Process for depositing a thin layer of a ceramic composition and a product obtained thereby
Assignee: Thales SA
•
Filing: 1990-11-20
•
Granted: 1993-09-14
•
Expires: 2010-11-20
Abstract
Abstract A process for depositing a thin layer of a ceramic composition on a substrate, which comprises: a) dissolving basic constituents of the ceramic composition, which are added in simple or mixed form to a solvent; b) adding to the solution, acetylacetone and hexamethylene tetramine in proportions suitable to the deposit method used; c) maturing or polymerizing the substance obtained in step b); d) depositing a layer of the substance on a substrate; e) drying the deposited layer, and f) sintering the layer deposited at low temperature.
Inventors
- 👤 Isabelle (wife Campion) Valente
- 👤 Sylvain Faure
- 👤 Philippe Gaucher
- 👤 Jacques Livage
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 07:25
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/63; H10P14/6326; H10P14/6342; C; C04; C04B; C04B41/00; C04B41/009; C04B41/45; C04B41/52; C04B41/80; C04B41/81; C04B41/89; C23; C23C; C23C18/00; C23C18/02; C23C18/12; C23C18/1204; C23C18/1208; C23C18/1225; H10P14/66; H10P14/668; H10P14/69; H10P14/692; H10P14/6938; H10P14/6939; H10P14/69397; H10P72/00; H10P72/04; H10P72/0431; H10P14/69398; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31678
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
136 words
A process for depositing a thin layer of a ceramic composition on a substrate of corundum, silicon or silicon coated with platinum, which consists essentially of: a) dissolving constituents of an inorganically polymerizable ceramic composition in acetic acid or a mixture of acetic acid and propanol or acetic acid and methoxyethanol, to form an acidic solution of said constituents, b) adding to the solution acetylacetone and hexamethylene tetramine in amounts effective for said constituents to remain solubilized in the medium during subsequent polymer formation and during drying on the substrate; c) maturing or polymerizing the solution obtained in step b) in the presence of said acidic solution until reaching a stable state; d) depositing a layer of the matured or polymerized substance on the substrate; e) drying the deposited layer; and f) sintering the deposited layer.
Claim 2
Dependent Claim
136 words
A process for depositing a thin layer of a ceramic composition on a substrate of corundum, silicon or silicon coated with platinum, which consists essentially of: a) dissolving constituents of an inorganically polymerizable ceramic composition in acetic acid or a mixture of acetic acid and propanol or acetic acid and methoxyethanol, to form an acidic solution of said constituents, b) adding to the solution acetylacetone and hexamethylene tetramine in amounts effective for said constituents to remain solubilized in the medium during subsequent polymer formation and during drying on the substrate; c) maturing or polymerizing the solution obtained in step b) in the presence of said acidic solution until reaching a stable state; d) depositing a layer of the matured or polymerized substance on the substrate; e) drying the deposited layer; and f) sintering the deposited layer.
Claim 3
Dependent Claim
23 words
The process according to claim 1, wherein the proportions of acetylacetone and hexamethylenetetramine are 2 moles of acetylacetone to 1 mole of hexamethylenetetramine.
Claim 4
Dependent Claim
32 words
The process according to claim 2, wherein the ceramic composition is lead titanate, and titanium is added as titanium tetrabutoxide and lead is added as lead acetate, the solvent being acetic acid.
Claim 5
Dependent Claim
26 words
The process according to claim 1, wherein at least one additional layer of the substance is deposited on the substrate after drying the previously deposited layer.
Claim 6
Dependent Claim
15 words
The process according to claim 1, wherein said deposited layer is dried at 300° C.
Claim 7
Dependent Claim
14 words
The process according to claim 1, wherein said sintering is effected at 700°-750° C.
References Cited (Backward Citations)
US4481134A
Cited
US4485094A
Cited
US4960618A
Cited
US4946710A
Cited
US4886654A
Cited
US4937208A
Cited
US4913708A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-09-13 | 1997-03-15 | 1997-09-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-09-13 | 2001-03-15 | 2001-09-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-09-13 | 2005-03-15 | 2005-09-14 | $7700.00 | Window Closed / Lapsed |