Fabrication method for quantum devices in compound semiconductor layers
Assignee: International Business Machines Corp
•
Filing: 1992-07-13
•
Granted: 1994-01-25
•
Expires: 2012-07-13
Abstract
Abstract Disclosed is a new method suitable for making highly integrated quantum wire arrays, quantum dot arrays in a single crystal compound semiconductor and FETs of less than 0.1 micron gate length. This makes it possible to construct a high-performance electronic device with high speed and low power consumption, using a combination of low-temperature-growth molecular beam epitaxy (LTG-MBE) and focused ion beam (FIB) implantation. The compound semiconductor (GaAs) epitaxial layers, which are made by LTG-MBE, are used as targets of Ga FIB implantation to make Ga wire or dot arrays. Precipitation of arsenic microcrystals, which are initially embedded in a single crystal GaAs layer and act as Schottky barriers, are typically observed in an LTG GaAs layer. A thermal annealing process, after implantation, changes the arsenic microcrystals to GaAs crystals if the arsenic microcrystals are in the region in which the Ga ions are implanted. A wire-like shape free of As microcrystals then acts as a quantum wire for electrons or holes whereas a dot-like shape free of As microcrystals acts as a quantum dot. The co-existence of Ga ions and dopant ions, which provides conductivity type carriers opposite to the conductivity type of the majority carriers of a channel region of an FET, provides the fabrication of very narrow junction gate region for any FET.
Inventors
- 👤 Tadashi Fukuzawa
- 👤 Hiro Munekata
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 01:43
CPC Classifications
H; H10; H10P; H10P30/00; H10P30/20; H10P30/202; H10P30/206; B; B82; B82Y; B82Y10/00; H10D; H10D30/00; H10D30/01; H10D30/014; H10D30/051; H10P14/00; H10P14/20; H10P14/38; H10P14/3824; H10P30/208; H10W; H10W90/00; H10D62/00; H10D62/80; H10D62/85; H10W90/20; H10W90/297; Y; Y10; Y10S; Y10S438/00; Y10S438/962
Claims Analysis
Total Claims: 39
Claim 1
Independent Claim
59 words
A method for fabricating semiconductor devices comprising the steps of: depositing a layer of a compound semiconductor such that said layer contains clusters of one of said compound semiconductor elements which render said layer highly resistive, and converting the crystalline structure of said compound semiconductor in at least a discrete region of said layer to render said region conductive.
Claim 2
Independent Claim
59 words
A method for fabricating semiconductor devices comprising the steps of: depositing a layer of a compound semiconductor such that said layer contains clusters of one of said compound semiconductor elements which render said layer highly resistive, and converting the crystalline structure of said compound semiconductor in at least a discrete region of said layer to render said region conductive.
Claim 3
Dependent Claim
48 words
A method according to claim 1 wherein the step of depositing includes the steps of: forming by molecular beam expitaxy a layer of said compound semiconductor such that said clusters result from the presence of an excess of said one of said compound semiconductor elements in said layer.
Claim 4
Dependent Claim
47 words
A method according to claim 1 wherein the steps of converting includes the steps of: ion implanting the other of said compound semiconductor elements into said at least a discrete region, and, annealing said layer for a time at a temperature sufficient to reform said compound semiconductor.
Claim 5
Dependent Claim
16 words
A method according to claim 1 wherein said layer is doped with a conductivity-type determining impurity.
Claim 6
Dependent Claim
25 words
A method according to claim 1 wherein said compound semiconductor is one taken from Groups III and V of the Periodic Table of the Elements.
Claim 7
Dependent Claim
25 words
A method according to claim 1 wherein said compound semiconductor is one taken from Groups II and VI of the Periodic Table of the Elements.
Claim 8
Dependent Claim
19 words
A method according to claim 1 wherein said compound semiconductor includes ternary and quaternary alloys of said compound semiconductor.
Claim 9
Dependent Claim
24 words
A method according to claim 1 wherein said clusters of one of said compound semiconductor elements includes microcrystals of said one of said elements.
Claim 10
Dependent Claim
26 words
A method according to claim 1 wherein said cluster of one of said compound semiconductor elements includes point defects made of said one of said elements.
