Abstract
Abstract A process for manufacturing porous tubes made from carbon-carbon composite material by winding over a mandrel a non-woven sheet, made from a carbon fiber precursor, followed by compression and hot stabilisation of the assembly, with impregnation of the compressed sheet by a resin, followed by a thermal carbonisation treatment of the resin. Tubes are obtained having high permeability, small pore diameter and an inner surface of low rugosity. The tubes produced ar particularly suitable for the manufacture of filtration elements and of filtering membrane supports.
Inventors
- 👤 Jean Salem
- 👤 Christophe Bommier
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 02:25
CPC Classifications
B; B01; B01D; B01D39/00; B01D39/14; B01D39/20; B01D39/2055; B01D39/2065; B01D69/00; B01D69/10; B01D69/107; B01D69/1071; B01D71/00; B01D71/02; B01D71/021; C; C04; C04B; C04B38/00; C04B38/0022; B01D2239/00; B01D2239/04; B01D2239/0464; B01D2239/06; B01D2239/0604; B01D2239/0613; B01D2239/0618; B01D2239/065; B01D2239/069; B01D2239/0695; B01D2239/10; B01D2239/12; B01D2239/1225; B01D2239/1241; C04B2111/00; C04B2111/00474; C04B2111/00793; C04B2111/00801
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
238 words
Process for manufacturing a porous tube made from carbon-carbon composite material, which comprises winding a carbonaceous sheet to form a fibrous substrate having the shape of a tube followed by densification of this substrate to form a porous carbonaceous matrix, comprising the steps of: a) winding a non-woven sheet of carbon fibre precursor of apparent density between 0.005 and 0.05 over a rigid mandrel having a smooth surface and low rugosity and introducing the sheet, wound over its mandrel, into a flexible, sheath to hold the wound non-woven sheet tight; b) compressing the wound sheet with the aid of compression means wherein the thickness of the wound non-woven sheet is homothetically reduced in relation to the configuration of the outer surface of the mandrel to obtain a fibrous substrate, uniformly compressed on the mandrel, of apparent density between 0.2 and 0.6 and subjecting the wound sheet, during or after its compression, to a thermal treatment in order to solidify its structure in the form of a fibrous substrate profile, and optionally carbonising; c) impregnating the fibrous profile with a resin and polymerising the resin to obtain a rigid profile having a matrix of polymerised resin; and d) bringing the rigid profile to a temperature between 700° and 1300° C. in order to carbonise it to obtain a tube having high permeability, small pore diameter and an inner surface of low rugosity and apparent density between 0.5 and 1.2.
Claim 2
Dependent Claim
238 words
Process for manufacturing a porous tube made from carbon-carbon composite material, which comprises winding a carbonaceous sheet to form a fibrous substrate having the shape of a tube followed by densification of this substrate to form a porous carbonaceous matrix, comprising the steps of: a) winding a non-woven sheet of carbon fibre precursor of apparent density between 0.005 and 0.05 over a rigid mandrel having a smooth surface and low rugosity and introducing the sheet, wound over its mandrel, into a flexible, sheath to hold the wound non-woven sheet tight; b) compressing the wound sheet with the aid of compression means wherein the thickness of the wound non-woven sheet is homothetically reduced in relation to the configuration of the outer surface of the mandrel to obtain a fibrous substrate, uniformly compressed on the mandrel, of apparent density between 0.2 and 0.6 and subjecting the wound sheet, during or after its compression, to a thermal treatment in order to solidify its structure in the form of a fibrous substrate profile, and optionally carbonising; c) impregnating the fibrous profile with a resin and polymerising the resin to obtain a rigid profile having a matrix of polymerised resin; and d) bringing the rigid profile to a temperature between 700° and 1300° C. in order to carbonise it to obtain a tube having high permeability, small pore diameter and an inner surface of low rugosity and apparent density between 0.5 and 1.2.
Claim 3
Dependent Claim
28 words
Process according to claim 1, wherein in step a) the non-woven sheet of carbon fibre precursor is a mat sheet of carbon fibre precursor in the preoxidised state.
Claim 4
Dependent Claim
28 words
Process according to claim 2, wherein the said precursor mat is an entanglement of carbon fibre precursor segments, oriented randomly, of average length between 1 and 100 mm.
Claim 5
Dependent Claim
44 words
Process according to claim 1, wherein all or a portion of the said sheet contains a fine refractory inorganic filler of particulate size between 0.1 and 10 μm to modify the pore diameter of the final tube and to obtain an asymmetrical porous tube.
Claim 6
Dependent Claim
45 words
Process according to claim 4, wherein only a portion of the said sheet corresponding to the inner windings of the said tube contain a fine inorganic filler, to reduce the pore diameter over a low thickness and over the inner face of the said tube.
