Fine grained BaTiO3 powder mixture and method for making
Assignee: MRA Laboratories Inc
•
Filing: 1992-07-27
•
Granted: 1993-11-02
•
Expires: 2012-07-27
Abstract
Abstract Disc and monolithic (multilayer) ceramic capacitors having a fine grained barium titanate body exhibit a high dielectric constant and a smooth (X7R) temperature coefficient of capacitance. The start ceramic materials for making such capacitors are predominantly spherical barium titanate powder particles of average particle size less than 0.7 micron and of narrow particle size distribution. The barium titanate is mixed with around 2 weight percent of a the cadmium silicate flux, 3Cd.SiO 2 , serving as a reactivity and sintering promoting agent; and about one weight percent of a reactivity and sintering inhibitor agent, Nb 2 O 5 . After preparing a green body of this mixture, the body is sintered at about 1100° C. A powder mixture for manufacture of such capacitors includes mixing powders of the three above-described materials, mildly sintering the powder mixture and if necessary comminuting the calcine to produce a ceramic powder of agglomerates of the start powders, each agglomerate having the same composition as did the precursor mixture. Low firing monolithic ceramic capacitors have been made with 70% Ag 30% Pd buried electrodes and with ten microns thick active ceramic dielectric layers having a dielectric constant (K) of 4800 and a temperature coefficient well within the X7R range.
Inventors
- 👤 Galeb H. Maher
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 16:47
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/46; C04B35/462; C04B35/465; C04B35/468; C04B35/4682; H; H01; H01G; H01G4/00; H01G4/002; H01G4/018; H01G4/06; H01G4/08; H01G4/12; H01G4/1209; H01G4/1218; H01G4/1227
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
163 words
A method for making a ceramic powder mixture comprising: a) combining from 95 to 98 weight percent of essentially pure and stoichiometric barium titanate powder of spherical particles with average particle size from 0.2 to 0.7 micron, from 1.5 to 2.5 weight percent of a powdered sintering aid composed of 3CdO.SiO 2 , and from 0.5 to 1.5 weight percent of a powdered grain-growth inhibitor powder, b) mixing said combined powders to form a homogenous powder mixture; and c) partially calcining said homogeneous mixture at approximately 700° C. to obtain a powder comprised of agglomerates of said homogeneous powder mixture wherein each of said agglomerates has essentially the same composition of barium titanate, cadmium silicate and grain-growth inhibitors as in said combined powders, to provide a powder mixture capable of being formed into a body that can be fired to maturity at 1100° C., which matured body has a high dielectric constant greater than 4000 and an X7R temperature coefficient of dielectric constant.
Claim 2
Independent Claim
163 words
A method for making a ceramic powder mixture comprising: a) combining from 95 to 98 weight percent of essentially pure and stoichiometric barium titanate powder of spherical particles with average particle size from 0.2 to 0.7 micron, from 1.5 to 2.5 weight percent of a powdered sintering aid composed of 3CdO.SiO 2 , and from 0.5 to 1.5 weight percent of a powdered grain-growth inhibitor powder, b) mixing said combined powders to form a homogenous powder mixture; and c) partially calcining said homogeneous mixture at approximately 700° C. to obtain a powder comprised of agglomerates of said homogeneous powder mixture wherein each of said agglomerates has essentially the same composition of barium titanate, cadmium silicate and grain-growth inhibitors as in said combined powders, to provide a powder mixture capable of being formed into a body that can be fired to maturity at 1100° C., which matured body has a high dielectric constant greater than 4000 and an X7R temperature coefficient of dielectric constant.
Claim 3
Dependent Claim
24 words
The method of claim 1 wherein said grain growth inhibitors are selected from the oxides of niobium, tantalum, bismuth and titanium, and bismuth titanate.
Claim 4
Dependent Claim
26 words
The method of claim 1 additionally comprising comminuting said calcined powder to produce a free flowing powder having an average agglomerate size of about 1 micron.
