Process for the manufacture of linear polyethylene containing α-alkene commonomers

Claim 2

A solution polymerization process for producing a blend of polyethylene and copolymers of ethylene and at least one α-olefin having three to twelve carbon atoms comprising: (A) in a first reactor, contacting ethylene and at least one α-olefin having three to twelve carbon atoms with a catalyst adopted for the polymerization thereof; (B) effecting the polymerization of a portion of the olefins in the first reactor at a temperature between about 125° and about 240° C. in a manner such that a copolymer of ethylene and at least one α-olefin having three to twelve carbon atoms is formed in admixture with said catalyst; (C) in a second reactor, parallel to said first reactor, contacting ethylene with a catalyst adopted for the polymerization thereof; (D) effecting the polymerization of a portion of the olefins in said second reactor at a temperature of about 180° to about 280° C. in a manner such that a homopolymer of ethylene is formed in admixture with said catalyst; (E) admixing the mixture from stop (B) with the mixture from step (D) in a third reactor; and (F) effecting the polymerization of olefins from said first and second reactors in the third reactor at a temperature of about 240° to about 320° C., where said process is adiabatic and the temperature in said third reactor is higher than the temperature in said first and second reactors, and where the polymerizations are effected so that the polymer produced in said first reactor has a higher molecular weight than the polymers produced in said second and third reactors.

Claim 3

A process according to claim 1 wherein the quantity of monomer converted to polymer in said first reactor is between 70 and 95 wt % of the monomer introduced into said first reactor.

Claim 4

A process according to claim 2 wherein the quantity of monomer converted to polymer in said first reactor is between 80 and 90 wt % of the monomer introduced into said first reactor.

Claim 5

A process according to claim 1 wherein said third reactor is a non-back-mixed tubular reactor.

Claim 6

A process according to claim 1 wherein the polymerization temperature in said first reactor is less than 200° C.

Claim 7

A process according to claim 1 wherein the weight ratio of ethylene to α-olefin in said first reactor is 0.5 to 50.

Claim 8

A process according to claim 1 wherein a chain transfer agent is introduced into said second reactor to control the molecular weight of said homopolymer.

Claim 9

A process according to claim 7 wherein said chain transfer agent is hydrogen.

Claim 10

A process according to claim 1 wherein said polymerizations in said first, second, and third reactors are performed in a saturated hydrocarbon solvent having a boiling point between 30° and 150° C.

Claim 11

A process according to claim 9 wherein said solvent is hexane or cyclohexane.

Claim 12

A process according to claim 1 wherein said polymerization in said first, second, and third reactors are performed so that the final product contains about 0.25 to about 5 wt % unreacted ethylene.

Claim 13

A process according to claim 11 wherein said unreacted ethylene is recycled to said first reactor.

Claim 14

A process according to claim 1 wherein said copolymer has a melt index less than 1.0, said homopolymer has a melt index of about 1 to about 15, and the polymer produced in said third reactor has a melt index of about 5 to about 50.

Claim 15

A solution polymerization process for producing a blend of polyethylene and copolymers of ethylene and at least one α-olefin having three to twelve carbon atoms comprising: (A) in a first reactor, copolymerizing ethylene with at least one α-olefin containing three to twelve carbon atoms, in a saturated hydrocarbon solvent having a boiling point between 30° and 150° C., in the presence of a suitable polymerization catalyst, at a temperature of between about 125° and about 240° C.; (B) in a second reactor, separately polymerizing ethylene in said hydrocarbon solvent, in the presence of a suitable polymerization catalyst, at a temperature of about 180° to about 280° C., to produce a homopolymer of ethylene; (C) combining the products of steps (A) and (B) in a plug-flow tubular third reactor; and (D) polymerizing olefins in said third reactor at a temperature of about 265° to about 300° C., where the temperature in said third reactor is higher than the temperature in said first and second reactors, where the polymerizations are effected adiabatically and so that the polymer produced in said first reactor has a higher molecular weight than the polymers produced in said second and third reactors, and where about 5 to about 60 wt % of the total polymer produced is formed in said first reactor, about 20 to about 60 wt % of the total polymer produced is formed in said second reactor, and the remainder of said polymer produced is formed in said third reactor.

