Adhesive tapes
Assignee: Tomoegawa Co Ltd
•
Filing: 1991-12-23
•
Granted: 1994-01-11
•
Expires: 2011-12-23
Abstract
Abstract An adhesive tape for electronic parts, comprising (a) a heat resistant base film, and (b) an adhesive layer laminated on at least one surface of said base film, said adhesive layer comprising (i) a resol type phenol resin, and (ii) an acrylonitrile/butadiene copolymer, in a proportion of from 100 to 500 parts by weight of said resol type phenol resin per 100 parts by weight of said acrylonitrile/butadiene copolymer, said resol type phenol resin being selected from the group consisting of bisphenol A type resins, alkylphenol type resins, phenol type resins and their co-condensed type phenol resins which contain as the phenol component at least one member selected from the group consisting of bisphenol A, alkylphenols and phenol.
Inventors
- 👤 Yukinori Sakumoto
- 👤 Shigeyuki Yokoyama
- 👤 Akihiro Shibuya
- 👤 Atsushi Koshimura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 06:53
CPC Classifications
H; H10; H10W; H10W70/00; H10W70/40; H10W70/421; H10W70/435; C; C09; C09J; C09J109/00; C09J109/02; C09J161/00; C09J161/04; C09J161/06; C09J7/00; C09J7/20; C09J7/22; C09J7/25; C09J7/30; C09J7/38; C08; C08L; C08L2666/00; C08L2666/02; C08L2666/14; C08L2666/16; C08L79/00; C08L79/04; C08L79/08; C08L9/00; C08L9/02; C09J2301/00; C09J2301/10; C09J2301/12; C09J2301/122; C09J2479/00; C09J2479/08; C09J2479/086; Y; Y10; Y10T; Y10T428/00; Y10T428/28; Y10T428/2848; Y10T428/2852; Y10T428/2874; Y10T428/2878; Y10T428/2887; Y10T428/31504; Y10T428/31721
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
150 words
An adhesive tape for electronic parts, comprising: (a) a heat resistant base film, and (b) an adhesive layer laminated on at least one surface of said base film, said adhesive layer comprising (i) a resol phenol resin, and (ii) an acrylonitrile/butadiene copolymer, in a proportion of from 100 to 500 parts by weight of said resol phenol resin per 100 parts by weight of acrylonitrile/butadiene copolymer, said resol phenol resin being selected from the group consisting of bisphenol A resins, alkyl-phenol resins, phenol resins and their co-condensed phenol resins which contains as the phenol component at least one member selected from the group consisting of bisphenol A alkylphenols and phenol, the copolymer having a number average molecular weight (MN) of from 20,000 to 200,000, a ratio of a weight average molecular weight (MW) of said acrylonitrile/butadiene co-polymer to said number average molecular weight (MN) being in a range of MW/MN≧2.5.
Claim 2
Dependent Claim
150 words
An adhesive tape for electronic parts, comprising: (a) a heat resistant base film, and (b) an adhesive layer laminated on at least one surface of said base film, said adhesive layer comprising (i) a resol phenol resin, and (ii) an acrylonitrile/butadiene copolymer, in a proportion of from 100 to 500 parts by weight of said resol phenol resin per 100 parts by weight of acrylonitrile/butadiene copolymer, said resol phenol resin being selected from the group consisting of bisphenol A resins, alkyl-phenol resins, phenol resins and their co-condensed phenol resins which contains as the phenol component at least one member selected from the group consisting of bisphenol A alkylphenols and phenol, the copolymer having a number average molecular weight (MN) of from 20,000 to 200,000, a ratio of a weight average molecular weight (MW) of said acrylonitrile/butadiene co-polymer to said number average molecular weight (MN) being in a range of MW/MN≧2.5.
Claim 3
Dependent Claim
53 words
An adhesive tape as claimed in claim 1, wherein said adhesive layer is laminated on only one surface of said heat resistant base film so that when an extract of said adhesive tape is obtained, said extract contains organic and inorganic ionic impurities which provide an electric conductivity of at most 70 μs/cm.
Claim 4
Dependent Claim
24 words
An adhesive tape as claimed in claim 1, wherein said adhesive tape contains sulfate ions in a concentration of not higher than 300 ppm.
Claim 5
Dependent Claim
58 words
An adhesive tape as claimed in claim 1, wherein said adhesive layer is laminated on one surface of said heat resistant base film and when the other surface of said heat resistant base film is bonded to a molding compound, the adhesive tape has an adhesion strength of not lower than 200 g/1.5 cm upon 180° peeling test.
Claim 6
Dependent Claim
76 words
An adhesive tape as claimed in claim 1, wherein said heat resistant base film has an average coefficient of linear thermal expansion along the width thereof at from 20° to 300° C. (as measured according to ASTM D-696-44) of from 0.4×10 -5 to 2.5×10 -5 cm/cm/° C. and a coefficient of dimensional change along the width thereof after heating at 300° C. for 3 minutes (as measured according to JIS C2318-6.3.5) being not higher than 0.15%.
Claim 7
Dependent Claim
48 words
An adhesive tape as claimed in claim 5, wherein said adhesive layer contains at least one filler selected from the group consisting of an inorganic filler and an organic filler in an amount of from 0.5 to 80% by weight based on the weight of said adhesive layer.
References Cited (Backward Citations)
US3917554A
Cited
US3873638A
Cited
US3837984A
Cited
US3784496A
Cited
US4212912A
Cited
US4435543A
Cited
GB2070460A
Cited
US4578315A
Cited
US4977003A
Cited
US4762747A
Cited
US4892602A
Cited
US4861648A
Cited
US5118567A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-01-10 | 1997-07-12 | 1998-01-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-01-10 | 2001-07-12 | 2002-01-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-01-10 | 2005-07-12 | 2006-01-11 | $7700.00 | Window Closed / Lapsed |