Unsaturated polyaminopolymer, derivatives thereof and processes for making
Assignee: Dow Chemical Co
•
Filing: 1992-08-11
•
Granted: 1994-01-11
•
Expires: 2012-08-11
Abstract
Abstract The present invention is a process for preparing a polyaminopolymer which contains functionality comprising the steps of (a) contacting a polyfunctional amine with an unsaturated alkylating agent under reaction conditions to form an amine/unsaturated alkylating agent adduct; (b) contacting the adduct with a polyfunctional compound such that a polyaminopolymer is formed; (c) contacting the polyaminopolymer with a halogen, hypohalous acid or precursor thereof such that a polyaminopolymer having halohydrin or dihalo functionality is formed; and (d) raising the pH of the polyaminopolymer having halohydrin or vicinal dihalo functionality sufficiently to cause an increase in molecular weight. Alternatively, the invention is a process having steps (a), (b), (c) and optionally (d), but with a step (h) between steps (b) and (c) of contacting the polyaminopolymer with a crosslinking agent therefor having at least two functional groups reactive with amine groups such that a crosslinked polyaminopolymer is formed. The invention includes polyaminopolymers so prepared, papers prepared using such polymers, and processes for preparing such papers. The papers so prepared preferably have improved wet strength. The polyaminopolymers are useful when dried and redissolved. Certain of the polyamino-polymers have structures of Formula IV: [--R'N--(C.sub.n H.sub.2n NR).sub.m --CO--Q--CO--] wherein R and R' are independently H or an unsaturated organic group; n is the number of carbon atoms between nitrogen atoms in a repeating unit of an amine which unit is repeated m times; and Q is divalent organic group of a dicarboxylic polyfunctional compound. Compounds of Formula IV are also made by forming a polyamide then alkylating the polyamide with excess alkylating agent at high pH.
Inventors
- 👤 Otha G. Weaver, Jr.
- 👤 Terry W. Glass
- 👤 Wanda G. Buckner
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 07:57
CPC Classifications
C; C08; C08G; C08G73/00; C08G73/02; C08G73/0206; C08G73/0213; D; D21; D21H; D21H17/00; D21H17/20; D21H17/33; D21H17/46; D21H17/54; D21H17/55
Claims Analysis
Total Claims: 50
Claim 1
Independent Claim
141 words
A process of preparing a polyaminopolymer which contains functionality comprising the steps of (a) contacting a polyfunctional amine with an ethylenically unsaturated alkylating agent under reaction conditions to form an amine/ethylenically unsaturated alkylating agent adduct; (b) contacting the adduct with a polyfunctional compound under reaction conditions to form a polyaminopolymer (c) contacting the polyaminopolymer with a halogen, hypohalous acid or precursor thereof under reaction conditions to form a polyaminopolymer having halohydrin or dihalo functionality; and crosslinking the polyaminopolymer by either or both: (h), after step (b) and before step (c), contacting the polyaminopolymer with a crosslinking agent therefor having at least two functional groups reactive with amine groups under reaction conditions to form a crosslinked polyaminopolymer; or (d), after step (c) raising the pH of the polyaminopolymer having halohyrin or vicinal dihalo functionality sufficiently to cause an increase in molecular weight.
Claim 2
Dependent Claim
141 words
A process of preparing a polyaminopolymer which contains functionality comprising the steps of (a) contacting a polyfunctional amine with an ethylenically unsaturated alkylating agent under reaction conditions to form an amine/ethylenically unsaturated alkylating agent adduct; (b) contacting the adduct with a polyfunctional compound under reaction conditions to form a polyaminopolymer (c) contacting the polyaminopolymer with a halogen, hypohalous acid or precursor thereof under reaction conditions to form a polyaminopolymer having halohydrin or dihalo functionality; and crosslinking the polyaminopolymer by either or both: (h), after step (b) and before step (c), contacting the polyaminopolymer with a crosslinking agent therefor having at least two functional groups reactive with amine groups under reaction conditions to form a crosslinked polyaminopolymer; or (d), after step (c) raising the pH of the polyaminopolymer having halohyrin or vicinal dihalo functionality sufficiently to cause an increase in molecular weight.
Claim 3
Dependent Claim
12 words
The process of claim 1 wherein the polyaminopolymer is soluble in water.
Claim 4
Dependent Claim
20 words
The process of claim 2 wherein step (b) additionally comprises contacting the adduct and polyfunctional compound with a saturated polyamine.
Claim 5
Dependent Claim
21 words
The process of claim 3 wherein the mole ratio of adduct to saturated polyamine is from about 100:0 to about 70:30.
