Method of making a molded applique product

Claim 1

A method of making applique products of the type made of synthetic resins and having printing thereon by a molding process to produce a three dimensional product having a shape including protruding portions or concave portions comprising the steps of: (1) providing a flat substrate having a minimum of 0.020 inches thickness, said substrate being made of a synthetic resin, (2) printing on a front surface of said substrate using a formable ink, (3) preparing the printed substrate for forming, (4) forming the printed substrate into a three dimensional shape having a front surface and a back surface, (5) providing a mold having a cavity including a mold surface of the same configuration as the front surface of said formed substrate, (6) preparing the formed substrate to have dimensions such that it fits into the mold cavity in a secure position with said front surface of said formed substrate in contact with said mold surface, (7) placing the formed substrate into the cavity of the mold in a secure position with said front surface of said formed substrate in contact with said mold surface and closing the mold in preparation for a molding operation, and, after the completion of steps (1) to (7), (8) injecting a molten resin into the cavity space located adjacent said back surface of said formed substrate at locations so the resin flows directly onto the formed substrate through a plurality of gates, said gates being constructed and arranged so that each gate does not supply molten resin to an area of the mold cavity greater than a predetermined area so as to reduce internal stress in the applique product produced, wherein step (4) is performed by a cold forming process to thereby reduce internal stress produced in the formed substrate, wherein step (6) of preparing the formed substrate is performed by die-cutting the formed substrate in a manner such that it is dimensioned to be placed into the mold with a minimal interference fit, wherein said flat substrate of step (1) is a clear polycarbonate and said molten resin of step (7) is made of a clear molten polycarbonate resin, wherein said formable ink is a high temperature ink that can withstand the stresses of the forming step as well as the heat from the injection of molten resin, wherein said mold surface is maintained at a temperature of 70°-110° F. and the molten resin temperature does not exceed 700° F., and wherein said molten resin is injected through gates directly onto and perpendicular to the back surface of the formed substrate placed in the mold in step (7).

Claim 2

A method of making applique products of the type made of synthetic resins and having printing thereon by a molding process to produce a three dimensional product having a shape including protruding portions or concave portions comprising the steps of: (1) providing a flat substrate having a minimum of 0.020 inches thickness, said substrate being made of a synthetic resin, (2) printing on a front surface of said substrate using a formable ink, (3) preparing the printed substrate for forming, (4) forming the printed substrate into a three dimensional shape having a front surface and a back surface, (5) providing a mold having a cavity including a mold surface of the same configuration as the front surface of said formed substrate, (6) preparing the formed substrate to have dimensions such that it fits into the mold cavity in a secure position with said front surface of said formed substrate in contact with said mold surface, (7) placing the formed substrate into the cavity of the mold in a secure position with said front surface of said formed substrate in contact with said mold surface and closing the mold in preparation for a molding operation, and, after the completion of steps (1) to (7), (8) injecting a molten resin into the cavity space located adjacent said back surface of said formed substrate at locations so the resin flows directly onto the formed substrate through a plurality of gates, said gates being constructed and arranged so that each gate does not supply molten resin to an area of the mold cavity greater than a predetermined area so as to reduce internal stress in the applique product produced, wherein step (4) is performed by a cold forming process to thereby reduce internal stress produced in the formed substrate, wherein step (6) of preparing the formed substrate is performed by die-cutting the formed substrate in a manner such that it is dimensioned to be placed into the mold with a minimal interference fit, wherein said flat substrate of step (1) is a clear polycarbonate and said molten resin of step (7) is made of a clear molten polycarbonate resin, wherein said formable ink is a high temperature ink that can withstand the stresses of the forming step as well as the heat from the injection of molten resin, wherein said mold surface is maintained at a temperature of 70°-110° F. and the molten resin temperature does not exceed 700° F., and wherein said molten resin is injected through gates directly onto and perpendicular to the back surface of the formed substrate placed in the mold in step (7).