Porous silicon carbide ceramics using filled polysiloxanes
Assignee: Dow Silicones Corp
•
Filing: 1993-05-04
•
Granted: 1994-02-01
•
Expires: 2013-05-04
Abstract
Abstract The preparation of porous ceramic bodies by sintering certain curable organopolysiloxanes filled with silicon carbide powders. This process is advantageous in that the green bodies have relative high strengths and thus can be easily handled and, if desired, machined before sintering.
Inventors
- 👤 William H. Atwell
- 👤 Chandan K. Saha
- 👤 Gregg A. Zank
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 16:55
CPC Classifications
C; C04; C04B; C04B38/00; C04B38/0022
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
183 words
A method of preparing a porous silicon carbide body comprising: (i) forming a mixture consisting essentially of silicon carbide powder, between about 0.1 and 50 wt % of a preceramic organopolysiloxane based on the weight of the silicon carbide powder wherein the preceramic organopolysiloxane sinters at 1800° C. to a char which contains between 0 and about 10 wt % free carbon based on the weight of the char and the silicon carbide powder, between 0 and about 3 wt. % metal-containing sintering aid based on the weight of the char and the silicon carbide powder, and, optionally, an organopolysiloxane curing agent in an amount effective to cure the organopolysiloxane, with the proviso that either the amount of free carbon derived from the preceramic organopolysiloxane or the amount of metal-containing sintering aid or both is less than about 0.1 wt. %; (ii) forming the mixture into a shape; and (iii) sintering the shape in an inert atmosphere at a temperature sufficient to obtain a porous silicon carbide body having a density less than 2.4 g/cm 3 and an open porosity greater than 25%.
Claim 2
Independent Claim
183 words
A method of preparing a porous silicon carbide body comprising: (i) forming a mixture consisting essentially of silicon carbide powder, between about 0.1 and 50 wt % of a preceramic organopolysiloxane based on the weight of the silicon carbide powder wherein the preceramic organopolysiloxane sinters at 1800° C. to a char which contains between 0 and about 10 wt % free carbon based on the weight of the char and the silicon carbide powder, between 0 and about 3 wt. % metal-containing sintering aid based on the weight of the char and the silicon carbide powder, and, optionally, an organopolysiloxane curing agent in an amount effective to cure the organopolysiloxane, with the proviso that either the amount of free carbon derived from the preceramic organopolysiloxane or the amount of metal-containing sintering aid or both is less than about 0.1 wt. %; (ii) forming the mixture into a shape; and (iii) sintering the shape in an inert atmosphere at a temperature sufficient to obtain a porous silicon carbide body having a density less than 2.4 g/cm 3 and an open porosity greater than 25%.
Claim 3
Dependent Claim
59 words
The method of claim 1 wherein the organopolysiloxane contains units selected from the group consisting of [RSiO 1 .5 ], [R 2 SiO], [R 3 SiO 0 .5 ] and [SiO 2 ] units where each R is independently selected from the group consisting of hydrogen, alkyl radicals containing 1 to 20 carbon atoms, phenyl radicals, and vinyl radicals.
Claim 4
Dependent Claim
18 words
The method of claim 1 wherein the shape is sintered at a temperature of 1600° to 2200° C.
Claim 5
Dependent Claim
26 words
The method of claim 1 wherein the organopolysiloxane has a char yield greater than about 40 wt % when pyrolyzed at a temperature of 1800° C.
Claim 6
Dependent Claim
35 words
The method of claim 1 wherein the silicon carbide powder has a particle size of less than about 10 microns and the powder is selected from the group consisting of alpha, beta and mixtures thereof.
Claim 7
Dependent Claim
22 words
The method of claim 1 wherein the mixture also contains a material selected from the group consisting of lubricants, deflocculants and dispersants.
Claim 8
Dependent Claim
17 words
The method of claim 1 wherein the shape is sintered in an atmosphere consisting essentially of nitrogen.
Claim 9
Dependent Claim
30 words
The method of claim 1 wherein the organopolysiloxane curing agent is an organic peroxide which is present at 0.1 to 5.0 weight percent based on the weight of the organopolysiloxane.