Claim 6
Dependent Claim
25 words
The process of claim 4 wherein in step (a) the mole ratio of polyfunctional amine to alkylating agent is from about 10:1 to about 1:10.
Claim 7
Dependent Claim
13 words
The process of claim 2 wherein the alkylating agent is an organic chloride.
Claim 8
Dependent Claim
30 words
The process of claim 5 wherein the alkylating agent is allyl chloride, allyl bromide, allyl iodide, 1-chloro-3-butene, 2-chloro-3-butene, 1-chloro-4-pentene, 2-chloro-4-pentene, 3-chloro-4-pentene, 1-chloro-2-butene, 1-chloro-2-pentene, 1-chloro-3-pentene, 3,3-dichloropropene, 3,3,3-trichloropropene, 1,3-dichloropropene, 1,2,3-trichloropropene or 1,1,3-trichloropropene.
Claim 9
Dependent Claim
20 words
The process of claim 2 wherein the polyfunctional amine is an alkanolamine, polyethylene polyamine, polypropylene polyamine, polybutylene polyamine, or hexamethylenediamine.
Claim 10
Dependent Claim
50 words
The process of claim 8 wherein the polyfunctional amine is diethylenetriamine, bis-2-hydroxyethyl ethylenediamine, triethylenetetraamine, tetraethylenepentamine, pentaethylenehexamine, hexaethyleneheptamine, aminoethylpiperazine, hydroxyethylpiperazine, aminoethylethanolamine, bis(3-aminopropyl)ethylenediamine, bis(3-aminoethyl)-1,3-diaminopropane, n,n-dimethyldiethylenetriamine, tris(2-aminoethyl)amine, polyethyleneimine, branched, a cyclic isomer or congener, of said amines or a polyethylene polyamine having an average molecular wight of from about 200 to about 500.
Claim 11
Dependent Claim
18 words
The process of claim 9 wherein the polyfunctional amine is diethylenetriamine and the alkylating agent is allyl chloride.
Claim 12
Dependent Claim
66 words
The process of claim 2 wherein the polyfunctional amine has more than one amine group, independently selected form primary of secondary amine groups, or amine groups which differ in their pK b 's by at least about 2 units, and at least one amine group is blocked under reaction conditions to form a selective reaction product of the ethylenically unsaturated alkylating agent and an amine group.
Claim 13
Dependent Claim
31 words
The process of claim 11 wherein the pH is adjusted to from about 4 to about 9 such that the ethylenically unsaturated alkylating agent reacts selectively agent and an amine group.
Claim 14
Dependent Claim
15 words
The process of claim 11 wherein the preselected amine group is a secondary amine group.
Claim 15
Dependent Claim
24 words
The process of claim 2 wherein in step (b) the mole ratio of adduct to polyfunctional compound is from about 0.6 to about 1.4.
Claim 16
Dependent Claim
36 words
The process of claim 14 wherein in step (b) the polyfunctional compound has at least 2 reactive groups which are independently carboxylic acid, carboxylic ester, acyl halide, a, β-ethylenically unsaturated acid, or a,β-ethylenically unsaturated ester groups.
Claim 17
Dependent Claim
27 words
The process of claim 15 wherein the polyfunctional compound is diglycolic acid or a saturated aliphatic dicarboxylic acid having from about 3 to about 8 carbon atoms.
Claim 18
Dependent Claim
26 words
The process of claim 15 wherein the polyfunctional compound is adipic acid, succinic acid, oxalic acid, glutaric acid, pimelic acid, suberic acid, azelaic acid, sebacic acid.
Claim 19
Dependent Claim
31 words
The process of claim 2 wherein in step (c) the equivalents of halogen, hypohalous acid or precursor thereof is from about 90 to about 110 percent of the equivalents of polyaminopolymer.
Claim 20
Dependent Claim
40 words
The process of claim 17 wherein step (c) comprises contacting the polyaminopolymer with a halogen, hypohalous acid or precursor thereof at a pH of less than about 3 under reaction conditions to form a polyaminopolymer having halohydrin or dihalo functionality.
Claim 21
Dependent Claim
20 words
The process of claim 2 wherein in step (d) the pH is raised to from about 5 to about 8.
Claim 22
Dependent Claim
39 words
The process of claim 2 comprising an additional step (e) between steps (b) and (c) of lowering the pH of the solution of polyaminopolymer having halohydrin or dihalo functionality to a pH of from about 1 to about 3.
Claim 23
Dependent Claim
24 words
The process of claim 21 wherein step (e) comprises adding an acid selected from the group consisting of hydrochloric, nitric, sulfuric, formic and perchloric.
Claim 24
Dependent Claim
10 words
The process of claim 22 wherein the acid is hydrochloric.
