US5273789A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of treating surface of molded article of polypropylene resin and method of coating said molded article with paint
Assignee: Sumitomo Chemical Co Ltd
•
Filing: 1992-08-07
•
Granted: 1993-12-28
•
Expires: 2012-08-07
Abstract
Abstract The present invention provides a method which enables the surface of a molded article of a polypropylene resin to be modified to a surface suitable for coating, bonding, printing, etc. A molded article of a polypropylene resin comprising polypropylene, an ethylene-propylene copolymer rubber and an ethylene-acrylic acid or ethylene-methacrylic acid copolymer and optionally a filler is irradiated in the air with a light from a synthetic quartz low pressure mercury lamp having an output of 200 W for 60 sec with the distance between the surface of the molded article and the lamp being kept at about 10 cm.
Inventors
- 👤 Hideo Shinonaga
- 👤 Satoru Sogabe
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 14:47
CPC Classifications
C; C08; C08J; C08J7/00; C08J7/12; C08J7/123; B; B05; B05D; B05D3/00; B05D3/06; B05D3/061; B05D3/062; B05D3/063; B29; B29C; B29C59/00; B29C59/005; C08L; C08L23/00; C08L23/02; C08L23/04; C08L23/08; C08L23/0846; C08L23/0869; C08L23/10; C08L23/14; C08L23/142; C08L53/00; B29C35/00; B29C35/02; B29C35/08; B29C35/0805; B29C2035/0827; B29K; B29K2023/00; B29K2023/10; B29K2023/12; B29K2105/00; B29K2105/0085; C08L2205/00; C08L2205/03; C08L23/16
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
311 words
A method of treating the surface of a molded article of a polypropylene resin, comprising a step of irradiating a molded article of a resin composition with ultraviolet rays having an irradiation wavelength in a region of 300 nm or less, said resin composition comprising (A) 10 to 90 parts by weight of at least one polypropylene selected from (a) a homopolypropylene having a melt index of 10 to 100 g/10 min, (b) a propylene-α-olefin random copolymer having a content of an α-olefin having 1 to 6 carbon atoms (exclusive of 3 carbon atoms) in the range of from 0.5 to 8% by weight and a melt index of 10 to 100 g/10 min, (c) a propylene-ethylene block copolymer having an ethylene content of 2 to 15% by weight and a melt index of 10 to 100 g/10 min, the propylene-ethylene copolymer portion having an ethylene content of 20 to 60% by weight and an intrinsic viscosity of 2 to 10 dl/g as measured in a tetralin solution at 135° C., and (d) a modified polypropylene including polypropylene modified by grafting an unsaturated carboxylic acid or its anhydride in an amount in the range of from 0.05 to 20% by weight onto the polypropylene; (B) 5 to 50 parts by weight of an ethylene-propylene copolymer rubber having a propylene content of 10 to 70% by weight and a Mooney viscosity (ML 1+4 100° C.) of 10 to 100, (C) 3 to 60 parts by weight of an ethylene-acrylic acid copolymer resin or ethylene-methacrylic acid copolymer resin having an ethylene content of 50 to 95% by weight, and 0 to 40 parts by weight, based on 100 parts by weight of the composition comprising (A) propylene, (B) the ethylene-propylene copolymer rubber and (C) the copolymer resin, of a filler comprising one of or both of an inorganic filler and a glass fiber.
Claim 2
Independent Claim
311 words
A method of treating the surface of a molded article of a polypropylene resin, comprising a step of irradiating a molded article of a resin composition with ultraviolet rays having an irradiation wavelength in a region of 300 nm or less, said resin composition comprising (A) 10 to 90 parts by weight of at least one polypropylene selected from (a) a homopolypropylene having a melt index of 10 to 100 g/10 min, (b) a propylene-α-olefin random copolymer having a content of an α-olefin having 1 to 6 carbon atoms (exclusive of 3 carbon atoms) in the range of from 0.5 to 8% by weight and a melt index of 10 to 100 g/10 min, (c) a propylene-ethylene block copolymer having an ethylene content of 2 to 15% by weight and a melt index of 10 to 100 g/10 min, the propylene-ethylene copolymer portion having an ethylene content of 20 to 60% by weight and an intrinsic viscosity of 2 to 10 dl/g as measured in a tetralin solution at 135° C., and (d) a modified polypropylene including polypropylene modified by grafting an unsaturated carboxylic acid or its anhydride in an amount in the range of from 0.05 to 20% by weight onto the polypropylene; (B) 5 to 50 parts by weight of an ethylene-propylene copolymer rubber having a propylene content of 10 to 70% by weight and a Mooney viscosity (ML 1+4 100° C.) of 10 to 100, (C) 3 to 60 parts by weight of an ethylene-acrylic acid copolymer resin or ethylene-methacrylic acid copolymer resin having an ethylene content of 50 to 95% by weight, and 0 to 40 parts by weight, based on 100 parts by weight of the composition comprising (A) propylene, (B) the ethylene-propylene copolymer rubber and (C) the copolymer resin, of a filler comprising one of or both of an inorganic filler and a glass fiber.
