Manufacture of vitreous silica product via a sol-gel process using a polymer additive
Assignee: Furukawa Electric North America Inc
•
Filing: 1992-08-14
•
Granted: 1993-08-31
•
Expires: 2012-08-14
Abstract
Abstract Lowered cost fabrication including preparation of large bodies of void-free, high-silica glass, depends upon gellation of an aqueous sol of colloidal silica particles, followed by drying and firing of such gel. Freedom from cracks in the dried gel is the consequence of included polymeric material which wets the particles. The polymeric material is removed by thermal decomposition attended upon temperature attained in firing.
Inventors
- 👤 Edwin A. Chandross
- 👤 Debra A. Fleming
- 👤 David W. Johnson, Jr.
- 👤 John B. MacChesney
- 👤 Frederick W. Walz, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 10:36
CPC Classifications
C; C03; C03B; C03B37/00; C03B37/01; C03B37/012; C03B37/014; C03B37/016; C03B19/00; C03B19/12; C03B37/01205; C03B37/01211; C03C; C03C1/00; C03C1/006; Y; Y02; Y02P; Y02P40/00; Y02P40/50; Y02P40/57; Y10; Y10S; Y10S65/00; Y10S65/901
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
200 words
Method for fabricating an article at least in part composed of high silica glass including fabricating a high-silica glass body by a method comprising gelling a sol, the sol comprising a suspension of colloidal silica particles in a suspension medium, so resulting in a gel, drying the gel so as to substantially remove the suspension medium, and firing such gel to produce a high-silica glass body, and carrying out any further processing necessary to yield the article characterized in that the said sol, during a substantial part of the gelling, contains additive including a first additive consisting essentially of at least one organic polymer, the polymer being characterized as: (1) of amount sufficient to monomolecularly coat from 5% to 50% of the total free surface of the colloidal silica particles, (2) of solubility as to result in substantially complete solution in the said sol prior to gelation, (3) of such nature as to wet the said silica particles, (4) of such composition as to thermally decompose primarily to gaseous decomposition product so that the high silica glass body is substantially free of the polymer as well as of decomposition product constituting a meaningful contaminant deleteriously affecting performance of the article.
Claim 2
Dependent Claim
200 words
Method for fabricating an article at least in part composed of high silica glass including fabricating a high-silica glass body by a method comprising gelling a sol, the sol comprising a suspension of colloidal silica particles in a suspension medium, so resulting in a gel, drying the gel so as to substantially remove the suspension medium, and firing such gel to produce a high-silica glass body, and carrying out any further processing necessary to yield the article characterized in that the said sol, during a substantial part of the gelling, contains additive including a first additive consisting essentially of at least one organic polymer, the polymer being characterized as: (1) of amount sufficient to monomolecularly coat from 5% to 50% of the total free surface of the colloidal silica particles, (2) of solubility as to result in substantially complete solution in the said sol prior to gelation, (3) of such nature as to wet the said silica particles, (4) of such composition as to thermally decompose primarily to gaseous decomposition product so that the high silica glass body is substantially free of the polymer as well as of decomposition product constituting a meaningful contaminant deleteriously affecting performance of the article.
Claim 3
Dependent Claim
22 words
Method of claim 1 in which the suspension medium is aqueous, and in which gelation entails reducing the pH of the sol.
Claim 4
Dependent Claim
61 words
Method of claim 2 in which the said particles have a maximum surface area of 100 square meters per gram, in which the amount of silica in the sol is at least 30 weight percent as based on the sol, and in which the pH of the sol prior to gelation at some time attains a value of at least 9.5.
Claim 5
Dependent Claim
47 words
Method of claim 3 in which the attained value of at least 9.5 prior to gelation is assured by inclusion of a pH-increasing ingredient in the sol, and in which reducing pH is at least in part due to addition of a pH-decreasing ingredient to the sol.
Claim 6
Dependent Claim
56 words
Method of claim 4 in which the sol is introduced into a mold within which the gelation takes place, in which the pH-decreasing ingredient is added to the sol prior to introduction of the sol into the mold, and in which the pH-decreasing ingredient consists essentially of an ester whereby the rate of gelation is controlled.