Claim 10
Dependent Claim
30 words
The method of claim 1 wherein the organopolysiloxane curing agent is a platinum-containing catalyst which is present at 1.0 to 1000 ppm Pt based on the weight of the organopolysiloxane.
Claim 11
Dependent Claim
37 words
The method of claim 1 wherein the organopolysiloxane curing agent comprises a polyfunctional organosilicon compound and it is included in an amount of between about 0.1 and 5 wt % based on the weight of the organopolysiloxane.
Claim 12
Dependent Claim
23 words
The method of claim 1 wherein the sintering aid is selected from the group consisting of boron, boron-containing compounds, aluminum, and aluminum-containing compounds.
Claim 13
Independent Claim
152 words
A method of preparing a porous silicon carbide body comprising: (i) forming a mixture consisting essentially of silicon carbide powder, between about 0.1 and 3 wt. percent metal-containing sintering aid based on the weight of silicon carbide powder, between about 0.1 and 50 wt % of a preceramic organopolysiloxane based on the weight of the silicon carbide powder and, optionally, an organopolysiloxane curing agent in an amount effective to cure the organopolysiloxane, wherein the organopolysiloxane sinters at 1800° C. to a char which contains between about 0.1 and about 10 wt % free carbon based on the weight of the char and the silicon carbide powder; (ii) forming the mixture into a shape; and (iii) sintering the shape in an inert atmosphere at a temperature less than about 1800° C. to obtain a porous silicon carbide body having a density less than 2.4 g/cm 3 and an open porosity greater than 25%.
Claim 14
Independent Claim
152 words
A method of preparing a porous silicon carbide body comprising: (i) forming a mixture consisting essentially of silicon carbide powder, between about 0.1 and 3 wt. percent metal-containing sintering aid based on the weight of silicon carbide powder, between about 0.1 and 50 wt % of a preceramic organopolysiloxane based on the weight of the silicon carbide powder and, optionally, an organopolysiloxane curing agent in an amount effective to cure the organopolysiloxane, wherein the organopolysiloxane sinters at 1800° C. to a char which contains between about 0.1 and about 10 wt % free carbon based on the weight of the char and the silicon carbide powder; (ii) forming the mixture into a shape; and (iii) sintering the shape in an inert atmosphere at a temperature less than about 1800° C. to obtain a porous silicon carbide body having a density less than 2.4 g/cm 3 and an open porosity greater than 25%.
Claim 15
Dependent Claim
59 words
The method of claim 12 wherein the organopolysiloxane contains units selected from the group consisting of [RSiO 1 .5 ], [R 2 SiO], [R 3 SiO 0 .5 ] and [SiO 2 ] units where each R is independently selected from the group consisting of hydrogen, alkyl radicals containing 1 to 20 carbon atoms, phenyl radicals, and vinyl radicals.
Claim 16
Dependent Claim
35 words
The method of claim 12 wherein the silicon carbide powder has a particle size of less than about 10 microns and the powder is selected from the group consisting of alpha, beta and mixtures thereof.
Claim 17
Dependent Claim
22 words
The method of claim 12 wherein the mixture also contains a material selected from the group consisting of lubricants, deflocculants and dispersants.
Claim 18
Dependent Claim
17 words
The method of claim 12 wherein the shape is sintered in an atmosphere consisting essentially of nitrogen.
Claim 19
Dependent Claim
30 words
The method of claim 12 wherein the organopolysiloxane curing agent is an organic peroxide which is present at 0.1 to 5.0 weight percent based on the weight of the organopolysiloxane.
Claim 20
Dependent Claim
30 words
The method of claim 12 wherein the organopolysiloxane curing agent is a platinum-containing catalyst which is present at 1.0 to 1000 ppm Pt based on the weight of the organopolysiloxane.
Claim 21
Dependent Claim
37 words
The method of claim 12 wherein the organopolysiloxane curing agent comprises a polyfunctional organosilicon compound and it is included in an amount of between about 0.1 and 5 wt % based on the weight of the organopolysiloxane.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-01-31 | 1997-08-02 | 1998-02-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-01-31 | 2001-08-02 | 2002-02-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-01-31 | 2005-08-02 | 2006-02-01 | $7700.00 | Window Closed / Lapsed |