Claim 3
Dependent Claim
89 words
A method of treating the surface of a molded article of a polypropylene resin according to claim 1, wherein said resin composition comprises (A) 10 to 60 parts by weight of the polypropylene, (B) 10 to 40 parts by weight of the ethylene-propylene copolymer rubber, (C) 30 to 60 parts by weight of the copolymer resin and 0 to 40 parts by weight, based on 100 parts by weight of the composition comprising (A) the polypropylene, (B) the ethylene-propylene copolymer rubber and (C) the copolymer resin, of the filler.
Claim 4
Dependent Claim
38 words
The method according to claim 1, wherein said modified polypropylene includes polypropylene modified by grafting an unsaturated carboxylic acid or its anhydride in an amount in the range of from 0.1 to 10% by weight onto the polypropylene.
Claim 5
Dependent Claim
34 words
The method according to claim 3, wherein said unsaturated carboxylic acid or its anhydride is selected from the group consisting of acrylic acid, methacrylic acid, maleic acid, itaconic acid, maleic anhydride, and itaconic anhydride.
Claim 6
Dependent Claim
41 words
The method according to claim 1, wherein said ethylene-acrylic acid copolymer resin or ethylene-methacrylic acid copolymer resin is selected from the group consisting of ethylene-acrylic acid copolymer resin, ethylene-acrylic ester copolymer resin, ethylene-methacrylic acid copolymer resin, and ethylene-methacrylic ester copolymer resin.
Claim 7
Dependent Claim
83 words
The method according to claim 5, wherein said acrylic ester is selected from the group consisting of methyl acrylate, ethyl acrylate, i-propyl acrylate, t-butyl acrylate, glycidyl acrylate, dimethylaminomethyl acrylate, dimethylaminoethyl acrylate, dimethylamino-i-propyl acrylate, dimethylamino-t-butyl acrylate, diethylaminomethyl acrylate, diethylamino ethyl acrylate, diethylamino-i-propyl acrylate, and diethylamino-t-butyl acrylate and said methacrylic ester is selected from the group consisting of methyl methacrylate, ethyl methacrylate, i-propyl methacrylate, t-butyl methacrylate, glycidyl methacrylate, dimethylaminomethyl methacrylate, dimethylaminoethyl methacrylate, dimethylamino-i-propyl methacrylate, dimethylamino-t-butyl methacrylate, diethylaminomethyl methacrylate, diethylaminoethyl methacrylate, diethylamino-i-propyl methacrylate, and diethylamino-t-butyl methacrylate.
Claim 8
Dependent Claim
26 words
The method according to claim 1, wherein said molded article is degreased prior to the irradiation of the surface of the molded article with ultraviolet rays.
Claim 9
Dependent Claim
30 words
The method according to claim 1, wherein said molded article is degreased using a solvent selected from the group consisting of water, an aqueous solution of an alkali, and alcohols.
Claim 10
Independent Claim
316 words
A method of coating a molded article of a polypropylene resin, comprising steps of irradiating a molded article of a resin composition with ultraviolet rays having an irradiation wavelength in a region of 300 nm or less said resin composition comprising (A) 10 to 90 parts by weight of at least one polypropylene selected from (a) a homopolypropylene having a melt index of 10 to 100 g/10 min, (b) a propylene-α-olefin random copolymer having a content of an α-olefin having 1 to 6 carbon atoms (exclusive of 3 carbon atoms) in the range of from 0.5 to 8% by weight and a melt index of 10 to 100 g/10 min, (c) a propylene-ethylene block copolymer having an ethylene content of 2 to 15% by weight and a melt index of 10 to 100 g/10 min, the propylene-ethylene copolymer portion having an ethylene content of 20 to 60% by weight and an intrinsic viscosity of 2 to 10 dl/g as measured in a tetralin solution at 135 C., and (d) a modified polypropylene including polypropylene modified by grafting an unsaturated carboxylic acid or its anhydride in an amount in the range of from 0.05 to 20% by weight onto the polypropylene; (B) 5 to 50 parts by weight of an ethylene-propylene copolymer rubber having a propylene content of 10 to 70% by weight and a Mooney viscosity (ML 1+4 , 100 C.) of 10 to 100, (C) 3 to 60 parts by weight of an ethylene-acrylic acid copolymer resin or ethylene-methacrylic acid copolymer resin having an ethylene content of 50 to 95% by weight, and 0to 40 parts by weight, based on 100 parts by weight of the composition comprising (A) propylene, (B) the ethylene-propylene copolymer rubber and (C) the copolymer resin, of a filler comprising one of or both of an inorganic filler and a glass fiber; and coating the irradiated molded article with a paint.