Claim 7
Dependent Claim
32 words
Method of claim 5 in which the wetting comprises reversible chemisorption, and in which the mold defines a cavity of shape to result in a near net shape molded body upon gelation.
Claim 8
Dependent Claim
25 words
Method of claim 6 in which said sol, during a substantial part of said gelation, contains a second additive consisting essentially of a polyhydric alcohol.
Claim 9
Dependent Claim
33 words
Method of claim 6 in which the amount of sol as introduced into the mold is sufficient to result in a high silica glass body of a weight of at least 1 kilogram.
Claim 10
Dependent Claim
45 words
Method of claim 8 in which the said polymer is primarily aliphatic and consists primarily of atoms selected from the group consisting of carbon, hydrogen, oxygen, and nitrogen, and in which the molecular weight of the polymer is of a maximum value of 1 million.
Claim 11
Dependent Claim
35 words
Method of claim 9 in which total content of alkali metal ions, selected from the group consisting of sodium and potassium, is at a maximum of 100 ppm. as based on the dried gelled body.
Claim 12
Dependent Claim
11 words
Method of claim 10 in which the polymer is a polyamide.
Claim 13
Dependent Claim
20 words
Method of claim 11 in which the polymer is selected from the group consisting of polyethyloxazoline, polymethyloxazoline and a polyacrylamide.
Claim 14
Dependent Claim
16 words
Method of claim 12 in which the polymer contains quaternary ammonium substituents and halide counter ions.
Claim 15
Dependent Claim
19 words
Method of claim 12 in which the sol includes a second additive which consists essentially of a polyhydric alcohol.
Claim 16
Dependent Claim
10 words
Method of claim 14 in which second additive is glycerin.
Claim 17
Dependent Claim
16 words
Method of claim 4 in which the pH-increasing ingredient is at least one quaternary ammonium hydroxide.
Claim 18
Dependent Claim
25 words
Method of claim 16 in which the pH-increasing ingredient is at least one compound selected from the group consisting of tetramethylammonium hydroxide and tetraethylammonium hydroxide.
Claim 19
Dependent Claim
33 words
Method of claim 4 in which the pH-reducing ingredient consists essentially of a water soluble aliphatic ester of an acid selected from the group consisting of formic acid, lactic acid, and glycolic acid.
Claim 20
Dependent Claim
23 words
Method of any one of claims 1-18 in which performance of the article entails low-loss transmission of electromagnetic energy within the optical spectrum.
Claim 21
Dependent Claim
41 words
Method of any one of claims 1-18 in which the article is optical fiber, in which the high-silica glass body yields a substantial portion of a fiber, the said method comprising drawing such fiber from a fiber preform comprising the body.
Claim 22
Dependent Claim
104 words
Method of any one of claims 1-18 in which the article is optical fiber, in which the high-silica glass body constitutes an overcladding tube, and in which said method comprises drawing a fiber from a fiber preform produced by collapsing of the tube so as to bring it into intimate contact with an enclosed core rod consisting of a core portion within an inner cladding portion, said core rod being produced by deposition using a process selected from the group consisting of Modified Chemical Vapor Deposition and a soot deposition process selected from the group consisting of Vapor Axial Deposition and Outside Vapor Deposition.
Claim 23
Dependent Claim
117 words
Method of any one of claims 1-18 in which the article is optical fiber, in which the high-silica glass body constitutes an overcladding tube, and in which said method comprises drawing a fiber from a fiber preform produced by collapsing of the tube so as to bring it into intimate contact with an enclosed core rod consisting of a core portion within an inner cladding portion, said core rod being produced by deposition using a process selected from the group consisting of Modified Chemical Vapor Deposition and a soot deposition process selected from the group consisting of Vapor Axial Deposition and Outside Vapor Deposition and in which the said tube is fired while enclosing such core rod.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-08-30 | 1997-03-01 | 1997-08-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-08-30 | 2001-03-01 | 2001-08-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-08-30 | 2005-03-01 | 2005-08-31 | $7700.00 | Window Closed / Lapsed |