Abstract
Abstract The invention relates to a plasma CVD method for the deposition of a thin film of amorphous silicon, or an amorphous silicon alloy, on a substrate by glow discharge decomposition of a raw material gas such as silane gas. The degradation of the photoconductivity of the obtained amorphous silicon film by irradiation with light is suppressed by mixing xenon gas with the raw material gas such that at the entrance to the reaction chamber the volume ratio of xenon gas to the raw material gas is not less than 1 and, preferably, not more than 30. A nearly comparable effect can be gained, and the material cost can be reduced, by mixing 1 part by volume of the raw material gas with 0.05 to 1 part of xenon gas and 5 to 30 parts of hydrogen gas.
Inventors
- 👤 Akihisa Matsuda
- 👤 Satoshi Mashima
- 👤 Makoto Toda
- 👤 Kouji Fujita
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 06:34
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/44; C23C16/50; C23C16/505; C23C16/22; C23C16/24
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
160 words
A plasma chemical vapor deposition method for forming a film of amorphous silicon on a substrate placed in a reaction chamber, the method comprising the steps of evacuating the reaction chamber and keeping the substrate heated at a temperature in a range from about 200° C. to about 300° C., introducing a silicon compound gas into the reaction chamber so as to maintain a partial vacuum in the reaction chamber, at a power density ranging from about 0.03 W/cm 2 to about 0.8 W/cm 2 , making a glow discharge in the reaction chamber so as to decompose the silicon compound gas and produce a reactive plasma in the vicinity of the substrate thereby depositing said film of the amorphous silicon on the substrate, wherein xenon gas is mixed with said silicon compound gas such that at the entrance to the reaction chamber the volume ratio of the xenon gas to the silicon compound gas is not less than 1.
Claim 2
Dependent Claim
160 words
A plasma chemical vapor deposition method for forming a film of amorphous silicon on a substrate placed in a reaction chamber, the method comprising the steps of evacuating the reaction chamber and keeping the substrate heated at a temperature in a range from about 200° C. to about 300° C., introducing a silicon compound gas into the reaction chamber so as to maintain a partial vacuum in the reaction chamber, at a power density ranging from about 0.03 W/cm 2 to about 0.8 W/cm 2 , making a glow discharge in the reaction chamber so as to decompose the silicon compound gas and produce a reactive plasma in the vicinity of the substrate thereby depositing said film of the amorphous silicon on the substrate, wherein xenon gas is mixed with said silicon compound gas such that at the entrance to the reaction chamber the volume ratio of the xenon gas to the silicon compound gas is not less than 1.
Claim 3
Dependent Claim
20 words
A method according to claim 1, wherein said silicon compound is selected from the group consisting of silane and disilane.
Claim 4
Dependent Claim
24 words
A method according to claim 2, wherein said volume ratio of the xenon gas to the silicon compound gas is not greater than 30.
Claim 5
Dependent Claim
24 words
A method according to claim 3, wherein said volume ratio of the xenon gas to the silicon compound gas is not less than 2.
Claim 6
Dependent Claim
16 words
A method according to claim 1, wherein said glow discharge is generated by a high-frequency power.
Claim 7
Dependent Claim
196 words
A plasma chemical vapor deposition method for forming a film of amorphous silicon on a substrate placed in a reaction chamber, the method comprising the steps of evacuating the reaction chamber and keeping the substrate heated at a temperature in a range from about 200° C. to about 300° C., introducing a silicon compound gas into the reaction chamber so as to maintain a partial vacuum in the reaction chamber, at a power density ranging from about 0.03 W/cm 2 to about 0.8 W/cm 2 , making a glow discharge in the reaction chamber so as to decompose the silicon compound gas and produce a reactive plasma in the vicinity of the substrate thereby depositing said film of the amorphous silicon on the substrate, wherein xenon gas and hydrogen gas are mixed with said silicon compound gas such that the volume ratio of the xenon gas to the silicon compound gas is in the range from 0.05 to 1 at the entrance to the reaction chamber and such that the volume ratio of the hydrogen gas to the silicon compound gas is in the range from 5 to 30 at the entrance to the reaction chamber.
Claim 8
Dependent Claim
196 words
A plasma chemical vapor deposition method for forming a film of amorphous silicon on a substrate placed in a reaction chamber, the method comprising the steps of evacuating the reaction chamber and keeping the substrate heated at a temperature in a range from about 200° C. to about 300° C., introducing a silicon compound gas into the reaction chamber so as to maintain a partial vacuum in the reaction chamber, at a power density ranging from about 0.03 W/cm 2 to about 0.8 W/cm 2 , making a glow discharge in the reaction chamber so as to decompose the silicon compound gas and produce a reactive plasma in the vicinity of the substrate thereby depositing said film of the amorphous silicon on the substrate, wherein xenon gas and hydrogen gas are mixed with said silicon compound gas such that the volume ratio of the xenon gas to the silicon compound gas is in the range from 0.05 to 1 at the entrance to the reaction chamber and such that the volume ratio of the hydrogen gas to the silicon compound gas is in the range from 5 to 30 at the entrance to the reaction chamber.