Claim 11
Independent Claim
316 words
A method of coating a molded article of a polypropylene resin, comprising steps of irradiating a molded article of a resin composition with ultraviolet rays having an irradiation wavelength in a region of 300 nm or less said resin composition comprising (A) 10 to 90 parts by weight of at least one polypropylene selected from (a) a homopolypropylene having a melt index of 10 to 100 g/10 min, (b) a propylene-α-olefin random copolymer having a content of an α-olefin having 1 to 6 carbon atoms (exclusive of 3 carbon atoms) in the range of from 0.5 to 8% by weight and a melt index of 10 to 100 g/10 min, (c) a propylene-ethylene block copolymer having an ethylene content of 2 to 15% by weight and a melt index of 10 to 100 g/10 min, the propylene-ethylene copolymer portion having an ethylene content of 20 to 60% by weight and an intrinsic viscosity of 2 to 10 dl/g as measured in a tetralin solution at 135 C., and (d) a modified polypropylene including polypropylene modified by grafting an unsaturated carboxylic acid or its anhydride in an amount in the range of from 0.05 to 20% by weight onto the polypropylene; (B) 5 to 50 parts by weight of an ethylene-propylene copolymer rubber having a propylene content of 10 to 70% by weight and a Mooney viscosity (ML 1+4 , 100 C.) of 10 to 100, (C) 3 to 60 parts by weight of an ethylene-acrylic acid copolymer resin or ethylene-methacrylic acid copolymer resin having an ethylene content of 50 to 95% by weight, and 0to 40 parts by weight, based on 100 parts by weight of the composition comprising (A) propylene, (B) the ethylene-propylene copolymer rubber and (C) the copolymer resin, of a filler comprising one of or both of an inorganic filler and a glass fiber; and coating the irradiated molded article with a paint.
Claim 12
Dependent Claim
86 words
A method of coating a molded article of a polypropylene resin according to claim 9, wherein said resin composition comprises (A) 10 to 60 parts by weight of the polypropylene, (B) 10 to 40 parts by weight of the ethylene-propylene copolymer rubber, (C) 30 to 60 parts by weight of the copolymer resin and 0 to 40 parts by weight, based on 100 parts by weight of the composition comprising (A) the polypropylene, (B) the ethylene-propylene copolymer rubber and (C) the copolymer resin, of the filler.
Claim 13
Dependent Claim
21 words
The method according to claim 9, wherein said molded article is coated with a paint prior to irradiation with ultraviolet rays.
Claim 14
Dependent Claim
22 words
The method according to claim 9, wherein said paint is selected from the group consisting of epoxy, polyester, acrylic, and urethane paints.
Claim 15
Dependent Claim
38 words
The method according to claim 9, wherein said modified polypropylene includes polypropylene modified by grafting an unsaturated carboxylic acid or its anhydride in an amount in the range of from 0.1 to 10% by weight onto the polypropylene.
Claim 16
Dependent Claim
34 words
The method according to claim 13, wherein said unsaturated carboxylic acid or its anhydride is selected from the group consisting of acrylic acid, methacrylic acid, maleic acid, itaconic acid, maleic anhydride, and itaconic anhydride.
Claim 17
Dependent Claim
41 words
The method according to claim 9, wherein said ethylene-acrylic acid copolymer resin or ethylene-methacrylic acid copolymer resin is selected from the group consisting of ethylene-acrylic acid copolymer resin, ethylene-acrylic ester copolymer resin, ethylene-methacrylic acid copolymer resin, and ethylene-methacrylic ester copolymer resin.
Claim 18
Dependent Claim
83 words
The method according to claim 15, wherein said acrylic ester is selected from the group consisting of methyl acrylate, ethyl acrylate, i-propyl acrylate, t-butyl acrylate, glycidyl acrylate, dimethylaminomethyl acrylate, dimethylaminoethyl acrylate, dimethylamino-i-propyl acrylate, dimethylamino-t-butyl acrylate, diethylaminomethyl acrylate, diethylamino ethyl acrylate, diethylamino-i-propyl acrylate, and diethylamino-t-butyl acrylate and said methacrylic ester is selected from the group consisting of methyl methacrylate, ethyl methacrylate, i-propyl methacrylate, t-butyl methacrylate, glycidyl methacrylate, dimethylaminomethyl methacrylate, dimethylaminoethyl methacrylate, dimethylamino-i-propyl methacrylate, dimethylamino-t-butyl methacrylate, diethylaminomethyl methacrylate, diethylaminoethyl methacrylate, diethylamino-i-propyl methacrylate, and diethylamino-t-butyl methacrylate.
Claim 19
Dependent Claim
26 words
The method according to claim 9, wherein said molded article is degreased prior to the irradiation of the surface of the molded article with ultraviolet rays.
Claim 20
Dependent Claim
30 words
The method according to claim 9, wherein said molded article is degreased using a solvent selected from the group consisting of water, an aqueous solution of an alkali, and alcohols.
References Cited (Backward Citations)
EP0032731A1
Cited
DE3831416A1
Cited
US5077082A
Cited
US5185188A
Cited
WO1991011483A1
Cited
WO1991011482A1
Cited
EP0466930A1
Cited
EP0471078A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-12-27 | 1997-06-28 | 1997-12-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-12-27 | 2001-06-28 | 2001-12-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-12-27 | 2005-06-28 | 2005-12-28 | $7700.00 | Window Closed / Lapsed |