Claim 16

A solution polymerization process for producing a blend of polyethylene and copolymers of ethylene and at least one α-olefin having three to twelve carbon atoms comprising: (A) in a first reactor, copolymerizing ethylene with at least one α-olefin containing three to twelve carbon atoms, in a saturated hydrocarbon solvent having a boiling point between 30° and 150° C., in the presence of a suitable polymerization catalyst, at a temperature of between about 125° and about 240° C.; (B) in a second reactor, separately polymerizing ethylene in said hydrocarbon solvent, in the presence of a suitable polymerization catalyst, at a temperature of about 180° to about 280° C., to produce a homopolymer of ethylene; (C) combining the products of steps (A) and (B) in a plug-flow tubular third reactor; and (D) polymerizing olefins in said third reactor at a temperature of about 265° to about 300° C., where the temperature in said third reactor is higher than the temperature in said first and second reactors, where the polymerizations are effected adiabatically and so that the polymer produced in said first reactor has a higher molecular weight than the polymers produced in said second and third reactors, and where about 5 to about 60 wt % of the total polymer produced is formed in said first reactor, about 20 to about 60 wt % of the total polymer produced is formed in said second reactor, and the remainder of said polymer produced is formed in said third reactor.

Claim 17

A process according to claim 14 wherein the quantity of monomer converted to polymer in the first reactor is between 70 and 95 wt % of the monomer introduced to said first reactor.

Claim 18

A process according to claim 14 wherein the weight ratio of ethylene to α-olefin in said first reactor is 0.5 to 50.

Claim 19

A process according to claim 14 wherein a chain transfer agent is introduced into said second reactor to control the molecular weight of said homopolymer.

Claim 20

A process according to claim 17 wherein said chain transfer agent is hydrogen.

Claim 21

A process according to claim 14 wherein said solvent is hexane or cyclohexane.

Claim 22

A solution polymerization process for producing a blend of polyethylene and copolymers of ethylene and at least on α-olefin having three to twelve carbon atoms comprising: (A) in a well-stirred, back-mixed tank first reactor, copolymerizing ethylene with at least one α-olefin having three to twelve carbon atoms, in hexane or cyclohexane, in the presence of a suitable polymerization catalyst, at a temperature of between about 125° and about 200° C., whereby 70 to 95 wt % of said ethylene and α-olefin is converted into polymer; (B) in a well-stirred, back-mixed tank second reactor, separately polymerizing ethylene in said hydrocarbon solvent, in the presence of a suitable polymerization catalyst, at a temperature of about 180° and about 280° C., to produce a homopolymer of ethylene; (C) combining the products of steps (A) and (B) in a plug-flow tubular third reactor; and (D) polymerizing olefins in said third reactor at a temperature of about 265° to about 320° C., where the temperature in said second reactor is higher than the temperature in said first reactor and the temperature in said third reactor is higher than the temperature in said second reactor, the polymerizations are effected adiabatically and so that the polymer produced in said first reactor has a higher molecular weight than the polymers produced in said second and third reactors, about 5 to about 60 wt % of the total polymer produced is formed in said first reactor, about 20 to about 60 wt % of the total polymer produced is formed in said second reactor, and the remainder of said polymer produced is formed in said third reactor, and said polymerizations in said first, second, and third reactors are performed so that the product of said third reactor contains about 0.25 to about 5 wt % unreacted ethylene; and (E) recycling said unreacted ethylene to said first reactor.

Claim 23

A solution polymerization process for producing a blend of polyethylene and copolymers of ethylene and at least on α-olefin having three to twelve carbon atoms comprising: (A) in a well-stirred, back-mixed tank first reactor, copolymerizing ethylene with at least one α-olefin having three to twelve carbon atoms, in hexane or cyclohexane, in the presence of a suitable polymerization catalyst, at a temperature of between about 125° and about 200° C., whereby 70 to 95 wt % of said ethylene and α-olefin is converted into polymer; (B) in a well-stirred, back-mixed tank second reactor, separately polymerizing ethylene in said hydrocarbon solvent, in the presence of a suitable polymerization catalyst, at a temperature of about 180° and about 280° C., to produce a homopolymer of ethylene; (C) combining the products of steps (A) and (B) in a plug-flow tubular third reactor; and (D) polymerizing olefins in said third reactor at a temperature of about 265° to about 320° C., where the temperature in said second reactor is higher than the temperature in said first reactor and the temperature in said third reactor is higher than the temperature in said second reactor, the polymerizations are effected adiabatically and so that the polymer produced in said first reactor has a higher molecular weight than the polymers produced in said second and third reactors, about 5 to about 60 wt % of the total polymer produced is formed in said first reactor, about 20 to about 60 wt % of the total polymer produced is formed in said second reactor, and the remainder of said polymer produced is formed in said third reactor, and said polymerizations in said first, second, and third reactors are performed so that the product of said third reactor contains about 0.25 to about 5 wt % unreacted ethylene; and (E) recycling said unreacted ethylene to said first reactor.