Claim 5
Dependent Claim
94 words
A ceramic powder mixture comprised of agglomerates, each of said agglomerates comprising a group of three kinds of powder particles having been partially calcined and superficially co-reacted to bind said group of powder particles together to form said each agglomerates, said three kinds of powder particles in said each agglomerates comprising from 95 to 98 weight percent of a barium titanate powder having an average particle size between 0.2 and 0.7 micron, from 1.5 to 2.5 weight percent of powdered 3CdO.SiO 2 and from 0.5 to 1.5 weight percent of a grain-growth inhibitor powder.
Claim 6
Dependent Claim
94 words
A ceramic powder mixture comprised of agglomerates, each of said agglomerates comprising a group of three kinds of powder particles having been partially calcined and superficially co-reacted to bind said group of powder particles together to form said each agglomerates, said three kinds of powder particles in said each agglomerates comprising from 95 to 98 weight percent of a barium titanate powder having an average particle size between 0.2 and 0.7 micron, from 1.5 to 2.5 weight percent of powdered 3CdO.SiO 2 and from 0.5 to 1.5 weight percent of a grain-growth inhibitor powder.
Claim 7
Dependent Claim
36 words
The ceramic powder mixture of claim 4 wherein 95 percent of said barium titanate powder particles have a size ranging from 0.8 to 1.2 of said average size providing thus a narrow distribution of particle sizes.
Claim 8
Dependent Claim
26 words
The ceramic powder mixture of claim 4 wherein said grain-growth inhibitors are selected from the oxides of niobium, tantalum, bismuth and titanium and from bismuth titanate.
Claim 9
Dependent Claim
16 words
The ceramic powder mixture of claim 4 wherein the average agglomerate size is about 1 micron.
Claim 10
Dependent Claim
15 words
The ceramic powder mixture of claim 4 wherein said barium titanate particles are essentially spherical.
Claim 11
Independent Claim
155 words
A method for making a dielectric ceramic body comprising: a) combining from 95 to 98 weight percent of essentially pure and stoichiometric barium titanate powder of spherical particles with average particle size from 0.2 to 0.7 micron, from 1.5 to 2.5 weight percent of a powdered sintering aid composed of 3CdO.SiO 2 , and from 0.5 to 1.5 weight percent of a powdered grain-growth inhibitor powder: b) mixing said combined powders to form a homogenous powder mixture; c) partially calcining said homogeneous mixture at approximately 700° C. to obtain a powder comprised of agglomerates of said homogeneous powder mixture wherein each of said agglomerates has essentially the same composition of barium titanate, cadmium silicate and grain-growth inhibitors as in said combined powders; d) forming a body of said calcined powder mixture; e) sintering said body at 1100° C. in a closed container; and f) annealing said body at about 1050° C. in an air atmosphere.
Claim 12
Independent Claim
155 words
A method for making a dielectric ceramic body comprising: a) combining from 95 to 98 weight percent of essentially pure and stoichiometric barium titanate powder of spherical particles with average particle size from 0.2 to 0.7 micron, from 1.5 to 2.5 weight percent of a powdered sintering aid composed of 3CdO.SiO 2 , and from 0.5 to 1.5 weight percent of a powdered grain-growth inhibitor powder: b) mixing said combined powders to form a homogenous powder mixture; c) partially calcining said homogeneous mixture at approximately 700° C. to obtain a powder comprised of agglomerates of said homogeneous powder mixture wherein each of said agglomerates has essentially the same composition of barium titanate, cadmium silicate and grain-growth inhibitors as in said combined powders; d) forming a body of said calcined powder mixture; e) sintering said body at 1100° C. in a closed container; and f) annealing said body at about 1050° C. in an air atmosphere.
References Cited (Backward Citations)
US5010443A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-11-01 | 1997-05-03 | 1997-11-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-11-01 | 2001-05-03 | 2001-11-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-11-01 | 2005-05-03 | 2005-11-02 | $7700.00 | Window Closed / Lapsed |