Abstract Commercially valuable chemicals are extracted from tire-derived pyrolytic oils by subjecting the pyrolytic oils to a fractional distillation at a temperature of up to about 204 DEG C. under atmospheric pressure to isolate at least one commercially valuable chemical selected from the group consisting of paraffins, naphthenes, olefins and aromatics. Particularly valuable chemicals which can be extracted from tire-derived pyrolytic oils are benzene, toluene, xylene, styrene and limonene-dl. The distillation fraction boiling above 204 DEG C. can be used as an extension oil in the manufacture of various rubber and plastic parts. Also disclosed is an improved process for producing carbon black by vacuum pyrolysis of used rubber tires.
A process for producing carbon black by vacuum pyrolysis of used rubber tires, which comprises pyrolysing used rubber tire material at a temperature in the range of about 490° C. to about 510° C. under an absolute pressure of less than about 5 kPa, and recovering a solid carbonaceous material containing carbon black having an iodine adsorption number of about 130 to about 150 mg/g.
Claim 2
Dependent Claim
65 words
A process for producing carbon black by vacuum pyrolysis of used rubber tires, which comprises pyrolysing used rubber tire material at a temperature in the range of about 490° C. to about 510° C. under an absolute pressure of less than about 5 kPa, and recovering a solid carbonaceous material containing carbon black having an iodine adsorption number of about 130 to about 150 mg/g.
Claim 3
Dependent Claim
19 words
A process according to claim 1, wherein said pyrolysis is carried out at a temperature of about 500° C.
Claim 4
Dependent Claim
42 words
A process according to claim 1, wherein said pyrolysis is carried out at a temperature of about 500° C. under an absolute pressure of about 0.3 kPa whereby to obtain a carbon black having an iodine adsorption number of about 150 mg/g.
Claim 5
Dependent Claim
57 words
A process according to claim 1, which consists essentially of pyrolysing used rubber tire material at a temperature of about 490° C. to about 510° C. under an absolute pressure of less than about 5 kPa and recovering a solid carbonaceous material containing carbon black having an iodine adsorption number of about 130 mg/g to 150 mg/g.