Claim 11
Dependent Claim
23 words
A method according to claim 1 wherein said compound semiconductor is gallium arsenide and said one of said compound semiconductor elements is arsenic.
Claim 12
Dependent Claim
23 words
A method according to claim 1 wherein said compound semiconductor is zinc selenide and said one of said compound semiconductor elements is selenium.
Claim 13
Dependent Claim
29 words
A method according to claim 3 further including the step of ion implanting a conductivity-type determining impurity simultaneously with the implanting of said other of said compound semiconductor elements.
Claim 14
Dependent Claim
33 words
A method according to claim 3 wherein said compound semiconductor is gallium arsenide, and said one of said compound semiconductor elements is arsenic and said other of said compound semiconductor elements is gallium.
Claim 15
Dependent Claim
32 words
A method according to claim 3 wherein said compound semiconductor is zinc selenide, said one of said compound semiconductor elements is selenium and said other of said compound semiconductor elements is zinc.
Claim 16
Independent Claim
59 words
A method for fabricating semiconductor devices comprising the steps of: depositing a layer of a compound semiconductor containing clusters of one of said compound semiconductor elements to render said layer substantially free of carriers, and converting the crystalline structure of said compound semiconductor in at least a discrete region of said layer to activate said carriers in said region.
Claim 17
Independent Claim
59 words
A method for fabricating semiconductor devices comprising the steps of: depositing a layer of a compound semiconductor containing clusters of one of said compound semiconductor elements to render said layer substantially free of carriers, and converting the crystalline structure of said compound semiconductor in at least a discrete region of said layer to activate said carriers in said region.
Claim 18
Dependent Claim
46 words
A method according to claim 15 wherein the step of depositing includes the step of: forming a layer of said compound semiconductor by molecular beam epitaxy such that said clusters result from the presence of an excess of said one of said elements in said layer.
Claim 19
Dependent Claim
48 words
A method according to claim 15 wherein the step of converting includes the steps of: ion implanting the other of said compound semiconductor elements into said at least a discrete region, and annealing said layer for a time and at a temperature sufficient to reform said compound semiconductor.
Claim 20
Dependent Claim
16 words
A method according to claim 15 wherein said layer is doped with a conductivity-type determining impurity.
Claim 21
Dependent Claim
25 words
A method according to claim 15 wherein said compound semiconductor is one taken from Groups III and V of the Periodic Table of the Elements.
Claim 22
Dependent Claim
25 words
A method according to claim 15 wherein said compound semiconductor is one taken from Groups II and VI of the Periodic Table of the Elements.
Claim 23
Dependent Claim
19 words
A method according to claim 15 wherein said compound semiconductor includes ternary and quaternary alloys of said compound semiconductor.
Claim 24
Dependent Claim
24 words
A method according to claim 15 wherein said clusters of one of said compound semiconductor elements includes microcrystals of said one of said elements.
Claim 25
Dependent Claim
26 words
A method according to claim 15 wherein said cluster of one of said compound semiconductor elements includes point defects made of said one of said elements.
Claim 26
Dependent Claim
23 words
A method according to claim 15 wherein said compound semiconductor is gallium arsenide and said one of said compound semiconductor elements is arsenic.
Claim 27
Dependent Claim
23 words
A method according to claim 15 wherein said compound semiconductor is zinc selenide and said one of said compound semiconductor elements is selenium.
Claim 28
Dependent Claim
32 words
A method according to claim 17 wherein said compound semiconductor is gallium arsenide, said one of said compound semiconductor elements is arsenic and said other of said compound semiconductor elements is gallium.
Claim 29
Dependent Claim
32 words
A method according to claim 17 wherein said compound semiconductor is zinc selenide, said one of said compound semiconductor elements is selenium and said other of said compound semiconductor elements is zinc.
Claim 30
Dependent Claim
29 words
A method according to claim 17 further including the step of ion implanting a conductivity-type determining impurity simultaneously with the implanting of said other of said compound semiconductor elements.