Claim 9
Dependent Claim
20 words
A method according to claim 6, wherein said silicon compound is selected from the group consisting of silane and disilane.
Claim 10
Dependent Claim
27 words
A method according to claim 7, wherein said volume ratio of the hydrogen gas to the silicon compound gas is in the range from 5.5 to 25.
Claim 11
Dependent Claim
27 words
A method according to claim 8, wherein said volume ratio of the xenon gas to the silicon compound gas is in the range from 0.1 to 0.9.
Claim 12
Dependent Claim
16 words
A method according to claim 6, wherein said glow discharge is generated by a high-frequency power.
Claim 13
Dependent Claim
109 words
In a plasma chemical vapor deposition method for forming a film of an amorphous silicon alloy on a heated substrate placed in a reaction chamber by glow discharge decomposition of a raw material gas which is a mixture of a gaseous silicon compound and a gaseous compound of an alloying element, the improvement comprising forming said film at a power density ranging from about 0.03 W/cm 2 to about 0.8 W/cm 2 , wherein xenon gas is mixed with said raw material gas such that at the entrance to the reaction chamber the volume ratio of the xenon gas to the raw material gas is not less than 1.
Claim 14
Dependent Claim
109 words
In a plasma chemical vapor deposition method for forming a film of an amorphous silicon alloy on a heated substrate placed in a reaction chamber by glow discharge decomposition of a raw material gas which is a mixture of a gaseous silicon compound and a gaseous compound of an alloying element, the improvement comprising forming said film at a power density ranging from about 0.03 W/cm 2 to about 0.8 W/cm 2 , wherein xenon gas is mixed with said raw material gas such that at the entrance to the reaction chamber the volume ratio of the xenon gas to the raw material gas is not less than 1.
Claim 15
Dependent Claim
20 words
A method according to claim 11, wherein said silicon compound is selected from the group consisting of silane and disilane.
Claim 16
Dependent Claim
16 words
A method according to claim 12, wherein said gaseous compound of said alloying element is germane.
Claim 17
Dependent Claim
16 words
A method according to claim 12, wherein said gaseous compound of said alloying element is methane.
Claim 18
Dependent Claim
145 words
In a plasma chemical vapor deposition method for forming a film of an amorphous silicon alloy on a heated substrate placed in a reaction chamber by glow discharge decomposition of a raw material gas which is a mixture of a gaseous silicon compound and a gaseous compound of an alloying element, the improvement comprising forming said film at a power density ranging from about 0.03 W/cm 2 to about 0.8 W/cm 2 , wherein xenon gas and hydrogen gas are mixed with said raw material gas such that the volume ratio of the xenon gas to the raw material gas is in the range from 0.05 to 1 at the entrance to the reaction chamber and such that the volume ratio of the hydrogen gas to the raw material gas is in the range from 5 to 30 at the entrance to the reaction chamber.
Claim 19
Dependent Claim
145 words
In a plasma chemical vapor deposition method for forming a film of an amorphous silicon alloy on a heated substrate placed in a reaction chamber by glow discharge decomposition of a raw material gas which is a mixture of a gaseous silicon compound and a gaseous compound of an alloying element, the improvement comprising forming said film at a power density ranging from about 0.03 W/cm 2 to about 0.8 W/cm 2 , wherein xenon gas and hydrogen gas are mixed with said raw material gas such that the volume ratio of the xenon gas to the raw material gas is in the range from 0.05 to 1 at the entrance to the reaction chamber and such that the volume ratio of the hydrogen gas to the raw material gas is in the range from 5 to 30 at the entrance to the reaction chamber.
Claim 20
Dependent Claim
20 words
A method according to claim 15, wherein said silicon compound is selected from the group consisting of silane and disilane.
Claim 21
Dependent Claim
16 words
A method according to claim 16, wherein said gaseous compound of said alloying element is germane.
Claim 22
Dependent Claim
16 words
A method according to claim 16, wherein said gaseous compound of said alloying element is methane.
References Cited (Backward Citations)
JPS5799725A
Cited
JPS5954274A
Cited
US4521447A
Cited
US4492736A
Cited
JPS627859A
Cited
JPS6384079A
Cited
JPH01294866A
Cited
JPH02219284A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-09-20 | 1997-03-22 | 1997-09-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-09-20 | 2001-03-22 | 2001-09-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-09-20 | 2005-03-22 | 2005-09-21 | $7700.00 | Window Closed / Lapsed |