Claim 25
Dependent Claim
29 words
The process of claim 2 comprising an additional step (f) after step (b) of reacting the polyaminopolymer with an alkylating agent under reaction conditions to form quaternary amine groups.
Claim 26
Dependent Claim
35 words
The process of claim 24 wherein the alkylating agent is methyl iodide, dimethyl carbonate, trimethyloxonium tetrafluoroborate, triethyloxonium tetrafluoroborate, methyltosylate, ethyl tosylate, dimethyl sulfate, diethyl sulfate, ethyl iodide, methyl bromide, ethyl bromide or a mixture thereof.
Claim 27
Dependent Claim
43 words
The process of claim 2 comprising an additional step (g) after step (b) of reacting the polyaminopolymer with a compound having a quaternary amine group and a group reactive with the polyaminopolymer under reaction conditions to introduce quaternary amine groups onto the polyaminopolymer.
Claim 28
Dependent Claim
17 words
The process of claim 26 wherein the compound is glycidyltrimethylammonium chloride, (2-bromoethyl)trimethylammonium chloride or bromide, (2-chloroethyl)trimethylammonium chloride.
Claim 29
Dependent Claim
21 words
The process of claim 1 wherein after step (a) the amine/unsaturated alkylating agent adduct is purified to remove unreacted alkylating agent.
Claim 30
Dependent Claim
38 words
The process of claim 1 wherein in step (h) the crosslinking agent is an alkyl compound having from 2 to about 6 carbon atoms and at least 2 halogen atoms selected from bromine or chlorine or mixtures thereof.
Claim 31
Dependent Claim
29 words
The process of claim 29 wherein the crosslinking agent is selected from 1,2-dichloroethane, succinyl chloride, malonyl chloride, 1,3-dichloropropane or 1,3-dibromopropane, 1,3-dibromopropane; 1,2-dibromoethane, succinyl bromide, malonyl bromide, or mixtures thereof.
Claim 32
Dependent Claim
33 words
The process of claim 29 wherein the crosslinking agent is contacted in an amount sufficient to produce from about 3 to about 18 percent crosslinking based on secondary amine groups in the polymer.
Claim 33
Dependent Claim
23 words
The process of claim 2 additionally comprising a step (j) drying the resulting polyaminopolymer to less than about 20 percent by weight water.
Claim 34
Dependent Claim
19 words
The process of claim 32 wherein step (j) comprises heating the polyaminopolymer to about 10 percent by weight water.
Claim 35
Dependent Claim
15 words
The process of claim 32 additionally comprising a step (k) dissolving the polyaminopolymer in water.
Claim 36
Dependent Claim
142 words
A water soluble polyaminopolymer prepared by a process comprising the steps of (a) contacting a polyfunctional amine with an ethylenically unsaturated alkylating agent under reaction conditions to form an amine/ethylenically unsaturated alkylating agent adduct; (b) contacting the adduct with a polyfunctional compound under reaction conditions to form a polyaminopolymer; (c) contacting the polyaminopolymer with a halogen, hypohalous acid or precursor thereof under reaction conditions to form a polyaminopolymer having halohydrin or dihalo functionality; and crosslinking the polyaminopolymer by either or both of: (h) after step (b) and before step (c), contacting the polyaminopolymer with a crosslinking agent therefor having at least two functional groups reactive with amine groups therefor having at least two functional groups reactive with amine (d), after step (c), raising the pH of the polyaminopolymer having halohydrin or vicinal dihalo functionality sufficiently to cause an increase in molecular weight.
Claim 37
Dependent Claim
142 words
A water soluble polyaminopolymer prepared by a process comprising the steps of (a) contacting a polyfunctional amine with an ethylenically unsaturated alkylating agent under reaction conditions to form an amine/ethylenically unsaturated alkylating agent adduct; (b) contacting the adduct with a polyfunctional compound under reaction conditions to form a polyaminopolymer; (c) contacting the polyaminopolymer with a halogen, hypohalous acid or precursor thereof under reaction conditions to form a polyaminopolymer having halohydrin or dihalo functionality; and crosslinking the polyaminopolymer by either or both of: (h) after step (b) and before step (c), contacting the polyaminopolymer with a crosslinking agent therefor having at least two functional groups reactive with amine groups therefor having at least two functional groups reactive with amine (d), after step (c), raising the pH of the polyaminopolymer having halohydrin or vicinal dihalo functionality sufficiently to cause an increase in molecular weight.
Claim 38
Dependent Claim
17 words
The polyaminopolymer of claim 35 wherein the adduct prepared in step (a) is purified before step (b).
Claim 39
Dependent Claim
22 words
The polyaminopolymer of claim 36 wherein, in step (b), contacting of the adduct and polyfunctional compound is additionally with a saturated polyamine.
