprising: covering said reflective metal surface with a titanium layer having a thickness of between about 200 to 1000 Angstroms; oxidizing said titanium layer to less than about an absorption of 30 atomic percentage of oxygen to form a uniform anti-reflective, conductive titanium oxide layer; covering said titanium oxide layer with a resist layer; selectively exposing said resist layer to light by directing light through a patterned mask to expose said resist layer; developing said resist layer to form an etching mask; etching openings in said metal layer using said etching mask; and removing said etching mask.
Claim 19
Dependent Claim
26 words
The method of claim 15 wherein said titanium layer is formed by sputtering, the thickness of said titanium layer is between about 200 and 1000 Angstroms.
Claim 20
Dependent Claim
27 words
The method of claim 15 wherein said oxidation of said titanium layer takes place within a vacuum chamber and the vacuum is less than about one Torr.
Claim 21
Dependent Claim
43 words
The method of claim 15 wherein said oxidation occurring in an oxygen plasma under the conditions of time between about 5 and 60 minutes, at a vacuum of between about 250 to 1000 mTorr and at a radio frequency power of 1300 watts.
Claim 22
Dependent Claim
13 words
The method of claim 15 wherein said metal layer is composed of aluminum.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-02-14 | 1997-08-16 | 1998-02-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-02-14 | 2001-08-16 | 2002-02-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-02-14 | 2005-08-16 | 2006-02-15 | $7700.00 | Window Closed / Lapsed |