Claim 7
Dependent Claim
43 words
Process according to claim 1, wherein several mat sheets having different properties are wound over a mandrel to obtain an asymmetrical porous tube exhibiting successive layers having a pore diameter varying by a factor of 10 from one layer to the next layer.
Claim 8
Dependent Claim
67 words
Process according to claim 1, several sheets in the form of non-woven strips of small width made from mat having different properties and of small width are wound over a mandrel to obtain an asymmetrical porous tube exhibiting successive layers having a pore diameter varying by a factor of 10 from one layer to the next layer and which are formed from contiguous turns or with overlap.
Claim 9
Dependent Claim
36 words
Process according to claim 7, wherein several strips are wound over a mandrel, one half being alternately wound at an angle +α, the other half being wound at an angle -α, to obtain improved mechanical properties.
Claim 10
Dependent Claim
45 words
Process according to claim 1, wherein the mandrel is a profile of length which exceeds 1000 mm of any constant cross-section not comprising a concave portion so that the mandrel, over all points of its surface, is in contact with the sheet and supports it.
Claim 11
Dependent Claim
56 words
Process according to claim 9, in which the mandrel is selected from the group consisting of rods and tubes having circular cross-section of diameter between 1 and 50 mm, which mandrel is made from material selected from the group consisting of graphite, metal, metal alloy, PTFE, metal covered with PTFE, and metal alloy covered with PTFE.
Claim 12
Dependent Claim
18 words
Process according to claim 10, wherein the said mandrel is a rod or a tube made from copper.
Claim 13
Dependent Claim
38 words
Process according to claim 1, wherein the sheath is a woven braid made from carbon, having a variable cross-section depending on the traction force exerted on it, to prevent forming folds during the compression of the wound sheet.
Claim 14
Dependent Claim
17 words
Process according to claim 1, wherein the sheath is a braid made from natural or synthetic fibres.
Claim 15
Dependent Claim
60 words
Process according to claim 12, the sheath exhibits a wide, open mesh to hold tight the wound sheet whilst covering less than 30% of the surface of the wound sheet to make it possible to impregnate the compressed wound sheet with a resin without having to remove said sheath and to obtain a porous tube, optionally reinforced by said sheath.
Claim 16
Dependent Claim
43 words
Process according to claims 1, wherein the wound non-woven sheet is compressed, continuously and cold, and is introduced into a metal tube in which it is subjected to said thermal treatment at a temperature between 100° and 400° C., to solidify its structure.
Claim 17
Dependent Claim
41 words
Process according to claim 15, wherein the metal tube is integral with the compression means and is provided with heating means enabling the compressed wound sheet to be thermally treated to deliver, continuously, a fibrous substrate profile having a solidified texture.
Claim 18
Dependent Claim
34 words
Process according to claim 15, wherein the said metal tube containing the compressed wound sheet is placed in an oven for the thermal treatment and the metaltube is withdrawn in order to be re-used.
Claim 19
Dependent Claim
34 words
Process according to claim 1, wherein the wound non-woven sheet is compressed, continuously and hot, at a temperature between 200° and 500° C., to obtain directly a fibrous substrate profile having a solidified texture.
Claim 20
Dependent Claim
23 words
Process according to any one of claims 15 to 17, wherein the said compression means are constituted by a die made from PTFE.
Claim 21
Dependent Claim
41 words
Process according to claim 1, wherein the resin is a resin giving an amount of carbon greater than 30% after carbonisation, which resin is selected from the group consisting of phenolic resins, furan resins and pitch-furfural mixtures catalysed with ethyl sulphate.
Claim 22
Dependent Claim
38 words
Process according to claim 1, wherein the fibrous substrate profile having a solidified texture is continuously impregnated with resin and the resin is continuously polymerised, at least partially, in order to obtain profiles which can be easily handled.
Claim 23
Dependent Claim
80 words
Process according to claim 1, wherein the mandrel is a rod or a tube made from metal or metal alloy, in which the rigid profile provided with its mandrel is carbonised at a temperature between 700° and 1300° C. to decrease the rugosity of the inner surface of the porous tube by virtue of the relative greater expansion of the mandrel due to a difference in expansion coefficient between the mandrel and the rigid profile or the final porous tube.
References Cited (Backward Citations)
DE2722575A1
Cited
FR2488244A1
Cited
JPS6037664A
Cited
US4776995A
Cited
FR2582956A1
Cited
US4944996A
Cited
EP0237031A2
Cited
JPH01239061A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-11-22 | 1997-05-24 | 1997-11-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-11-22 | 2001-05-24 | 2001-11-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-11-22 | 2005-05-24 | 2005-11-23 | $7700.00 | Window Closed / Lapsed |