Thermal barrier coating system with intermetallic overlay bond coat

Claim 2

A superalloy article having a thermal barrier coating system thereon, comprising: a substrate made of a material selected from the group consisting of a nickel-based superalloy and a cobalt-based superalloy; and a thermal barrier coating system on the substrate, the thermal barrier coating system including an intermetallic bond coat overlying the substrate, the bond coat being selected from the group consisting of a nickel aluminide and a platinum aluminide intermetallic compound, a thermally grown aluminum oxide layer overlying the intermetallic bond coat, and a ceramic topcoat overlying the aluminum oxide layer.

Claim 3

The article of claim 1, wherein the intermetallic bond coat is from about 0.001 to about 0.005 inches thick.

Claim 4

The article of claim 1, wherein the ceramic topcoat is from about 0.005 to 0.015 inches thick.

Claim 5

The article of claim 1, wherein the ceramic topcoat has a columnar grain structure wherein the columnar axis is substantially perpendicular to the surface of the intermetallic bond coat.

Claim 6

The article of claim 1, wherein the ceramic topcoat includes zirconium oxide and yttrium oxide.

Claim 7

The article of claim 1, wherein the ceramic topcoat is zirconium oxide plus from about 6 to about 20 percent by weight yttrium oxide.

Claim 8

The article of claim 1, wherein the article is a gas turbine blade.

Claim 9

The article of claim 1, wherein the intermetallic coating includes at least one alloying element that does not alter the intermetallic character of the coating.

Claim 10

The article of claim 2, wherein the layer of aluminum oxide is from about 1.2×10 -6 to about 1.2×10 -4 inches thick.

Claim 11

A superalloy article having a thermal barrier coating system thereon, comprising: a substrate made of a superalloy selected from the group consisting of a nickel-based superalloy and a cobalt-based superalloy; and a thermal barrier coating system on the substrate, the thermal barrier coating system including an aluminide intermetallic bond coat upon the substrate, the bond coat being selected from the group consisting of a nickel aluminide and a platinum aluminide, the bond coat having a thickness of from about 0.001 to about 0.005 inches thick, a layer of a thermally grown aluminum oxide upon the intermetallic bond coat, the layer of aluminum oxide being from about 1.2×10 -6 to about 1.2×10 -4 inches thick, and a ceramic topcoat upon the layer of aluminum oxide, the ceramic topcoat having a composition of zirconium oxide plus from about 6 to about 20 weight percent yttrium oxide and a columnar grain structure wherein the columnar axis is substantially perpendicular to the surface of the intermetallic bond coat.

Claim 12

A superalloy article having a thermal barrier coating system thereon, comprising: a substrate made of a superalloy selected from the group consisting of a nickel-based superalloy and a cobalt-based superalloy; and a thermal barrier coating system on the substrate, the thermal barrier coating system including an aluminide intermetallic bond coat upon the substrate, the bond coat being selected from the group consisting of a nickel aluminide and a platinum aluminide, the bond coat having a thickness of from about 0.001 to about 0.005 inches thick, a layer of a thermally grown aluminum oxide upon the intermetallic bond coat, the layer of aluminum oxide being from about 1.2×10 -6 to about 1.2×10 -4 inches thick, and a ceramic topcoat upon the layer of aluminum oxide, the ceramic topcoat having a composition of zirconium oxide plus from about 6 to about 20 weight percent yttrium oxide and a columnar grain structure wherein the columnar axis is substantially perpendicular to the surface of the intermetallic bond coat.

Claim 13

The article of claim 10, wherein the nickel aluminide is NiAl.

Claim 14

A process for preparing a superalloy article having a thermal barrier coating system thereon, comprising: furnishing a substrate made of a nickel-based superalloy; depositing upon the surface of the substrate an aluminide intermetallic coating that has a substantially smooth upper surface, said bond coating being selected from the group consisting of a nickel aluminide and a platinum aluminide intermetallic compound; thermally oxidizing the upper surface of the intermetallic coating to form an aluminum oxide layer; and depositing upon the surface of the aluminum oxide layer a ceramic topcoat by physical vapor deposition.

Claim 15

A process for preparing a superalloy article having a thermal barrier coating system thereon, comprising: furnishing a substrate made of a nickel-based superalloy; depositing upon the surface of the substrate an aluminide intermetallic coating that has a substantially smooth upper surface, said bond coating being selected from the group consisting of a nickel aluminide and a platinum aluminide intermetallic compound; thermally oxidizing the upper surface of the intermetallic coating to form an aluminum oxide layer; and depositing upon the surface of the aluminum oxide layer a ceramic topcoat by physical vapor deposition.

Claim 16

The process of claim 12, wherein the temperature of the substrate during the step of depositing the intermetallic coating is greater than about 1800°F.

Claim 17

The process of claim 12, wherein the temperature of the substrate during the step of depositing the ceramic topcoat is from about 1700°F. to about 1900°F.

Claim 18

The process of claim 12, further including the step of oxidizing the surface of the intermetallic coating adjacent the ceramic topcoat to form aluminum oxide.

Claim 19

The process of claim 12, wherein the aluminide is platinum rhodium aluminide.

Claim 20

A thermal barrier coating system for metallic substrates, comprising: an intermetallic bond coat overlying a substrate selected from the group consisting of nickel-based superalloys and cobalt-based superalloys, the bond coat being selected from the group consisting of a nickel aluminide and a platinum aluminide intermetallic compound, and a ceramic topcoat overlying the intermetallic coating.

Claim 21

A thermal barrier coating system for metallic substrates, comprising: an intermetallic bond coat overlying a substrate selected from the group consisting of nickel-based superalloys and cobalt-based superalloys, the bond coat being selected from the group consisting of a nickel aluminide and a platinum aluminide intermetallic compound, and a ceramic topcoat overlying the intermetallic coating.

Claim 22

The coating system of claim 17, wherein the bond coat is oxidized to form an aluminum oxide layer between the bond coat and the topcoat.

Claim 23

The article of claim 1, wherein the substrate is the nickel-based superalloy Rene N5, having a nominal composition of 7.5 weight percent cobalt, 7.0 weight chromium, 6.2 weight percent aluminum, 6.5 weight percent tantalum, 5.0 weight percent tungsten, 3.0 weight percent rhenium, 1.5 weight percent molybdenum, 0.15 weight percent hafnium, 0.05 weight percent carbon, 0.004 weight percent boron, remainder nickel.