Method for producing closed cell spherical porosity in spray formed metals
Assignee: United States Department of the Navy
•
Filing: 1992-08-11
•
Granted: 1993-11-30
•
Expires: 2012-08-11
Abstract
Abstract Metal and metal alloy preforms having closed cell, spherical porosity are spray formed at high deposition rates by introducing blowing agents into the thixotropic semisolid deposition layer, within which gas formed in thermal decomposition reactions are trapped. Density reductions of nearly 30% were generated in a phosphor bronze matrix, using barium carbonate as the blowing agent. Hollow glass particles were produced in the same matrix alloy by injection of microsphere precursor frit containing sulfur. A simple Newtonian heat transfer model of agent heating in the spray predicts agent/matrix compatibility. Along with modest improvements in damping capacity, tensile and compressive properties were found to be equal or superior to powder metallurgy product at the same porosity levels.
Inventors
- 👤 Paul Kelley
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 08:03
CPC Classifications
B; B22; B22F; B22F3/00; B22F3/10; B22F3/11; B22F3/1121; B22F3/1125; B22F3/115; C; C22; C22C; C22C1/00; C22C1/04; C22C1/05; C22C1/059; C22C1/10; C22C1/1036; C22C1/1042; C23; C23C; C23C4/00; C23C4/12; C23C4/123; F; F28; F28F; F28F13/00; F28F13/003; B22F3/1103; B22F2003/1106; B22F2998/00
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
122 words
A method for spray forming a preform on a substrate, said preform containing closed cell, spherical porosity for increased strength, comprising: A. heating a metallic material to obtain a melted metallic material having a selected superheat; B. passing said melted metallic material through a nozzle to form a melt stream; C. accelerating said melt stream toward said substrate with a stream of an inert gas to form an atomized melt stream at a point of atomization; D. injecting particles of a blowing agent into said point of atomization; E. receiving said atomized melt stream mixed with said blowing agent particles on said substrate to form said preform, wherein said superheat is sufficient to produce a thixotropic semisolid deposition layer on said preform.
Claim 2
Independent Claim
122 words
A method for spray forming a preform on a substrate, said preform containing closed cell, spherical porosity for increased strength, comprising: A. heating a metallic material to obtain a melted metallic material having a selected superheat; B. passing said melted metallic material through a nozzle to form a melt stream; C. accelerating said melt stream toward said substrate with a stream of an inert gas to form an atomized melt stream at a point of atomization; D. injecting particles of a blowing agent into said point of atomization; E. receiving said atomized melt stream mixed with said blowing agent particles on said substrate to form said preform, wherein said superheat is sufficient to produce a thixotropic semisolid deposition layer on said preform.
Claim 3
Dependent Claim
20 words
The method of claim 1, wherein said metallic material is selected from the group consisting of metals and metal alloys.
Claim 4
Dependent Claim
25 words
The method of claim 2, wherein said alloys are selected from the group consisting of copper based, nickel based, iron based, and aluminum based alloys.
Claim 5
Dependent Claim
39 words
The method of claim 1, wherein said blowing agent is selected from the group consisting of inorganic compounds, organic compounds, and elements having boiling temperatures, sublimation temperatures, or decomposition temperatures within the range of 425° C. and 1360° C.
Claim 6
Dependent Claim
98 words
The method of claim 4, wherein said inorganic compounds are selected from the group consisting of BaCO 3 , FeCO 3 , NiCO 3 , CdBr 2 , CeO 2 CO 3 , Cs 2 O 2 , GaCl 2 , PbBr 2 , MnSO 4 , K 2 Cr 2 O7, KCNS, RbBF 4 , Rb 2 CO 3 , AgNO 3 , NaClO 4 .H 2 O, TlBr, TlCl, TlF, TlI, ThI 4 , SnBr 2 , SnI 2 , Y 2 (SO 4 ) 3 .H 2 O, ZnBr 2 , and ZnI 4 .
Claim 7
Dependent Claim
23 words
The method of claim 4, wherein said organic compounds are selected from the group consisting of metal carbonyls, metal hydrides, an poly(alkylene carbonates).
Claim 8
Dependent Claim
25 words
The method of claim 4, wherein said elements are selected from the group consisting of arsenic, cadmium, cesium, potassium, rubidium, selenium, sodiu, sulfur, and zinc.
Claim 9
Dependent Claim
37 words
The method claim 1, wherein a majority fraction of said blowing agent particles collide with said atomized melt stream and are heated by conduction, the remainder of said blowing agent particles being heated by convection and radiation.
Claim 10
Dependent Claim
15 words
The method of claim 1, wherein said blowing agent particles decompose within said deposition layer.
Claim 11
Dependent Claim
26 words
The method of claim 9, wherein the viscosity of said deposition layer is sufficient to entrap gas pores formed by decomposition of said blowing agent particles.
Claim 12
Dependent Claim
25 words
The method of claim 10, wherein said preform contains closed, spherical pores, the majority thereof having diameters in the range of 100 to 250 microns.
Claim 13
Dependent Claim
33 words
The method of claim 1, wherein said blowing agent particles are BaCO 3 particles of -270 mesh in size and said atomized metal stream is phosphor bronze powder of -140 mesh in size.
Claim 14
Dependent Claim
37 words
The method of claim 12, wherein said BaCO 3 particles are mixed with said phosphor bronze powder as a carrier of said BaCO 3 particles to form a mixture which is injected into said point of atomization.
Claim 15
Dependent Claim
19 words
The method of claim 13, wherein said BaCO 3 particles are 0.44 to 8.8 weight percent of said mixture.
Claim 16
Dependent Claim
21 words
The method of claim 14, wherein the feed rate of said mixture is within the range of 0.5 and 1.5 kg/minute.
Claim 17
Dependent Claim
20 words
The method of claim 1, further comprising the step of controlling size and flow rate of said blowing agent particles.
Claim 18
Dependent Claim
25 words
The method of claim 1, further comprising the step of controlling time during which said blowing agent particles are injected into said point of atomization.
Claim 19
Dependent Claim
36 words
The method of claim 17, wherein said blowing agent particles are injected into said deposition layer only at the center of said preform, whereby only said center is porous and said preform has a sandwich structure.
References Cited (Backward Citations)
US2434775A
Cited
US2751289A
Cited
US3671221A
Cited
US3743353A
Cited
US3940262A
Cited
US4460529A
Cited
US4569821A
Cited
SU1073002A1
Cited
US4735862A
Cited
US4920084A
Cited
US5110631A
Cited
US5004710A
Cited
US4999182A
Cited
US4877705A
Cited
US4917852A
Cited
US5080672A
Cited
US5120567A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-11-29 | 1997-05-31 | 1997-11-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-11-29 | 2001-05-31 | 2001-11-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-11-29 | 2005-05-31 | 2005-11-30 | $7700.00 | Window Closed / Lapsed |