Abstract
Abstract A wrapping film comprising at least an outer layer, an interlayer, and an inner layer in this order, (a) the wrapping film having a shear peel strength of 0.20 kg/cm 2 or more and a 180° peel strength of 8.0 g/50 mm or less, (b) the outer layer and the inner layer each being a polyolefin resin composition layer, (c) the interlayer being an aliphatic polyamide resin layer, (d) the wrapping film exhibiting a tensile elongation at break of 200% or less in the direction of film withdrawal and a tensile elongation at break of 80% or more in the direction perpendicular to the direction of film withdrawal, (e) the ratio of the tensile elongation at break in the direction of film withdrawal to that in the direction perpendicular to the direction of film withdrawal being in the range of 0.7 or less, and (f) the total thickness of the wrapping film being in the range of 40 μm or less, and the thickness of the interlayer is in the range of 10 to 90% of the total thickness of the wrapping film.
Inventors
- 👤 Toshio Fujii
- 👤 Toyomitsu Kondo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 00:18
CPC Classifications
B; B32; B32B; B32B27/00; B32B27/06; B32B27/08; B32B27/32; B32B27/34; B32B38/00; B32B38/0012; B32B2038/0028; B32B2307/00; B32B2307/50; B32B2307/54; B32B2377/00; B32B2439/00; B32B2439/70; B32B7/00; B32B7/04; B32B7/12; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24942; Y10T428/2495; Y10T428/31504; Y10T428/31725; Y10T428/3175; Y10T428/31757
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
108 words
A wrapping film comprising at least an outer layer, an interlayer, and an inner layer in this order, (a) said wrapping film having a shear peel strength of 0.40 kg/cm 2 or more and a 180° peel strength of 4.0 g/50 mm or less, (b) said outer layer and said inner layer each being a polyolefin resin composition layer, (c) said interlayer being an aliphatic polyamide resin layer, and (d) the total thickness of said wrapping film being in the range of 40 μm or less, and the thickness of said interlayer being in the range of 10 to 90% of the total thickness of said wrapping film.
Claim 2
Dependent Claim
108 words
A wrapping film comprising at least an outer layer, an interlayer, and an inner layer in this order, (a) said wrapping film having a shear peel strength of 0.40 kg/cm 2 or more and a 180° peel strength of 4.0 g/50 mm or less, (b) said outer layer and said inner layer each being a polyolefin resin composition layer, (c) said interlayer being an aliphatic polyamide resin layer, and (d) the total thickness of said wrapping film being in the range of 40 μm or less, and the thickness of said interlayer being in the range of 10 to 90% of the total thickness of said wrapping film.
Claim 3
Dependent Claim
23 words
A wrapping film as claimed in claim 1, wherein the content of (B) polybutene-1 or polyisobutylene is 5 to 20 parts by weight.
Claim 4
Dependent Claim
26 words
A wrapping film as claimed in claim 1, wherein the number-average molecular weight of (B) polybutene-1 or polyisobutylene is in the range of 400 to 3,000.
Claim 5
Dependent Claim
21 words
A wrapping film as claimed in claim 1, wherein the total thickness of said wrapping film is 2 to 30 μm.
Claim 6
Dependent Claim
43 words
A wrapping film as claimed in claim 1, wherein a polyolefin resin composition contained in said outer layer and said inner layer has a melt flow rate of 0.5 to 20 g/10 min., and a density of 0.89 to 0.91 g/cm 3 .
Claim 7
Dependent Claim
43 words
A wrapping film as claimed in claim 1, wherein said wrapping film is obtained by stretching a laminated film comprising said outer layer, said intermediate layer and said inner layer in the direction of film withdrawal by a factor of 2 to 4.5.
Claim 8
Dependent Claim
50 words
A wrapping film as claimed in claim 6, wherein said polyolefin resin composition contained in said outer layer and said inner layer is a polypropylene resin composition comprising (A) 100 parts by weight of a polypropylene resin and (B) 3 to 30 parts by weight of a polybutene-1 or polyisobutylene.
Claim 9
Dependent Claim
24 words
A wrapping film as claimed in claim 7, wherein the content of (B) of polybutene-1 or polyisobutylene is 5 to 20 parts by weight.
Claim 10
Dependent Claim
26 words
A wrapping film as claimed in claim 7, wherein the number-average molecular weight of (B) polybutene-1 or polyisobutylene is in the range of 400 to 3,000.
Claim 11
Dependent Claim
50 words
A wrapping film as claimed in claim 1, wherein said polyolefin resin composition contained in said outer layer and said inner layer is a polypropylene resin composition comprising (A) 100 parts by weight of a polypropylene resin and (B) 3 to 30 parts by weight of a polybutene-1 or polyisobutylene.
Claim 12
Dependent Claim
23 words
A wrapping film as claimed in claim 10, wherein the content of (B) polybutene-1 or polyisobutylene is 5 to 20 parts by weight.
Claim 13
Dependent Claim
26 words
A wrapping film as claimed in claim 10, wherein the number-average molecular weight of (B) polybutene-1 or polyisobutylene is in the range of 400 to 3,000.