Claim 40
Dependent Claim
76 words
The polyaminopolymer of claim 35 wherein the alkylating agent is allyl chloride, allyl bromide, allyl iodide, 1-chloro-3-butene, 2-chloro-3-butene, 1-chloro-4-pentene, 2-chloro-4-pentene, 3-chloro-4-pentene, 1-chloro-2-butene, 1-chloro-2-pentene, 1-chloro-3-pentene, 3,3-dichloropropene, 3,3,3-trichloropropene, 1,3-dichloropropene, 1,2,3-tirchloropropene or 1,1,3-trichloropropene and the polyfunctional amine is diethylenetriamine, bis-2-hydroxyethyl ethylenediamine, triethylenetetraamine, tetraethylenepentamine, pentaethylenehexamine, hexaethyleneheptamine, aminoethylpiperazine, hydroxyethylpiperazine, aminoethylethanolamine, bis(3-aminopropyl)ethylenediamine, bis(3-aminoethyl)-1,3-diaminopropane, n,n-dimethyldiethylenetriamine, tris-(2-aminoethyl)amine, polyethyleneimine, a branched or cyclic isomer or congener of said amines, or a polyethylene polyamine having an average molecular weight of from about 200 to about 500.
Claim 41
Dependent Claim
27 words
The polyaminopolmyer of claim 35 wherein the polyaminopolymer is contacted with hypochlorus acid, and in step (c) contacting is at a pH of less than about 3.
Claim 42
Dependent Claim
20 words
The polyaminopolymer of claim 39 wherein step (b) additionally comprises contacting the adduct and polyfunctional compound with a saturated polyamine.
Claim 43
Dependent Claim
21 words
The polyaminopolymer of claim 40 wherein the mole ratio of adduct to saturated polyamine is from about 100:0 to about 70:30.
Claim 44
Dependent Claim
65 words
The polyaminopolymer of claim 35 wherein the polyfunctional amine has more than one amine group, selected from primary and secondary amine groups and amine groups which differ in their pK b 's by at least about 2 units, and at least one amine group is blocked under reaction conditions to form a selective reaction product of the ethylenically unsaturated alkylating agent a preselected amine group.
Claim 45
Dependent Claim
33 words
The polyaminopolymer of claim 35 prepared by a process additionally comprising a step (f) after step (b) of reacting the polyaminopolymer with an alkylating agent under reaction conditions to form quaternary amine groups.
Claim 46
Dependent Claim
34 words
The polyaminopolymer of claim 43 wherein the alkylating agent is methyl iodide, dimethyl carbonate, trimethyloxonium tetrafluoroborate, triethyloxonium tetrafluoroborate, methyltosylate, ethyl tosylate, diethyl sulfate, dimethyl sulfate, ethyl iodide, methyl bromide, ethyl bromide or mixtures thereof.
Claim 47
Dependent Claim
47 words
The polyaminopolymer of claim 35 prepared by a process comprising an additional step (g) after step (b) of reacting the polyaminopolymer with a compound having a quaternary amine group and a group reactive with the polyaminopolymer under reaction conditions to introduce quaternary amine groups onto the polyaminopolymer.
Claim 48
Dependent Claim
17 words
The polyaminopolymer of claim 45 wherein the compound is glycidyltrimethylammonium chloride, (2-bromoethyl)trimethylammonium chloride or bromide, (2-chloroethyl)trimethylammonium chloride.
Claim 49
Dependent Claim
27 words
The polyaminopolymer of claim 35 prepared by a process additionally comprising a step (j) drying the resulting polyaminopolymer to less than about 20 percent by weight water.
Claim 50
Dependent Claim
19 words
The polyaminopolymer of claim 47 prepared by a process additionally comprising a step (k) dissolving the polyaminopolymer in water.
References Cited (Backward Citations)
US3058873A
Cited
US3051751A
Cited
US3240761A
Cited
US3197427A
Cited
US3532751A
Cited
US3565941A
Cited
US3578400A
Cited
US3845145A
Cited
US3558501A
Cited
US3634523A
Cited
US3947383A
Cited
US4172840A
Cited
US4096133A
Cited
US4287110A
Cited
US4336835A
Cited
US4410714A
Cited
US4354006A
Cited
US4419500A
Cited
US4419498A
Cited
GB2092150A
Cited
US4481092A
Cited
US4520159A
Cited
US5110878A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-01-10 | 1997-07-12 | 1998-01-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-01-10 | 2001-07-12 | 2002-01-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-01-10 | 2005-07-12 | 2006-01-11 | $7700.00 | Window Closed / Lapsed |