US5234625A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Synthesis of lead-activated barium silicate phosphor
Assignee: Osram Sylvania Inc
•
Filing: 1992-07-27
•
Granted: 1993-08-10
•
Expires: 2012-07-27
Abstract
Abstract A method of making lead-activated barium silicate phosphor involves the use of a lead source which is not lead oxide. More particularly, the lead source may be lead silicate or lead carbonate-lead hydroxide.
Inventors
- 👤 Cheryl M. Forster
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 15:59
CPC Classifications
C; C09; C09K; C09K11/00; C09K11/08; C09K11/66; C09K11/666
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
64 words
A method of making lead-activated barium Silicate phosphor having the formula BaSi 2 O 5 :Pb, comprising the steps of: combining a silica precursor, a barium precursor, a barium halide flux material, and lead silicate to form a uniform mixture, and firing said uniform mixture at between 750° C. and 990° C. for between 3 and 7 hours in air to form said phosphor.
Claim 2
Independent Claim
64 words
A method of making lead-activated barium Silicate phosphor having the formula BaSi 2 O 5 :Pb, comprising the steps of: combining a silica precursor, a barium precursor, a barium halide flux material, and lead silicate to form a uniform mixture, and firing said uniform mixture at between 750° C. and 990° C. for between 3 and 7 hours in air to form said phosphor.
Claim 3
Dependent Claim
48 words
A method as in claim 1 further comprising the step of milling said phosphor with a second barium halide flux material to form a second uniform mixture, and firing said second uniform mixture at between 900° C. and 1200° C. for between 3 and 7 hours in air.
Claim 4
Dependent Claim
30 words
A method as in claim 2 wherein said second flux material is barium chloride and is provided in an amount of between 2 and 6 weight percent of said phosphor.
Claim 5
Dependent Claim
37 words
A method as in claim 1 wherein said silica precursor is fumed silica, said barium precursor is barium carbonate, and said flux material is barium fluoride provided in an amount of 0.044 mole per mole of barium.
Claim 6
Dependent Claim
48 words
A method as in claim 1 wherein said lead silicate is selected from the group consisting of PbSiO 3 , Pb 2 SiO 4 , and Pb 3 Si 2 O 7 and is provided in an amount of between 0.006 and 0.06 mole per mole of barium.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-08-09 | 1997-02-08 | 1997-08-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-08-09 | 2001-02-08 | 2001-08-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-08-09 | 2005-02-08 | 2005-08-10 | $7700.00 | Window Closed / Lapsed |