Claim 14
Dependent Claim
62 words
A wrapping film as claimed in claim 6, wherein said polyolefin resin composition contained in said outer layer and said inner layer is a polypropylene resin composition comprising (A) 100 parts by weight of a polypropylene resin, (B) 3 to 30 parts by weight of a polybutene-1 or polyisobutylene, and (C) 0.2 to 5 parts by weight of a polyglycerin aliphatic ester.
Claim 15
Dependent Claim
23 words
A wrapping film as claimed in claim 13, wherein the content of (B) polybutene-1 or polyisobutylene is 5 to 20 parts by weight.
Claim 16
Dependent Claim
26 words
A wrapping film as claimed in claim 13, wherein the number-average molecular weight of (B) polybutene-1 or polyisobutylene is in the range of 400 to 3,000.
Claim 17
Dependent Claim
66 words
A wrapping film as claimed in claim 6, wherein said polyolefin resin composition contained in said outer layer and said inner layer is a polypropylene resin composition comprising (A) 100 parts by weight of a polypropylene resin, (B) 3 to 30 parts by weight of a polybutene-1 or polyisobutylene, and (C) 0.2 to 5 parts by weight of a monoglyceride containing a C 8-22 acyl group.
Claim 18
Dependent Claim
23 words
A wrapping film as claimed in claim 16, wherein the content of (B) polybutene-1 or polyisobutylene is 5 to 20 parts by weight.
Claim 19
Dependent Claim
26 words
A wrapping film as claimed in claim 16, wherein the number-average molecular weight of (B) polybutene-1 or polyisobutylene is in the range of 400 to 3,000.
Claim 20
Dependent Claim
157 words
A wrapping film comprising at least an outer layer, an interlayer, and an inner layer, in this order, (a) said wrapping film having a shear peel strength of 0.40 kg/cm 2 or more and a 180° peel strength of 4.0 g/50 mm or less, (b) said outer layer and said inner layer each being a polyolefin resin composition layer, wherein a polyolefin resin composition contained in said outer layer and said inner layer comprises (A) 100 parts by weight of a polypropylene resin, (B) 3 to 30 parts by weight of a polybutene-1 or polyisobutylene, and (C) 0.2 to 5 parts by weight of a polyglycerin aliphatic ester; (c) said interlayer being an aliphatic polyamide resin layer, and (d) the total thickness of said wrapping film being in the range of 40 μm or less, and the thickness of said interlayer being in the range of 10 to 90% of the total thickness of said wrapping film.
Claim 21
Dependent Claim
157 words
A wrapping film comprising at least an outer layer, an interlayer, and an inner layer, in this order, (a) said wrapping film having a shear peel strength of 0.40 kg/cm 2 or more and a 180° peel strength of 4.0 g/50 mm or less, (b) said outer layer and said inner layer each being a polyolefin resin composition layer, wherein a polyolefin resin composition contained in said outer layer and said inner layer comprises (A) 100 parts by weight of a polypropylene resin, (B) 3 to 30 parts by weight of a polybutene-1 or polyisobutylene, and (C) 0.2 to 5 parts by weight of a polyglycerin aliphatic ester; (c) said interlayer being an aliphatic polyamide resin layer, and (d) the total thickness of said wrapping film being in the range of 40 μm or less, and the thickness of said interlayer being in the range of 10 to 90% of the total thickness of said wrapping film.
Claim 22
Dependent Claim
161 words
A wrapping film comprising at least an outer layer, an interlayer, and an inner layer in this order, (a) said wrapping film having a shear peel strength of 0.40 kg/cm 2 or more and a 180° peel strength of 4.0 g/50 mm or less, (b) said outer layer and said inner layer each being a polyolefin resin composition layer, wherein a polyolefin resin composition contained in said outer layer and said inner layer comprises (A) 100 parts by weight of a polypropylene resin, (B) 3 to 30 parts by weight of a polybutene-1 or polyisobutylene, and (C) 0.2 to 5 parts by weight of a monoglyceride containing a C 8-22 acyl group; (c) said interlayer being an aliphatic polyamide resin layer, and (d) the total thickness of said wrapping film being in the range of 40 μm or less, and the thickness of said interlayer being in the range of 10 to 90% of the total thickness of said wrapping film.
Claim 23
Dependent Claim
161 words
A wrapping film comprising at least an outer layer, an interlayer, and an inner layer in this order, (a) said wrapping film having a shear peel strength of 0.40 kg/cm 2 or more and a 180° peel strength of 4.0 g/50 mm or less, (b) said outer layer and said inner layer each being a polyolefin resin composition layer, wherein a polyolefin resin composition contained in said outer layer and said inner layer comprises (A) 100 parts by weight of a polypropylene resin, (B) 3 to 30 parts by weight of a polybutene-1 or polyisobutylene, and (C) 0.2 to 5 parts by weight of a monoglyceride containing a C 8-22 acyl group; (c) said interlayer being an aliphatic polyamide resin layer, and (d) the total thickness of said wrapping film being in the range of 40 μm or less, and the thickness of said interlayer being in the range of 10 to 90% of the total thickness of said wrapping film.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-11-29 | 1997-05-31 | 1997-11-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-11-29 | 2001-05-31 | 2001-11-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-11-29 | 2005-05-31 | 2005-11-30 | $7700.00 | Window Closed / Lapsed |