Abstract
Abstract Extruded, smooth finished solid sheet or film, which may have a thickness<1 mm, of a thermoplastic plastic (such as polycarbonate) with a glass transition temperature >50 degrees C., which under conditions of orientation displays optical birefringence, may be manufactured into a flat strip with smooth finished surfaces, to yield a strip which has characteristics as follows: optical birefringence path difference less than or equal to 50 nm (single pass); low surface roughness; low variation in thickness; by extrusion of the plastic in a thermoplastic state, through a slot nozzle; wherein during or after the smoothing of the two surfaces one of the surfaces of the strip is cooled to below the glass transition temperature, while the other surface and the predominant part of the interior region of the strip remain in the thermoplastic state and the strip is cooled to below the glass transition temperature, under conditions which minimize the deforming forces on the surfaces of the extruded strip.
Inventors
- 👤 Karl Funk
- 👤 Heinz Gross
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 01:20
CPC Classifications
B; B29; B29D; B29D11/00; B29C; B29C48/00; B29C48/03; B29C48/07; B29C48/25; B29C48/88; B29C48/90; B29C48/911; B29C48/9135; B29C48/9145; B29C59/00; B29C59/02; B29C59/04; B29D7/00; B29D7/01; B29C48/001; B29C48/0018; B29C48/0022; B29C48/08; B29K; B29K2069/00; B29K2995/00; B29K2995/0037; B29K2995/0072; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24942; Y10T428/2495; Y10T428/24967; Y10T428/31504; Y10T428/31507; Y10T428/31533; Y10T428/3154; Y10T428/31786; Y10T428/31855; Y10T428/31931; Y10T428/31935
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
159 words
A method of manufacturing an extruded, smooth-finished solid sheet or film of thermoplastic plastic having a glass transition temperature of more than 50° C., comprising the steps of: a) extruding said thermoplastic plastic in a thermoplastic state from a slit nozzle, to form a flat strip having a first surface and a second surface, b) smoothing said first surface and said second surface of said strip whole in said thermoplastic state, c) cooling said first surface and a layer of said strip adjoining said first surface to below the glass transition temperature, while maintaining said second surface and the remainder of said strip in the thermoplastic state, said layer of said strip adjoining said first surface being sufficiently thick hat said fist surface does not become reheated by the thermoplastic plastic in the thermoplastic state in the remainder of said strip; and d) cooling said strip under conditions which minimize deforming forces on the surfaces of the extruded strip.
Claim 2
Independent Claim
159 words
A method of manufacturing an extruded, smooth-finished solid sheet or film of thermoplastic plastic having a glass transition temperature of more than 50° C., comprising the steps of: a) extruding said thermoplastic plastic in a thermoplastic state from a slit nozzle, to form a flat strip having a first surface and a second surface, b) smoothing said first surface and said second surface of said strip whole in said thermoplastic state, c) cooling said first surface and a layer of said strip adjoining said first surface to below the glass transition temperature, while maintaining said second surface and the remainder of said strip in the thermoplastic state, said layer of said strip adjoining said first surface being sufficiently thick hat said fist surface does not become reheated by the thermoplastic plastic in the thermoplastic state in the remainder of said strip; and d) cooling said strip under conditions which minimize deforming forces on the surfaces of the extruded strip.
Claim 3
Dependent Claim
17 words
The method of claim 1, wherein said smooth-finished sheet or film has a thickness of <1 mm.
Claim 4
Dependent Claim
17 words
The method of claim 2, wherein said smooth-finished sheet or film has a thickness of <0.5 mm.
Claim 5
Dependent Claim
34 words
The method of claim 1, wherein said thermoplastic plastic has an absolute value of the quotient of the observed birefringence (delta-n) and the measured orientation function (F or ) greater than 10×10 -3 .
Claim 6
Dependent Claim
63 words
The method of claim 1, wherein said surfaces of said strip are smoothed by means of a first and a second smoothing device, wherein said first smoothing device has a surface temperature which is below the glass transition temperature of said thermoplastic plastic, and said second smoothing device has a surface temperature which is in the thermoplastic state domain of said thermoplastic plastic.
Claim 7
Dependent Claim
51 words
The method of claim 5, wherein after a firsts surface of said strip is cooled to below the glass transition temperature, said strip is freed from said first smoothing device, and the free surface is kept free from deforming forces until the strip is cooled to below the glass transition temperature.
Claim 8
Dependent Claim
12 words
The method of claim 1, wherein said thermoplastic plastic is polycarbonate plastic.
Claim 9
Dependent Claim
28 words
The method of claim 1, wherein said layer of said strip adjoining said first surface has a thickness not greater than one-half of the thickness of said strip.
Claim 10
Dependent Claim
26 words
The method of claim 8, wherein said thickness of said layer adjoining said fist surface is not greater than one-third of the thickness of said strip.
Claim 11
Dependent Claim
29 words
The method of claim 5, wherein said surface temperature of said first smoothing device is 60°-140° C., and said surface temperature of said second smoothing device is 160°-300° C.
Claim 12
Independent Claim
135 words
An apparatus for manufacturing an extruded, smooth finished solid sheet or film, which sheet or film is comprised of thermoplastic material, said apparatus comprising: (a) a slot nozzle fed by an extruder for producing a flat extruded strip; (b) a smoothing apparatus comprised of at least one smooth-finished upper roll and a lower roll, for smoothing said flat strip in a gap between said upper and lower rolls; wherein said upper roll has a cooling means; and said lower roll has a means for heating said lower roll to a temperature in the thermoplastic state domain of the plastic; (c) a planar cooling plate; and (d) a smooth finished endless belt which is passed around said lower roll and is guided over said planar cooling plate and a redirecting roll, back to said lower roll.
Claim 13
Independent Claim
135 words
An apparatus for manufacturing an extruded, smooth finished solid sheet or film, which sheet or film is comprised of thermoplastic material, said apparatus comprising: (a) a slot nozzle fed by an extruder for producing a flat extruded strip; (b) a smoothing apparatus comprised of at least one smooth-finished upper roll and a lower roll, for smoothing said flat strip in a gap between said upper and lower rolls; wherein said upper roll has a cooling means; and said lower roll has a means for heating said lower roll to a temperature in the thermoplastic state domain of the plastic; (c) a planar cooling plate; and (d) a smooth finished endless belt which is passed around said lower roll and is guided over said planar cooling plate and a redirecting roll, back to said lower roll.
References Cited (Backward Citations)
US2791801A
Cited
US2815308A
Cited
DE2432778A1
Cited
JPS5417982A
Cited
EP0008543A1
Cited
JPS58131050A
Cited
DE3319279A1
Cited
DE3429818A1
Cited
EP0199824A1
Cited
US4734229A
Cited
US4826560A
Cited
US4994229A
Cited
US4859392A
Cited
DE3730043A1
Cited
US4858139A
Cited
US4921669A
Cited
US5149481A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-02-14 | 1997-08-16 | 1998-02-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-02-14 | 2001-08-16 | 2002-02-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-02-14 | 2005-08-16 | 2006-02-15 | $7700.00 | Window Closed / Lapsed |