Claim 31
Independent Claim
108 words
A method of fabricating a structure in a III-V compound layer, comprising the steps of: (a) growing epitaxially on a substrate a III-V compound layer, the epitaxial growth parameters being controlled to produce group V element clusters embedded therein in such concentration that the grown layer becomes a carrier depletion layer; (b) implanting ions including at least Group III element ions into a region of said III-V compound layer, the concentration of the implanted Group III element ions in the region being adjusted to compensate for the Group V element clusters; and (c) annealing the ion implanted region whereby a region free from carrier depletion is formed therein.
Claim 32
Independent Claim
108 words
A method of fabricating a structure in a III-V compound layer, comprising the steps of: (a) growing epitaxially on a substrate a III-V compound layer, the epitaxial growth parameters being controlled to produce group V element clusters embedded therein in such concentration that the grown layer becomes a carrier depletion layer; (b) implanting ions including at least Group III element ions into a region of said III-V compound layer, the concentration of the implanted Group III element ions in the region being adjusted to compensate for the Group V element clusters; and (c) annealing the ion implanted region whereby a region free from carrier depletion is formed therein.
Claim 33
Dependent Claim
23 words
A method according to claim 29 wherein the step of growing includes the step of doping said layer with a conductivity-type determining impurity.
Claim 34
Dependent Claim
34 words
A method according to claim 29 wherein the step of implanting includes the step of ion implanting a conductivity-type determining impurity into said region simultaneously with the implanting of said Group III element ions.
Claim 35
Dependent Claim
38 words
A method according to claim 29 wherein the step of ion implanting includes the step of ion implanting Group III and Group II element ions into said layer to form at least a n-conductivity region in said layer.
Claim 36
Dependent Claim
38 words
A method according to claim 29 wherein the step of ion implanting includes the step of ion implanting Group III and Group II element ions into said layer to form at least a p-conductivity region in said layer.
Claim 37
Independent Claim
203 words
A method of fabricating an electronic device including at least one FET with source, drain, gate and channel regions comprising the steps of: growing epitaxially on a substrate a first III-V compound semiconductor layer, the epitaxial growth parameters being controlled to produce Group V element clusters embedded therein in such concentration that the grown layer becomes a carrier depletion layer; implanting ions including at least Group III element ions into regions of said III-V compound layer, the concentration of the implanted Group III element ions in the region being adjusted to compensate for the Group V element clusters; growing on said first III-V compound layer a second III-V compound layer like said first layer; implanting ions including at least Group III element ions into regions of said second III-V compound layer, the concentration of the implanted Group III element ions in the region being adjusted to compensate for the Group V element clusters, and annealing the ion implanted regions, to form said source, said drain, and said channel regions free from carrier depletion in said first layer and a gate region over said channel region and ohmic contact regions over said source and drain regions free from carrier depletion in said second layer.
Claim 38
Independent Claim
203 words
A method of fabricating an electronic device including at least one FET with source, drain, gate and channel regions comprising the steps of: growing epitaxially on a substrate a first III-V compound semiconductor layer, the epitaxial growth parameters being controlled to produce Group V element clusters embedded therein in such concentration that the grown layer becomes a carrier depletion layer; implanting ions including at least Group III element ions into regions of said III-V compound layer, the concentration of the implanted Group III element ions in the region being adjusted to compensate for the Group V element clusters; growing on said first III-V compound layer a second III-V compound layer like said first layer; implanting ions including at least Group III element ions into regions of said second III-V compound layer, the concentration of the implanted Group III element ions in the region being adjusted to compensate for the Group V element clusters, and annealing the ion implanted regions, to form said source, said drain, and said channel regions free from carrier depletion in said first layer and a gate region over said channel region and ohmic contact regions over said source and drain regions free from carrier depletion in said second layer.
Claim 39
Dependent Claim
47 words
The method of claim 34, further including the steps of: growing an insulating layer on said second III-V compound layer, and forming in said insulating layer ohmic contact regions over said gate region and said ohmic contact regions which are formed in said second III-V compound layer.
References Cited (Backward Citations)
US4503447A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-01-24 | 1997-07-26 | 1998-01-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-01-24 | 2001-07-26 | 2002-01-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-01-24 | 2005-07-26 | 2006-01-25 | $7700.00 | Window Closed / Lapsed |