US5268244A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Self-aligned phase shifter formation
Assignee: Taiwan Semiconductor Manufacturing Co TSMC Ltd
•
Filing: 1992-08-13
•
Granted: 1993-12-07
•
Expires: 2012-08-13
Abstract
Abstract The process of fabricating the phase-shifting photomask includes forming on a substrate a patterned metal layer having vertical and horizontal surfaces. A substantially uniform phase-shifting material is deposited over the patterned metal layer surfaces. The phase-shifting material anisotropically etched to substantially remove the material from the horizontal surfaces and to substantially leave in place the material on the vertical or sidewall surfaces of metal layer to form phase shifter sidewall structures on the vertical or sidewall surfaces to form the phase shifting photomask without use of photoresist lithography in the formation of the phase shifter sidewall structures.
Inventors
- 👤 Chue-San Yoo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 13:30
CPC Classifications
G; G03; G03F; G03F1/00; G03F1/26; G03F1/29
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
148 words
The process of fabricating a self-aligned phase-shifting photomask having a phase shifter sidewall structure with a thickness and a width dimension comprising: forming on a substrate a patterned metal layer having vertical and horizontal surfaces; wherein said thickness dimension (d) is determined by the height of said patterned metal layer and is equal to 0.5 L/(n-1) where L is the wavelength and n is the refractive index of material of said shifter sidewall structure; depositing a substantially uniform thickness layer of phase-shifting material over said patterned metal layer surfaces wherein said width dimension is determined from said uniform thickness layer; and anisotropically etching said phase-shifting material to substantially remove said material from said horizontal surfaces and to substantially leave in place said material on said vertical surfaces of said metal layer to form phase shifter sidewall structures on said vertical surfaces to form said self-aligned phase shifting photomask.
Claim 2
Dependent Claim
148 words
The process of fabricating a self-aligned phase-shifting photomask having a phase shifter sidewall structure with a thickness and a width dimension comprising: forming on a substrate a patterned metal layer having vertical and horizontal surfaces; wherein said thickness dimension (d) is determined by the height of said patterned metal layer and is equal to 0.5 L/(n-1) where L is the wavelength and n is the refractive index of material of said shifter sidewall structure; depositing a substantially uniform thickness layer of phase-shifting material over said patterned metal layer surfaces wherein said width dimension is determined from said uniform thickness layer; and anisotropically etching said phase-shifting material to substantially remove said material from said horizontal surfaces and to substantially leave in place said material on said vertical surfaces of said metal layer to form phase shifter sidewall structures on said vertical surfaces to form said self-aligned phase shifting photomask.
Claim 3
Dependent Claim
10 words
The process of claim 1 wherein said substrate is quartz.
Claim 4
Dependent Claim
16 words
The process of claim 1 wherein said metal layer is composed of chromium and chromium oxide.
Claim 5
Dependent Claim
16 words
The process of claim 3 wherein said chromium layer is between 800 and 1200 Angstroms thick.
Claim 6
Dependent Claim
17 words
The process of claim 3 wherein said chromium oxide layer is between 100 to 200 Angstroms thick.
Claim 7
Dependent Claim
16 words
The process of claim 1 wherein the thickness of said metal layer determines the shifting angle.
Claim 8
Dependent Claim
18 words
The process of claim 1 wherein the thickness of said metal layer is between 800 to 1500 Angstroms.
Claim 9
Dependent Claim
23 words
The process of claim 1 wherein said shifter material is silicon oxide having a deposited thickness of between about 300 to 1000 Angstroms.
Claim 10
Dependent Claim
23 words
The process of claim 1 wherein said shifter material is silicon nitride having a deposited thickness of between about 300 to 1000 Angstroms.
Claim 11
Dependent Claim
28 words
The process of claim 1 wherein the thickness of said shifter material is chosen so that it will be able to shift light by 180° of phase angle.
Claim 12
Dependent Claim
32 words
The process of claim 1 wherein the etch back conditions are 300-500 watts, 600-900 mTorr, 5-20 sccm CF 4 , 10-30 sccm CHF 3 , 300-600 sccm Ar, 0.5-1.0 cm electrode gap.
Claim 13
Dependent Claim
39 words
A projection printing phase shifter mask manufactured by the process of claim 1 wherein said patterned metal layer is chromium, said phase shifter material is an inorganic transparent and further comprising a chromium oxide layer on said chromium layer.
Claim 14
Dependent Claim
21 words
The mask of claim 12 wherein said phase shifter mask has a phase shifter material that is composed of silicon oxide.
Claim 15
Dependent Claim
21 words
The mask of claim 12 wherein said phase shifter mask has a phase shifter material that is composed of silicon nitride.
Claim 16
Dependent Claim
31 words
The mask of claim 12 wherein the vertical phase shifter dimension is between about 500 to 4000 Angstroms and the horizonal phase shifter dimension is between about 500 to 4000 Angstroms.
References Cited (Backward Citations)
US5045417A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-12-06 | 1997-06-07 | 1997-12-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-12-06 | 2001-06-07 | 2001-12-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-12-06 | 2005-06-07 | 2005-12-07 | $7700.00 | Window Closed / Lapsed |